Method for producing environment-friendly fabric with carbon effect

A production method and carbon technology, applied in temperature recording method, fabric surface trimming, textiles and papermaking, etc., can solve the problems of inconsistent grain thickness, dull color, poor adsorption capacity of non-leather fabrics, etc., to overcome the inconsistent thickness, color and luster Soft, slippery effect

Inactive Publication Date: 2012-06-13
吴新民
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing fabrics are too traditional, with dull color, poor sensory impact, poor functionality and environmental protection. In the PU industry, the effect of imitation leather is not strong
The existing leather fabrics are time-consuming and labor-intensive due to the inconsistent thickness of the texture when making garments, and the adsorption capacity is poor, and non-leather fabrics are too traditional

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] 1. Base cloth coating (coating) treatment: apply 0.3 mm thick wet-process PU resin on the 0.55 mm left inclined base cloth, and dry it into a base material;

[0018] 2. Transfer veneer: select the Aw-67 release pattern produced by a British company, and transfer dry PU resin on the base material;

[0019] 3. Carbon treatment: Mix and stir 30% polishing material and 70% carbon pigment, dry at 130°C with 100 mesh * 110 mesh wheel (45g / Y), and wait for embossing;

[0020] 4. Embossing: pressing the leather pattern on the treated carbon leather to form a semi-finished product;

[0021] 5. Washing: At 55°C, wash with 5% enzyme solution (biocatalyst) for 15mm, and then wash with 6% softener (4-grade amine salt) and 7% smoothing agent (organic silicon emulsion) for 10 minutes , dried at 100°C.

[0022] PU is the abbreviation of English ploy urethane, the chemical Chinese name is polyurethane, and PU leather is the skin of polyurethane. Now clothing manufacturers widely use t...

Embodiment 2

[0024] 1. Coating treatment of the base fabric: On the 0.4mm tiger fur base fabric, coat (coat) 0.3mm thick wet-process PU, and dry it into a base material.

[0025] 2. Transfer veneer: Select the B-251 pattern produced in Italy, and transfer the velvet PU on the base material.

[0026] 3. Carbon treatment: Mix and stir 20% polishing material and 80% carbon pigment, dry at 130°C with 100 mesh*200 mesh wheel (40g / Y), and wait for production.

[0027] 4. Embossing: Therefore, the pattern has the style of lambskin, and this process can be omitted.

[0028] 5. Washing: At 55°C, wash with 5% enzyme solution (biocatalyst) for 15mm, and then wash with 6% softener (4-grade amine salt) and 7% smoothing agent (organic silicon emulsion) for 10 minutes , drying at 100°C, the above enzyme solution includes a cellulase.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for producing an environment-friendly fabric with carbon effect, comprising the following steps: coating wet-type PU resin at the bottom of the fabric and drying the fabric, sizing the fabric to form a base material; transferring different textures on the base material to form different imitation-leather texture effects; preparing different carbon mixtures for embossing according to the differences of the textures in the last step; choosing different textures and pressing different textures on the leather materials of the processed carbon mixtures; carrying out enzyme wash for 10-20min at 50 DEG C on the pressed PU leather and then carrying out softening treatment on the PU leather for 15min before drying the PU leather to obtain the finished product. The fabric prepared by the method of the invention features environmental protection and adsorption function, can deodorize and resist toxin and achieve real leather effect in terms of leather imitation.

Description

technical field [0001] The invention discloses a method for making an environmentally friendly fabric with carbon effect, which belongs to the technical field of fabric production with imitation leather effect. Specifically, after introducing carbon components, it can achieve the luster of genuine leather, and is suitable for clothing, shoe materials, bags, etc. field. Background technique [0002] The existing fabrics are too traditional, with dull color, poor sensory impact, poor functionality and environmental protection. In the PU industry, the effect of imitation leather is not strong. The existing genuine leather fabrics are time-consuming and labor-intensive due to the inconsistent thickness of the textures when the typesetting of garments is made, and the adsorption capacity is poor, and the non-leather fabrics are too traditional. Contents of the invention [0003] Aiming at the deficiencies of the existing imitation leather technology for fabrics, the invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06N3/12D06C23/04B41M5/36
Inventor 吴新民
Owner 吴新民