Method for preparing material containing amorphous iron oxide hydroxide and methods for regenerating the same
An iron oxyhydroxide, amorphous technology, applied in the direction of iron oxide/iron hydroxide, etc., can solve the problem of low content of amorphous iron oxyhydroxide, and achieve the effects of slow oxidation speed, good desulfurization effect and fast oxidation speed.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0018] Example 1
[0019] Preparation of materials containing amorphous iron oxyhydroxide:
[0020] 152 g FeSO 4 Prepare the aqueous solution and place it in the reaction kettle, add 58 grams of solid Na under stirring conditions 2 CO 3 Finally, the pH of the mixed aqueous solution was adjusted to 8, after 0.5 hours of reaction, filtered, and the filter cake was washed with water until Na in the filter cake + The content of the filter cake is less than 0.5%, and then the filter cake is prepared into an aqueous suspension with a solid mass percentage of 30%, and air is oxidized until Fe 2+ / Fe total If it is less than 1%, the material is completely oxidized, filtered, and dried at 100°C to obtain a material containing amorphous iron oxyhydroxide. The mass percentage of amorphous iron oxyhydroxide in the material is 85%, and the rest is Na 2 SO 4 , Water and TiO 2 (TiO 2 FeSO 4 The impurities in the salt are the same in the following examples), and the sulfur capacity of the material ...
Example Embodiment
[0025] Example 2
[0026] Preparation of materials containing amorphous iron oxyhydroxide:
[0027] 127 g FeCl 2 Prepare the aqueous solution and place it in the reaction kettle, and put 88 grams of solid K under stirring conditions 2 CO 3 , Carry out the reaction, adjust the pH of the mixed solution to 8.01 hours, filter, wash the filter cake with water until K in the filter cake + The content of the filter cake is less than 0.5%, and then the filter cake is prepared into an aqueous suspension with a solid mass percentage of 15%, and air is oxidized until Fe 2+ / Fe total If it is less than 1%, the material is completely oxidized, filtered, and dried at 90°C to obtain a material containing amorphous iron oxyhydroxide. The mass percentage of amorphous iron oxyhydroxide in the material is 80%, and the rest is KCl , Moisture, ferroferric oxide and unknown impurities, the sulfur capacity of the material is 49.6%. Where K + The content is determined by flame photometry, and the followi...
Example Embodiment
[0033] Example 3
[0034] Preparation of materials containing amorphous iron oxyhydroxide:
[0035] 152 g FeSO 4 ·7H 2 The aqueous solution of O is placed in the reaction kettle, and 92 grams of solid NaHCO is added under stirring conditions 3 , Carry out the reaction, adjust the pH of the mixed solution to 8, 0.5 hours later, filter, and wash the filter cake with water until Na is in the filter cake + The content of the filter cake is less than 0.5%, and then the filter cake is prepared into an aqueous suspension with a solid mass percentage of 30%, and air is oxidized until Fe 2+ / Fe total If it is less than 1%, the material is completely oxidized, filtered, and dried at 45°C to obtain a material containing amorphous iron oxyhydroxide. The mass percentage of amorphous iron oxyhydroxide in the material is 80%, and the rest is Na 2 SO 4 , Water, TiO 2 , The sulfur capacity of the material is 49.6%.
[0036] Regeneration method 1:
[0037] The material containing amorphous iron oxyhydr...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap