Water-permeable road edge batten and manufacturing method thereof

A technology for layering and curbs, which is applied to manufacturing tools, gutter/curbstone, ceramic molding machines, etc., can solve the problems that the layering does not have water permeable natural breathing and anti-skid, cannot effectively supplement groundwater, and unfavorable growth of green plants, etc. Achieve the effect of overcoming easy breakage, cost-effective, and not easy to fade

Inactive Publication Date: 2010-06-23
广州市坚基环保数码彩砖有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, with the continuous improvement of people's living standards, people's requirements for the surrounding environment of the residence are also getting higher and higher. The traditional layering on the sidewalk is mostly natural marble layering or cement molded roadside layering. Because these layerings It does not have the functions of water permeability, water seepage, water storage, ventilation and heat dissipation, natural breathing and anti-skid. Therefore, especially after rainy and snowy days, the rainwater cannot quickly penetrate into the ground with the layering, resulting in a large amount of rainwater accumulating on the layering and cement pavement surrounding areas, resulting in soil erosion, unable to effectively replenish groundwater, and detrimental to the growth of surrounding green plants
At the same time, because the surface of the traditional bead is too smooth, it is easy for pedestrians to slip and fall when walking on it after rainy and snowy days, which will also have a certain impact on pedestrian traffic safety. In addition, the compressive strength of the traditional cement molded roadside bead is 30 MPa Below, and therefore prone to breakage under the weight of the vehicle, resulting in prohibitively expensive repairs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Take the production of red 1000*250*100mm permeable road bead as an example to describe in detail. First, weigh 500Kg of the fabric, including 350Kg of white corundum with a diameter of 2.5mm, and 115Kg of high-standard silicate P.I42.5R grade gray cement. Red iron oxide pigment 3.5Kg, water 31.5Kg; then weigh 1500Kg of base material, including 185Kg of stones with a diameter of 20mm, 185Kg of stones with a diameter of 15mm, 370Kg of stones with a diameter of 8mm, 370Kg of refined sand with a diameter of 6mm, and coarse sand with a diameter of 1-6mm 120Kg, high standard silicate P.I42.5R grade gray cement 230Kg, water 40Kg.

[0026] Its production method is as follows:

[0027] Preparation of fabric: Put 350Kg of white corundum with a diameter of 2.5mm, 3.5Kg of red iron oxide pigment, 115Kg of high-standard silicate P.I42.5R grade gray cement, and 31.5Kg of water into a fabric mixer and stir until it becomes thick shape.

[0028] Preparation of base material: Weigh 1...

Embodiment 2

[0032] Taking the production of orange 1000*250*100mm permeable road bead as an example to describe in detail, first weigh 418Kg of the fabric, including 300Kg of white corundum with a diameter of 2.5mm, and 100Kg of high-standard silicate P.I42.5R grade gray cement. 3Kg of orange iron oxide pigment, 15Kg of water; weigh 1220Kg of base material, including 150Kg of stones with a diameter of 20mm, 150Kg of stones with a diameter of 15mm, 300Kg of stones with a diameter of 8mm, 300Kg of refined sand with a diameter of 6mm, and 100Kg of coarse sand with a diameter of 1-6mm. High standard Portland P.I42.5R grade gray cement 190Kg, water 30Kg.

[0033] Its production method is as follows:

[0034] Preparation of fabric: Put 300Kg of white corundum with a diameter of 2.5mm, 3Kg of orange iron oxide pigment, 100Kg of high-standard silicate P.I42.5R grade gray cement, and 15Kg of water into a fabric mixer and stir into a viscous shape.

[0035] Preparation of base material: Weigh 150K...

Embodiment 3

[0039] Taking the production of black 1000*250*100mm permeable road bead as an example to describe in detail, first weigh 500Kg of the fabric, including 350Kg of white corundum with a diameter of 2.5mm, and 115Kg of high-standard silicate P.I42.5R grade gray cement. 3.5Kg of black iron oxide pigment, 31.5Kg of water; weigh 1000Kg of base material, including 125Kg of stones with a diameter of 20mm, 125Kg of stones with a diameter of 15mm, 245Kg of stones with a diameter of 8mm, 245Kg of refined sand with a diameter of 6mm, and coarse sand with a diameter of 1-6mm 85Kg, high standard Portland P.I42.5R grade gray cement 155Kg, water 20Kg.

[0040] Its production method is as follows:

[0041] Preparation of fabrics: Put 350Kg of white corundum with a diameter of 2.5mm, 3.5Kg of black iron oxide pigments, 115Kg of high-standard silicate P.I42.5R grade gray cement, and 31.5Kg of water into a fabric mixer and stir until it becomes thick shape.

[0042] Preparation of base material: ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a water-permeable road edge batten, mainly comprising surface materials and bottom materials, wherein the surface materials comprise carborundum, high-strength silicate P.I42.5R level of cement, pigment and water; and the bottom materials comprise three types of stones with different diameters, refined sand, grit, high-strength silicate P.I42.5R level of cement and water. The invention also discloses a preparation method of the water-permeable road edge batten, comprising the steps: preparation of the surface materials: mixing carborundum, high-strength silicate P.I42.5R level of cement and pigment according to the proportion, then putting the obtained mixture into a stirrer for the surface materials, adding water, stirring into viscous mixture, and the like. The invention not only can effectively solve the problems of the impounded water of the road and the water splash when vehicles pass, but also can absorb and discharge water quickly on raining days, thus ensuring that the rain can permeate the earth surface well to supply the underground water effectively, giving full play to the advantage that soil can adjust the temperature and the humidity of cities, and maintaining the ecological balance of the city surface.

Description

technical field [0001] The invention relates to a water-permeable roadside bead, in particular to a water-permeable roadside bead which is paved on the side of a road and can quickly permeate water and keep the surrounding environment free from water accumulation and a manufacturing method thereof. Background technique [0002] At present, with the continuous improvement of people's living standards, people's requirements for the surrounding environment of the residence are also getting higher and higher. The traditional layering on the sidewalk is mostly natural marble layering or cement molded roadside layering. Because these layerings It does not have the functions of water permeability, water seepage, water storage, ventilation and heat dissipation, natural breathing and anti-skid. Therefore, especially after rainy and snowy days, the rainwater cannot quickly penetrate into the ground with the layering, resulting in a large amount of rainwater accumulating on the layering...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E01C11/22C04B28/04B28B1/087
Inventor 赖友谷
Owner 广州市坚基环保数码彩砖有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products