Process for preparing flame-retarding washable filtering material

A filter material and a preparation process technology, which are applied in the field of preparation technology of flame-retardant and water-washable filter materials to achieve the effects of reducing emissions, reducing use costs and protecting the environment

Inactive Publication Date: 2009-10-14
HENAN ANKELIN FILTER IND
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved in the present invention is to disclose a preparation method of a flame-retardant and washable filter material, so as to meet the problems of resource conservation and environmental protection in contemporary society. The flame-retardant and washable filter material in the present invention is made of several different polyester Or polypropylene staple fiber and three-dimensional crimped polyester staple fiber are needled in a certain proportion to form the basic material, and then soaked in a flame-retardant glue solution made of acrylic ester polymer and cyclophosphate flame retardant in a certain proportion. Double-roll rolling, drying, spraying flame-retardant glue solution, drying and ironing to form a filter material with fiber intersections fixed by glue spots and fiber surface covered by a smooth glue layer, that is, the present invention is obtained.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] (1) Preparation of acupuncture materials:

[0016] It is made of polyester or polypropylene staple fiber with a fiber fineness of 2dtex and a length of 50mm; three-dimensional crimped polyester staple fiber with a fiber fineness of 5dtex and a length of 40mm; the above weight ratio is 85:15, uniformly mixed, through opening, It is made by carding, laying net, and acupuncture. The speed of the acupuncture machine is 1000 times / min, and the needle density is 2000 pieces / m, so that several kinds of polyester or polypropylene fibers are evenly connected into one.

[0017] (2) Preparation of flame retardant glue:

[0018] Acrylate polymer or melamine resin or water-based polyurethane: cyclic phosphate ester or phosphoric acid ester or ammonium polyphosphate flame retardant is uniformly proportioned in a ratio of 40:60, and the weight ratio is mixed evenly.

[0019] (3) Soak the needle-punched material in the mixture of (2) and water, run at a speed of 0.5 m / min, pass throug...

Embodiment 2

[0032] (1) Preparation of acupuncture materials:

[0033] It is made of polyester or polypropylene staple fiber with a fiber fineness of 16dtex and a length of 75mm; three-dimensional crimped polyester staple fiber with a fiber fineness of 12dtex and a length of 50mm; the above weight ratio is 85:15, uniformly mixed, through opening, It is made by carding, laying net, and acupuncture. The speed of the acupuncture machine is 1200 times / min, and the needle density is 3000 pieces / m, so that several kinds of polyester or polypropylene fibers are evenly connected into one.

[0034] (2) Preparation of flame retardant glue:

[0035] Acrylate polymer or melamine resin or water-based polyurethane: cyclic phosphate ester or phosphoric acid ester or ammonium polyphosphate flame retardant is uniformly proportioned in a ratio of 50:50, and the weight ratio is mixed evenly.

[0036] (3) Soak the needle-punched material in the mixture of (2) and water, run at a speed of 5 m / min, pass throug...

Embodiment 3

[0049] (1) Preparation of acupuncture materials:

[0050] It is made of polyester or polypropylene staple fiber with a fiber fineness of 20dtex and a length of 80mm; three-dimensional crimped polyester staple fiber with a fiber fineness of 18dtex and a length of 60mm; the above weight ratio is 85:15, uniformly mixed, through opening, It is made by carding, laying net, and acupuncture. The speed of the acupuncture machine is 1500 times / min, and the needle density is 4000 pieces / m, so that several kinds of polyester or polypropylene fibers are evenly connected into one.

[0051] (2) Preparation of flame retardant glue:

[0052] Acrylate polymer or melamine resin or water-based polyurethane: cyclic phosphate ester or phosphoric acid ester or ammonium polyphosphate flame retardant is uniformly proportioned in a ratio of 60:40, and the weight ratio is mixed evenly.

[0053] (3) Soak the needle-punched material in the mixture of (2) and water, run at a speed of 10 m / min, pass throu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a process for preparing a flame-retarding washable filtering material. The flame-retarding washable filtering material is prepared by the following steps of: needling various terylene or polypropylene staple fiber and three-dimensional crimp polyester staple fiber by a certain proportion to prepare a basic material; subsequently soaking the basic material in a flame-retarding adhesive solution prepared by mixing an acrylate polymer and a cyclic phosphate flame retardant with a certain proportion; subsequently rolling by dual rollers, drying and spraying the flame-retarding adhesive; and subsequently drying and ironing out the solution, thus forming the filtering material with the fiber crossing fixed by adhesive point and fiber surface covered by a smooth adhesive layer. The process is flame-retarding and washable.

Description

Technical field: [0001] The invention relates to a flame-retardant and water-washable filter material and a preparation process thereof, in particular to a filter material for systems such as centralized ventilation, central air conditioning, and liquid purification. Background technique: [0002] China is the most populous developing country in the world. Since the end of the 1970s, with the continuous and rapid development of China's economy, the environmental problems that have emerged in stages in the industrialization process of developed countries for hundreds of years have concentrated in China. The contradiction between environment and development Eyes are prominent. The relative shortage of resources, fragile ecological environment, and insufficient environmental capacity have gradually become major problems in China's development. [0003] my country's "Eleventh Five-Year Plan" puts forward higher requirements for environmental protection. Water, gas, sound, slag ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01D39/16
Inventor 李瑞乐
Owner HENAN ANKELIN FILTER IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products