Composite foaming agent for urea-formaldehyde resin, preparing method and application thereof

A technology of composite foaming agent and urea-formaldehyde resin, applied in the direction of aldehyde/ketone condensation polymer adhesive, adhesive type, adhesive additive, etc., can solve the problem of increased investment, inability to meet the operating time of plywood, and insufficient foam durability Good and other problems, to achieve the effect of improving fluidity, good uniformity and penetration balance, and moderate surface tension

Inactive Publication Date: 2012-04-25
EVERFIRST WISEFUND TECH BEIJING
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing adhesive foaming technology is generally suitable for low-viscosity, urea-formaldehyde resin without adding flour, and needs to increase special foaming equipment (rotating speed needs to be greater than 2000r / min) (for example, the invention patent with publication number CN1907552A), which is very important for mechanization Low-level plywood production enterprises undoubtedly need to increase investment in equipment and training operators. In addition, because the foam durability is not good enough, it cannot meet the needs of long operating times in plywood production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite foaming agent for urea-formaldehyde resin, preparing method and application thereof
  • Composite foaming agent for urea-formaldehyde resin, preparing method and application thereof
  • Composite foaming agent for urea-formaldehyde resin, preparing method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The preparation of embodiment 1 composite blowing agent

[0031] 1. Weigh each component according to the following weight:

[0032] Foaming agent 500g, guar gum 100g, sodium dodecylbenzenesulfonate 100g;

[0033] Wherein the foaming agent is obtained by mixing the following components by weight: 2 parts of dehydrated alum, 7 parts of sodium bicarbonate, 4 parts of calcium carbonate, and 7 parts of ammonium sulfate;

[0034] 2. The above-mentioned components are mechanically crushed to a particle size of 100-200 microns, and then mixed evenly to obtain the product.

Embodiment 2

[0035] The preparation of embodiment 2 composite blowing agent

[0036] 1. Weigh each component according to the following weight:

[0037] Foaming agent 450g, bone glue 90g, sodium dodecylbenzenesulfonate 90g;

[0038] Wherein the foaming agent is obtained by mixing the following components by weight: 2 parts of dehydrated alum, 6 parts of sodium bicarbonate, 3 parts of calcium carbonate, and 5 parts of ammonium sulfate;

[0039] 2. The above-mentioned components are pulverized to a particle size of 100-200 microns by means of jet milling, and then mixed evenly to obtain the final product.

Embodiment 3

[0040] Embodiment 3 Preparation of Composite Blowing Agent

[0041] 1. Weigh each component according to the following weight:

[0042] Foaming agent 550g, polyacrylamide 110g, sodium lauryl sulfate 110g;

[0043] Wherein the foaming agent is obtained by mixing the following components by weight: 3 parts of dehydrated alum, 9 parts of sodium bicarbonate, 5 parts of calcium carbonate, and 8 parts of ammonium sulfate;

[0044] 2. The above-mentioned components are pulverized by mechanical pulverization and mixed evenly to obtain the product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The present invention discloses a composite foaming agent for urea-formaldehyde resin, a preparing method and an application thereof. The composite foaming agent of the invention is composed of a foaming agent, a foam stabilizer and a dispersing agent. After the composite foaming agent is added into the urea-formaldehyde resin additive, the volume of the urea-formaldehyde resin can be increased for 2-3 times for forming the fine, uniform and long-lasting foamed urea-formaldehyde resin, effectively regulating the surface tension of the glue solution, reducing the conglobation phenomenon of flour, increasing the fluidity of the urea-formaldehyde resin, settling the adverse phenomena of glue bleeding, glue leakage, non-homogeneous adhesive layer, etc. which commonly exist in the prior urea-formaldehyde resin adhesive, so that the urea-formaldehyde resin on the plate blank of the veneer board has excellent homogeneity and the bleeding balancing is kept and the total usage of flour and theurea-formaldehyde resin after adhesive mixing is reduced for 10-30%. Additionally, the composite foaming agent of the invention has the advantages of excellent safety, no adverse effect in the using process and capability for effectively reducing the release amount of the formaldehyde of the artificial board. Furthermore the mechanical properties of the prepared artificial board can equally obtainthe requirement of the national standard.

Description

technical field [0001] The present invention relates to a composite foaming agent and a preparation method thereof, in particular to a composite foaming agent for urea-formaldehyde resin adhesives used in the manufacture of wood-based panels and a preparation method thereof. The present invention also relates to urea-formaldehyde containing the composite foaming agent The invention relates to a resin adhesive and its application in manufacturing wood-based panels, belonging to the field of wood adhesive additives. Background technique [0002] Over the past 30 years of reform and opening up, China's wood industry has developed rapidly, especially the production and consumption of wood-based panels has ranked first in the world. As a major producer of wood-based panels in the world, China's wood-based panel production reached 88.3858 million cubic meters in 2007, an increase of 18.98% over 2006, and the growth rate remained stable. Correspondingly, my country's wood adhesive...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J161/24C09J11/04
Inventor 雷得定王然
Owner EVERFIRST WISEFUND TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products