A storage-resistant rubber powder modified asphalt and its preparation method

A modified asphalt and storage-resistant technology, which is applied in building components, building insulation materials, buildings, etc., can solve the problems that rubber asphalt cannot meet the design requirements, rubber asphalt cannot be stored overnight, and mixture design failures, etc., to achieve low prices , Reduce product cost, good performance attenuation resistance and low temperature crack resistance

Inactive Publication Date: 2011-11-30
SHENYANG SANXIN GROUP PANJIN ROAD MATERIALS
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, experiments and physical engineering have proved that when the rubber powder modified asphalt is heated to 185-195°C, if it is not used immediately, the viscosity of the rubber asphalt will be less than 1 Pa.s at 180°C after being stored for 2 days, and the softening point will decay to about 50°C. As a result, the rubber asphalt does not meet the design requirements, the design of the mixture fails, the rubber asphalt cannot be stored overnight, and the rubber asphalt is discarded in case of rain or construction failure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Take 7.8t of Liaohe No. 90 asphalt and heat it to 180°C in a reactor, then add 2.2t of waste tire rubber powder with a water content of less than 5%, a metal content of less than 0.4%, an ash content of less than 8%, and a mesh size of 30 mesh. Containing 0.25% dicumyl peroxide in the mass fraction of the rubber powder, adding 0.3% alkylphenol polysulfide in the rubber powder mass, stirring at a low speed (300-1000 rpm) for 15 minutes in a mixing tank, Raise the temperature to 190°C, then grind it again with a high-speed shearing machine, pump it to a storage tank for development, and add an anti-reversion agent of 0.15% of the rubber powder mass to the developed product, wherein the anti-reversion agent is bismaleimide and stir evenly to obtain storable rubber powder modified asphalt.

Embodiment 2

[0026] Take 8.5t of Liaohe No. 90 asphalt and heat it to 180°C in a reaction kettle, then add 1.5t of waste tire rubber powder with a water content of less than 5%, a metal content of less than 0.4%, an ash content of less than 8%, and a mesh size of 30 mesh. Containing 0.25% dicumyl peroxide in the mass fraction of the rubber powder, adding 0.3% alkylphenol polysulfide in the rubber powder mass, stirring at a low speed (300-1000 rpm) for 15 minutes in a mixing tank, Raise the temperature to 190°C, then grind it again with a high-speed shearing machine, pump it to a storage tank for development, add an anti-reversion agent of 0.15% of the rubber powder mass to the developed product, wherein the anti-reversion agent is a silane tetrasulfide compound, and stir Evenly, the storable rubber powder modified asphalt is obtained.

Embodiment 3

[0028] Take 7.9 tons of Liaohe No. 90 asphalt and heat it to 180°C in a reaction kettle, then add 2.1 tons of waste tire rubber powder with a water content of less than 5%, a metal content of less than 0.4%, an ash content of less than 8%, and a mesh size of 30 mesh. Containing 0.25% dicumyl peroxide in the mass fraction of the rubber powder, adding 0.3% alkylphenol polysulfide in the rubber powder mass, stirring at a low speed (300-1000 rpm) for 15 minutes in a mixing tank, Raise the temperature to 190°C, then grind it again with a high-speed shearing machine, pump it to a storage tank for development, add an anti-reversion agent of 0.15% of the rubber powder mass to the developed product, wherein the anti-reversion agent is a silane tetrasulfide compound, and stir Evenly, the storable rubber powder modified asphalt is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
penetrationaaaaaaaaaa
penetrationaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to view more

Abstract

A storage-resistant rubber powder modified asphalt, characterized in that: the storage-resistant rubber powder modified asphalt is composed of asphalt, rubber powder, activator, and anti-reversion agent; wherein the asphalt is heavy traffic road petroleum asphalt, injected into The degree is 50-110. The rubber powder is ground rubber powder from waste tires prepared by the normal temperature method. The weight ratio of asphalt to rubber powder is 70-85:15-25. The rubber powder contains cross-linking agent, accounting for the weight of the rubber powder. The technical indicators of the rubber powder are: moisture less than 5%, metal content less than 0.4%, ash content less than 8%, and size 20-80 mesh. The activator is alkylphenol polysulfide, accounting for 0.1-1% of the weight of the rubber powder, and the anti-reversion agent is bismaleimide or silane tetrasulfide compound, accounting for 0.1-0.5% of the weight of the rubber powder. It has the characteristics of anti-softening point decay during high-temperature storage, and is widely used in asphalt mixtures. It has the characteristics of continuous, stable and environmentally friendly production in factories and low oil consumption.

Description

technical field [0001] The invention relates to a road construction material, and in particular provides a storage-resistant rubber powder modified asphalt and a preparation method thereof. Background technique [0002] As a continuous pavement, asphalt pavement has the characteristics of comfortable driving and easy maintenance, and has become the main form of pavement. However, asphalt pavement has insufficient high temperature stability, low temperature crack resistance, and water damage resistance, which easily cause rutting, cracks, and potholes. In order to reduce the premature appearance of diseases, modified asphalt materials are mostly used now. At present, SBS modified asphalt is widely used as the modified asphalt material, but this kind of asphalt modifier has the problem of high price, and the modification process is relatively complicated. The addition of waste rubber powder can make the asphalt achieve the effect of modification, and its performance index ca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L95/00C08L21/00C08K5/14C08K5/372C08K5/3415C08K5/548
Inventor 卢长虹郭志刚徐桂荣王仕峰周乃承李荫国张海峰佟军华郭巍巍
Owner SHENYANG SANXIN GROUP PANJIN ROAD MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap