Gas shield welding wire with high strength and tenacity

A technology of gas-shielded welding wire and high toughness, which is applied in the field of gas-shielded welding of 800MPa high-strength steel and high-strength and high-toughness gas-shielded welding wire. Issues such as cost and difficulty of welding

Active Publication Date: 2010-06-09
SHOUGANG CORPORATION
View PDF0 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Construction machinery, hydropower and water conservancy, petrochemical and other industries have begun to use a large number of steel grades with a strength level of 800Mpa. However, the research and development of welding materials for this ultra-high-strength steel in China is still lagging behind, and the existing welding wires are less than equal. Even if a small amount of successfully developed welding wire is not costly and requires heat treatment after welding, the low-temperature impact toughness and manufacturability of the weld metal cannot meet the requirements. In addition, the content of Mo and Ni in the currently developed welding wire is very high. Moreover, preheating is required during the welding process, which greatly increases the cost and welding difficulty of the welding wire. Therefore, it is very urgent to develop a gas-shielded welding wire with high strength, high toughness and good manufacturability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment example 1

[0017] The preparation of the welding wire is carried out according to the test requirements, and the desulfurized hot metal is used to control the sulfur content of the molten iron. The converter steel is used to select raw materials with low S and P content. The top-bottom composite blowing process is used to strictly control the steelmaking end point Composition, tapping temperature and other parameters, the billet is hot-rolled into a Φ5.5mm wire rod, and the surface is descaled and wire-drawn to make a Φ1.2mm copper-coated or non-copper-coated welding wire. The chemical composition of the welding wire is: C 0.04; Si 0.46; Mn 2.05; P<0.010; S<0.010; Cr 0.92; Mo 0.94; Ti 0.09;

[0018] The cladding metal welding test under the protection of mixed protective gas (95%Ar+5%CO2) is used to complete, the specific specifications are: current 270-300A, welding voltage 28-30V, welding speed 24-30cm / min. The thickness of the welding test plate is 25mm, with a 15mm backing plate, the...

Embodiment example 2

[0020] Using the same process as Case 1 to smelt and draw the welding wire, the obtained welding wire composition is: C 0.032; Si 0.61; Mn 2.15; Pm =875MPa, R eL =815MPa, impact energy A at -50℃ KV =162J.

Embodiment example 3

[0022] Using the same process as Case 1 to smelt and draw the welding wire, the obtained welding wire composition is: C 0.048; Si 0.56; Mn 2.10; Pm =845MPa, R eL =790MPa, impact energy A at -50℃ KV =87J.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a gas shield welding wire with high strength and tenacity, which is suitable for the welding of 800MPa-grade high-strength steel. The gas shield welding wire comprises the following ingredients in percentage by weight: 0.02-0.05 percent of C, 0.30-0.80 percent of SiO, 2.0-2.50 percent of Mn, less than 0.010 percent of P, less than 0.010 percent of S, 0.70-1.2 percent of Cr, 0.70-1.2 percent of Mo, 0.02-0.12 percent of Ti, 0.003-0.005 percent of B, 2.0-3.2 percent of Ni, 0.05-0.1 percent of RE, 0-0.06 percent of Nb, and the balance of Fe and unavoidable impurities. The welding wire has the advantages of simple ingredient design, low cost, good manufacturability, and the like; in addition, and weld metal has high tenacity and is suitable for the welding at the position with higher low-temperature tenacity requirement. Experiments show that the Rm of the weld metal welded by the welding wire is not less than 800MPa, and the ReL is more than 760MPa; and the impact energy at -50 DEG C of the weld metal is not less than 37J.

Description

technical field [0001] The invention relates to a high-strength and high-toughness gas-shielded welding wire, which belongs to the field of matching welding materials for high-strength steel, and is particularly suitable for gas-shielded welding of 800MPa high-strength steel. Background technique [0002] With the rapid development of my country's industry, the strength level of steel materials is gradually developing in the direction of high strength and high toughness. Construction machinery, hydropower and water conservancy, petrochemical and other industries have begun to use a large number of steel grades with a strength level of 800Mpa. However, the research and development of welding materials for this ultra-high-strength steel in China is still lagging behind, and the existing welding wires are less than equal. Even if a small amount of successfully developed welding wire is not costly and requires heat treatment after welding, the low-temperature impact toughness an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/30
Inventor 许良红章军陈延清
Owner SHOUGANG CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products