Polymer for PP-R high polymer

A PP-R, 1. PP-R technology, applied in the field of masterbatch of plastic products, can solve the problems of small filling, low strength, and product quality impact

Inactive Publication Date: 2011-09-21
沈阳大圆天地塑料制品有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing plastic masterbatch has a small amount of filling, any kind of filling will have an impact on product quality, and there is no way to improve such a situation at present
Moreover, the strength of the existing plastic masterbatch is low, and the toughness needs to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The polymer for PP-R macromolecule of the present invention is prepared from the following raw materials according to the stated parts by weight: 66 parts of calcium carbonate, 1.5 parts of lubricant, 0.5 part of polyethylene wax, 0.5 part of polypropylene wax, 0.5 part of polypropylene wax, 11 parts of ethylene, 5 parts of polypropylene, 3 parts of coupling agent, 1 part of zinc stearate, 1.5 parts of stearic acid, 10 parts of talcum powder.

[0015] Its preparation method is as follows:

[0016] 1. Prepare small ingredients first:

[0017] Put lubricant, polyethylene wax, polypropylene wax, zinc stearate, and stearic acid into the mixing pot according to the above ratio, and the temperature is raised to 100-120 degrees, and stirred for 10 minutes to make the material into a paste mixture;

[0018] 2. Activation:

[0019] (1) After the mixing pot is turned on, calcium carbonate and talcum powder are added to the pasty mixture according to the ratio;

[0020] (2) Pre...

Embodiment 2

[0028] The polymer for PP-R macromolecule of the present invention is prepared by the following raw materials according to the stated parts by weight: 55 parts of calcium carbonate, 1 part of lubricant, 0.3 part of polyethylene wax, 0.3 part of polypropylene wax, 0.3 part of polypropylene wax, 5 parts of ethylene, 3 parts of polypropylene, 1 part of coupling agent, 0.5 parts of zinc stearate, 1 part of stearic acid, 15 parts of talcum powder.

[0029] The coupling agent used in this example is an aluminate coupling agent. The lubricant is 303A lubricant.

[0030] Its preparation method is with embodiment 1.

Embodiment 3

[0032] The modified plastic masterbatch for PP-R of the present invention is prepared by the following raw materials according to the stated parts by weight: 75 parts of calcium carbonate, 3 parts of lubricant, 0.8 part of polyethylene wax, 0.8 part of polypropylene wax, 15 parts of polyethylene, 8 parts of polypropylene, 5 parts of coupling agent, 2. parts of zinc stearate, 3 parts of stearic acid, 5 parts of talcum powder.

[0033] The coupling agent used in this embodiment is titanate coupling agent. The lubricant is 303A lubricant.

[0034] Its preparation method is with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a master batch of plastic products, in particular to a polymer for PP-R high polymer. The polymer for PP-R high polymer comprises the following raw materials according to the parts by weight: 55-75 of calcium carbonate, 1-3 of lubricant, 0.3-0.8 of polyethylene wax, 0.3-0.8 of polypropylene wax, 5-15 of polyethylene, 3-8 of polypropylene, 1-5 of coupling agent, 0.5-2.5 of zinc stearate, 1-3 of stearic acid and 5-15 of talcum powder. The polymer for PP-R high polymer of the invention fills the gap of the field; the invention has large filling volume, and the original physical properties of the polymer can be kept after being filled; the invention is characterized by high strength and toughness, good sizing and the like and the cost of the manufacturers of PP-R products can be largely decreased. Under the current situation of energy scarcity, a great amount of energy can be saved.

Description

technical field [0001] The invention relates to a masterbatch of plastic products, in particular to a polymer for PP-R macromolecule. Background technique [0002] At present, PP-R special plastic masterbatch is still blank, and the price of other plastic masterbatch raw materials has been high, so PP-R modified plastic masterbatch products have remained high. The existing plastic masterbatch has a small amount of filling, and any kind of filling will have an impact on product quality, and there is no way to improve such a situation at present. Moreover, the strength of the existing plastic masterbatch is low, and the toughness needs to be further improved. Contents of the invention [0003] In order to solve the above technical problems, the present invention provides a polymer for PP-R polymer, which has large filling capacity, low cost, high strength, increased toughness, good shaping, and can save a lot of energy. toxic free and safe. [0004] In order to solve the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08L23/12C08K13/02C08K3/26C08K5/098C08K5/09C08K3/34
Inventor 毕忠义
Owner 沈阳大圆天地塑料制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com