Coal-series hard kaolinite stripping method capable of keeping crystal form of kaolinite

A technology of kaolinite and coal measures, applied in chemical instruments and methods, inorganic chemistry, non-metallic elements, etc., can solve the problems of complex process, difficult to keep the crystal shape intact, not easy to large-scale industrial production, etc., and achieve a low degree of damage. Effect

Inactive Publication Date: 2010-06-23
CHINA UNIV OF MINING & TECH (BEIJING)
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] The methods used in the above-mentioned related inventions are all grinding or ultrasonic treatment after intercalation, and the process is complicated, the crystal shape is difficult to keep intact, and it is not easy to carry out large-scale industrial production
No flaking method for coal-measure kaolinite with good crystal shape has been found so far

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coal-series hard kaolinite stripping method capable of keeping crystal form of kaolinite
  • Coal-series hard kaolinite stripping method capable of keeping crystal form of kaolinite
  • Coal-series hard kaolinite stripping method capable of keeping crystal form of kaolinite

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] The coarse crystalline kaolinite was selected and crushed into 325 mesh. The intercalation composite system slurry was prepared at a mass ratio of kaolin: water: hydrazine hydrate = 1:2:0.15, and stirred slowly for 12 hours. Pour the prepared kaolin slurry into the grinding and peeling bucket filled with medium balls. The mass ratio of medium balls with different particle sizes (0.8-1.2mm, 1.5-2.0mm, 2.0-2.5mm) is 3:2:1. The mass ratio to the medium ball is 1:1. Adjust the rotating speed of the grinding and peeling machine to 1200 rpm, and grind and peel for 1.5 hours. Filter, wash with 3 times of water, finally make 45% mud, and then spray dry to get the product. The obtained product D97=1.9 μm, the thickness of the wafer is ≤200nm, about 30% has hexagonal crystal shape, and the ratio of diameter to thickness is 10:1. See attached figure 1 .

Embodiment 2

[0046] Mesocrystalline kaolinite was selected and crushed to 325 mesh. The intercalation composite system slurry was prepared according to the mass ratio of kaolin: water: formamide = 1: 1.5: 0.2, and stirred slowly for 15 hours. Mix medium balls with diameters of 0.8-1.2mm, 1.5-2.0mm, and 2.0-2.5mm in a mass ratio of 3:2:1, pour them into the grinding and peeling bucket, and then pour kaolin mud into it to make the mud and The mass ratio of the medium balls is 1:1.2. Adjust the rotating speed of the grinding and peeling machine to 1300 rpm, and grind and peel for 1.0 hour. Filter, wash with 5 times of water, finally make 45% mud, and then spray dry to get the product. The obtained product D97=1.5 μm, the thickness of the wafer is ≤100 nm, about 60% has a hexagonal crystal shape, and the aspect ratio is 20:1. See attached figure 2 .

Embodiment 3

[0048] Fine-grained kaolinite was selected and crushed into 250 mesh. The intercalation composite system slurry was prepared at a mass ratio of kaolin: water: dimethyl sulfoxide = 1:3:0.3, heated at 70°C and stirred slowly for 30 hours. Mix medium balls with diameters of 0.8-1.2mm, 1.5-2.0mm, and 2.0-2.5mm according to the mass ratio of 3:2:1, pour them into the grinding and peeling bucket, and then pour kaolin mud to make the mud and the medium The mass ratio of the balls is 1:1.5. Adjust the rotating speed of the grinding and peeling machine to 1500 rpm, and grind and peel for 1.5 hours. Filter and wash with 5 times of water, finally make 40% mud, and then spray dry to get the product. The obtained product D97=1.0 μm, the thickness of the wafer is ≤50 nm, about 60% has a hexagonal crystal shape, and the diameter-thickness ratio is 10:1. See attached image 3 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a coal-series hard kaolinite stripping method. The method comprises the following steps of: crushing the coal-series hard kaolinite, mixing the crushed coal-series hard kaolinite with water and an intercalator to obtain intercalated compound pulp, striping the intercalated compound pulp by using medium spheres of three types grain sizes, and performing filtration washing and spray-drying to obtain the finished product. By the method, the hexagonal sheet-shaped crystal form of the kaolinite is kept relatively complete, and the content of hexagonal sheet-shaped kaolinite crystals is 30 to 60 percent.

Description

technical field [0001] The invention relates to a preparation method of ultrafine kaolin, which belongs to the technical field of preparation of inorganic ultrafine powder materials. Background technique [0002] There are abundant kaolinite resources in my country's coal-bearing strata, and its resources are predicted to reach more than 18 billion tons. This kind of minerals generally occurs in the gangue or roof and floor of coal seams, and was previously discarded as ore. In order to make full use of coal resources and develop circular economy, there has been an upsurge in the development of coal-measure kaolinites in my country's coal mining areas in the past ten years. At present, more than 50 coal-measure kaolinite processing enterprises have been established in the coal mining areas of Shanxi, Inner Mongolia, Henan, Shandong, Hebei and other provinces in my country, and the cumulative annual output of the country has reached 600,000-800,000 tons. Coal-measure kaolin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01B33/40C01B33/44
Inventor 刘钦甫程宏飞
Owner CHINA UNIV OF MINING & TECH (BEIJING)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap