Resin composition for forming heat-cured film
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of resin composition and thermal curing, which is applied in the field of resin composition for thermal curing film formation and cured film, can solve the problems of flatness and transparency reduction, and achieve simplification and low cost, high flatness, and high transparency sexual effect
Active Publication Date: 2010-03-24
NISSAN CHEM IND LTD
View PDF3 Cites 16 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, if it is regarded as a flattening film of a color filter, there are problems such as a large decrease in flatness and transparency.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment
[0134] Hereinafter, examples are given and the present invention will be described in more detail, but the present invention is not limited to these examples.
[0135] [Abbreviations used in Examples]
[0136]The meanings of the abbreviated symbols used in the examples below are as follows.
[0147] [Determination of number average molecular weight and weight average molecular weight]
...
Synthetic example 1
[0150] A polyimide precursor solution (solid content concentration: 30.0 mass %) was obtained by making CBDA 14.7g, TDA 22.5g, and DDS 26.1 react in NMP 147.7g at 23 degreeC for 24 hours (P1). Mn of the obtained polyimide precursor was 2,000, and Mw was 3,500.
Synthetic example 2
[0152] A polyimide precursor solution (solid content concentration: 30.0 mass %) was obtained by making CBDA 19.6g and DDS 17.4 react in NMP 86.3g at 23 degreeC for 24 hours (P2). Mn of the obtained polyimide precursor was 3,200, and Mw was 5,500.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
thickness
aaaaa
aaaaa
Login to View More
Abstract
To provide a resin composition for heat-cured-film formation which can form a cured film having the property of aligning liquid crystals and realizing high transparency and high planarization. ¢MEANSFOR SOLVING PROBLEMS! The resin composition for heat-cured-film formation comprises ingredients (A) and (B). Ingredient (A): A polyimide precursor having structural units represented by the followingformulae (1) and (2). Ingredient (B): A bismaleimide compound. (In the formulae, A1 is an organic group including an alicyclic structure; A2 is an organic group comprising a structure having an organic group including a structure formed by the fusion of an aliphatic ring with a benzene ring; at least one of B1 and B2 is an organic group including the structure -SO2-; and R1, R2, R3, and R4 each independently represents hydrogen or a C1-7 organic group.
Description
technical field [0001] The present invention relates to a resin composition for forming a thermosetting film and a cured film obtained from the composition. More specifically, it relates to a resin composition for forming a thermosetting film containing a polyimide precursor having high flatness during step coating and having liquid crystal orientation, a cured film thereof, and applications of the cured film. This composition for thermosetting film formation is used especially suitably as a color filter coating agent which has the function of aligning a liquid crystal in a liquid crystal display. Background technique [0002] In general, in optical devices such as liquid crystal display elements, organic EL (electroluminescent) elements, and solid-state imaging elements, a protective film is provided to prevent the element surface from being exposed to solvents and heat during the manufacturing process. Such a protective film requires not only high adhesion to the substrat...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 