Maize fiber multifunctional line

A corn fiber, multi-functional technology, used in heating/cooling fabrics, textiles and papermaking, fabric surface trimming, etc., can solve the problem that corn fiber yarn cannot be used for embroidery and sewing, etc. colorful effect

Active Publication Date: 2012-05-23
SHANGHAI SHUIXING HOME TEXTILE
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] The technical problem to be solved by the present invention is to provide a corn fiber multifunctional thread in the first aspect, which can make up for the defects that the corn fiber yarn produced by the existing technology cannot be used for embroidery and sewing.
[0012] The technical problem to be solved by the present invention The second aspect is to provide a production method of corn fiber multifunctional thread to solve the problems existing in the existing production process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The corn fiber multifunctional thread of the present invention is woven from 100% corn fiber, and the corn fiber is long corn fiber.

[0031] In this embodiment, the production method of the corn fiber multifunctional thread includes a thread making step and a dyeing step, the manufacturing step includes: corn fiber long fiber winding, normal temperature setting, compound twisting, twisting; the dyeing step includes : Preheating and shaping, degreasing, dyeing, color fixing, drying, doffing, packaging finished products.

[0032] 1. Manufacturing steps

[0033] (1) winding wire:

[0034] Use a KV2000 high-speed computer with side bobbins to carry out PLA long fiber winding. The speed of winding is 3000 rpm, the tension is 1-2 N, and the weight is 250 grams per piece, so that the tension is uniform and the size is uniform.

[0035] The finished PLA long fiber is naturally set on the cylinder for 40 hours, so as to increase the twistability of the PLA long fiber.

[003...

Embodiment 2

[0056] The corn fiber multifunctional thread of the present invention is woven from 100% corn fiber, and the corn fiber is long corn fiber.

[0057] In this embodiment, the production method of the corn fiber multifunctional thread includes a thread making step and a dyeing step, the manufacturing step includes: corn fiber long fiber winding, normal temperature setting, compound twisting, twisting; the dyeing step includes : Preheating and shaping, degreasing, dyeing, color fixing, drying, doffing, packaging finished products.

[0058] 1. Manufacturing steps

[0059] (1) winding wire:

[0060] Use a KV2000 high-speed computer with side bobbins to wind PLA long fibers. The speed of winding is 4000 rpm, the tension is 1-2 N, and the weight is 500 grams per piece, so that the tension is uniform and the size is uniform.

[0061] The finished PLA long fiber is naturally set on the cylinder for 50 hours, so as to increase the twistability of the PLA long fiber.

[0062] (2) Compo...

Embodiment 3

[0081] The corn fiber multifunctional thread of the present invention is woven from 100% corn fiber, and the corn fiber is long corn fiber.

[0082] In this embodiment, the production method of the corn fiber multifunctional thread includes a thread making step and a dyeing step, the manufacturing step includes: corn fiber long fiber winding, normal temperature setting, compound twisting, twisting; the dyeing step includes : Preheating and shaping, degreasing, dyeing, color fixing, drying, doffing, packaging finished products.

[0083] 1. Manufacturing steps

[0084] (1) winding wire:

[0085] Use a KV2000 high-speed computer with side bobbins to wind PLA long fibers. The speed of winding is 3500 rpm, the tension is 1-2 N, and the weight is 250 grams per piece, so that the tension is uniform and the size is uniform.

[0086] The finished PLA long fiber is naturally set on the cylinder for 48 hours, so as to increase the twistability of the PLA long fiber.

[0087] (2) Compo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a maize fiber multifunctional line which is manufactured by 100% of maize fiber. The maize fiber is long fiber, and the preparation method thereof comprises a line manufacturing step and a dying step, wherein, the line manufacture step comprises reeling of maize fiber long fiber, sizing at normal temperature, compound twisted thread and skeining; and the dying step comprises preheating and sizing, degreasing, dying, color fixing, stoving, doffing and packaging to obtain the finished product. Compared with the petroleum chemical fiber functional line, the maize fiber multifunctional line has the advantages of environmental protection, moisture absorption, perspiration and being beneficial to preventing bacterial growth and the like, has the health maintenance performance, such as the reduction of human body allergic source of the diseases and the like when being applied to the technologies of textile embroidery, sewing and the like, and has the characteristics of smooth pattern, soft handfeel, brilliant color, difficult color fading, light, thin and comfort wearness, moisture absorption, ventilation and the like; in addition, the maize fiber functional line has higher flame resistance, slow combustion, and initial fireproof performance to prevent fire caused by accident combustion when being used for the above applications, and realizes the purposes of the invention.

Description

technical field [0001] The invention relates to a corn fiber thread and a production method thereof, in particular to a corn fiber multifunctional thread woven from corn fiber and a production method thereof. Background technique [0002] With the advancement of science and technology and the improvement of market requirements, textile raw materials have developed rapidly in the past ten years, and new functional fibers have been developed and applied in large quantities; on the other hand, some green and environmentally friendly fibers are also very popular in the market. In the field of environmental protection, it has become the target development direction of the world to make every effort to recycle and reuse and save resources. [0003] In recent years, the American Grain Association and Cargill-Dow (CARGILL-DOW) Polymer Company and Japan Zhongbo Fiber Co., Ltd. have jointly developed a new type of environmentally friendly fiber, which is polylactic acid fiber made fro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D02G3/02D02G1/02D06C7/02
Inventor 林孝建余宝林
Owner SHANGHAI SHUIXING HOME TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com