Organic descaling composition, preparation method and application thereof

A composition and organic technology, applied in the directions of organic non-surface active cleaning compositions, cleaning methods and utensils, detergent compositions, etc., can solve the problems of insufficient scale removal rate, slow scale removal speed of scale removers, etc.

Active Publication Date: 2011-08-17
河南伯淼水处理有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the descaling speed of described descaling agent is slow, and the descaling rate is also not high enough

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic descaling composition, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Formula (by weight ratio):

[0031] Cleaning agent: MA-AA 2%

[0032] HEDP 6%

[0033] ATMP 8%

[0034] JFC 1‰

[0035] Water 84%

[0036] Corrosion inhibitor: 1‰ of the weight of CM-911 cleaning agent

[0037] preparation:

[0038] 1. First, add the water in the said proportion to the cleaning agent preparation container, and add the corrosion inhibitor (CM-911) and the penetrant (JFC) in the said proportion, and stir evenly.

[0039] 2. Add the ratio of MA-AA to the container of step 1, and stir evenly.

[0040] 3. Add HEDP in the stated proportion, stir again, and finally add ATMP in the stated proportion, and stir well to obtain product A, which is a light yellow transparent liquid and tasteless.

[0041] Descaling test:

[0042] Carbonate salt scale for the test, the scale thickness is 3.85mm, the temperature is 25°C, it is completely dissolved in 15 minutes, and the corrosion rate is 0.032g / m 2 .h.

[0043] Descaling application:

[0044] The prepared product A can be used to remove...

Embodiment 2

[0046] Formula (by weight ratio):

[0047] Cleaning agent: MA-AA 10%

[0048] HEDP 15%

[0049] ATMP 25%

[0050] JFC 1‰

[0051] Water 50%

[0052] Corrosion inhibitor: 2‰ of the weight of CM-911 cleaning agent

[0053] Preparation: The method and steps are the same as in Example 1, and product B is prepared.

[0054] Descaling test:

[0055] Carbonate salt scale for the test, the scale thickness is 3.85mm, the temperature is 20°C, it is completely dissolved in 18 minutes, and the corrosion rate is 0.033g / m 2 .h.

[0056] Descaling application:

[0057] The prepared product B can be used to remove silicate scale on the surface of carbon steel, and the cleaning temperature is 50°C.

Embodiment 3

[0059] Formula (by weight ratio):

[0060] Cleaning agent: MA-AA 15%

[0061] HEDP 20%

[0062] ATMP 30%

[0063] JFC 5‰

[0064] Water 34.5%

[0065] Corrosion inhibitor: 1‰ of the weight of CM-911 cleaning agent

[0066] Preparation: The method and steps are the same as in Example 1, and product C is obtained.

[0067] Descaling test:

[0068] Carbonate salt scale for test, scale thickness 3.58mm, temperature 25℃, completely dissolved in 13 minutes, corrosion rate 0.033g / m 2 .h.

[0069] Descaling application:

[0070] The prepared product C can be used to remove silicate scale on the surface of carbon steel, and the cleaning temperature is 50°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an organic descaling composition, which includes an organic cleaning agent and a corrosion inhibitor CM-911, and the weight ratio of the organic cleaning agent and the corrosioninhibitor is 100:0.1-0.3. The organic cleaning agent includes the follow components by weight: 1%-15% of maleic acid-crylic acid copolymer (MA-AA), 1%-25% of 1-hydroxyethylidene-1,1-diphosphonic acid(HEDP), 2%-30% of amino trimethylene phosphonic acid (ATMP), 0.03%-0.5% of penetrating agent JFC and balance of water. The organic descaling agent provided by the present invention has advantages offast reaction speed, small corrosivity for material and high descaling efficiency.

Description

Technical field [0001] The invention relates to a descaling composition, in particular to an organic descaling composition and its application. Background technique [0002] The water quality of the Yellow River basin in my country is poor. Short-term use will easily cause scale in the water heaters, automobile water tanks and other containers whose temperature can reach 30℃ or higher, which will affect the heat transfer performance of these equipment. When the scale thickness of the water heater reaches 2mm thick, the energy waste caused is about 25%. Compared with the thermal conductivity of metal, the thermal conductivity of metal is dozens or even hundreds of times higher than that of scale. . In areas with poor water quality, it takes only 2-3 months to form scale with a thickness of 2mm. Whether the water heater is used for a few months of scale removal will vary greatly in terms of energy consumption. The working effect of the car water tank is to dissipate heat and main...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C11D7/36B08B3/04B08B9/027C11D7/32C11D7/26
Inventor 董宇新
Owner 河南伯淼水处理有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com