A kind of low hardness polyurethane elastomer composition

A polyurethane elastomer, low hardness technology, applied in the field of polyurethane elastomers, can solve the problems of limitation, low production efficiency, long curing time, etc., and achieve the effects of high production efficiency, comfortable hardness and hand feeling, and easy industrial production.

Active Publication Date: 2011-12-14
SHANDONG INOV POLYURETHANE
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Polyurethane is a polymer synthetic material with properties between rubber and plastic. It is characterized by a wide range of hardness adjustment. It has both the elasticity of rubber and the hardness of plastic. The usual low-hardness polyurethane elastomers are added by adding a lot of Plasticizers are obtained, so that after a period of time, the plasticizers will migrate and precipitate to the surface, which limits its use in the production of products that come into contact with the human body
Moreover, the curing time of low-hardness polyurethane elastomer products is long, and the production efficiency is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Polymer components: 20% polyether polyol with functionality 2 and molecular weight 1000, 78% polyether polyol (PPG330N) with functionality 3 and molecular weight 3000, organic bismuth catalyst 1%, UV-329 0.5%, 1010 0.5 % prepared according to the method of the present invention.

[0026] Prepolymer: 45% of polyether polyol with 2 functionalities and molecular weight of 1000, 55% of liquefied MDI, reacted at 70°C to 90°C for 2 to 3 small vacuums (-0.095MPa) to remove bubbles, and obtain isocyanate content 10% prepolymer.

[0027] The prepolymer and the polymer component are mixed at a ratio of 100:20, the mixing temperature is 25°C-40°C, the vulcanization temperature of the product is 60°C-70°C, and the vulcanization is 8 minutes to obtain a Shore 5A polyurethane elastomer product.

Embodiment 2

[0029] Polymer components: 5% polyether polyol with functionality 3 and molecular weight 300, 93% polyether polyol (PPG330N) with functionality 3 and molecular weight 5000, bismuth catalyst 0.5%, zinc catalyst 0.5%, UV-3280.5% , 1010 0.5% prepared according to the method of the present invention.

[0030] Prepolymer: 65% of polyether polyol with 2 functionalities and molecular weight of 3000, MDI30%, liquefied MDI5%, reacted at 70℃~90℃ for 2~3 small vacuums (-0.095MPa) to remove bubbles and obtain iso Prepolymer with 7% cyanate content.

[0031] The prepolymer and the polymer component are mixed at a ratio of 100:35, the mixing temperature is 25°C-40°C, the product vulcanization temperature is 60°C-70°C, and vulcanized for 5 minutes to obtain a Shore 20A polyurethane elastomer product.

Embodiment 3

[0033] Polymer component: 10% of polyether polyol with functionality 2 and molecular weight 2000, 88.5% of polyether polyol with functionality 3 and molecular weight 6000, bismuth catalyst 0.5%, UV-531 0.5%, BHT 0.5% according to the present invention Prepared by the method described.

[0034] Prepolymer: 62% of polyether polyol with 2 functionalities and molecular weight of 2000, MDI30%, and liquefied MDI8% are reacted at 70°C to 90°C for 2 to 3 small vacuums (-0.095MPa) to remove air bubbles and obtain isocyanide Prepolymer with 10% acid group content.

[0035] The prepolymer and the polymer component are mixed at a ratio of 100:20, the mixing temperature is 25°C-40°C, the vulcanization temperature of the product is 60°C-70°C, and the vulcanization is 8 minutes to obtain a polyurethane elastomer product of Shore 0A.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of unsaturationaaaaaaaaaa
Login to View More

Abstract

The low-hardness polyurethane elastomer composition adopts a two-component system, consisting of a prepolymer and a polymer component. The prepolymer is made of diphenylmethane diisocyanate and polypropylene oxide ether polyol at 70 ℃~90℃ to react to obtain a prepolymer with an isocyanate content of 7~14%. The polymer component is prepared from polypropylene oxide ether polyol, catalyst and antiaging agent. The polymer component and the prepolymer component are mixed according to the ratio of 100-20 to 100-35 to obtain a product with a Shore 0 to 20A. Human wheelchair cushions and other health protection products. The obtained product is environment-friendly and safe, has good processing performance, and has a comfortable handle.

Description

technical field [0001] The invention belongs to the field of polyurethane elastomers, in particular to a low-hardness polyurethane elastomer composition. Background technique [0002] Polyurethane is a polymer synthetic material with properties between rubber and plastic. It is characterized by a wide range of hardness adjustment. It has both the elasticity of rubber and the hardness of plastic. The usual low-hardness polyurethane elastomers are added by adding a lot of Plasticizers are obtained, so that after a period of time, the plasticizers will migrate and precipitate to the surface, which limits its use in the production of products that come into contact with the human body. Moreover, the curing time of low-hardness polyurethane elastomer products is long, and the production efficiency is low. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a low-hardness polyurethane elastomer composition. The obtained p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L75/08C08G18/76C08G18/48C08G18/10
Inventor 陈海良李健曹士强
Owner SHANDONG INOV POLYURETHANE