High-gloss cathodic electrophoretic paint and preparation method thereof

A cathodic electrophoretic coating, high-gloss technology, applied in the field of coatings, can solve the problems of poor wettability of pigments, poor decoration, low gloss of the coating film, etc., achieve good decoration, reduce coating costs, and high gloss of the coating film

Active Publication Date: 2010-10-06
湖南伟邦汽车涂料有限公司
View PDF0 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] But the cathodic electrophoretic paint of above-mentioned prior art has the following deficiencies: due to the relatively poor wettability to pigment, common cathodic electrophoretic coating film gloss is low, and decoration is poor, only uses as primer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1, the preparation of amine modified epoxy resin, the unit of consumption is (g):

[0023] raw material

[0024] Prepared using mature existing technology.

Embodiment 2

[0025] Embodiment 2, the preparation of isocyanate blocking material, the unit of consumption is (g):

[0026] raw material

[0027] Prepared using mature existing technology.

Embodiment 3

[0028] Embodiment 3, the preparation of quaternary ammonium salt dispersion resin, the unit of consumption is (g):

[0029] raw material

[0030] Prepared using mature existing technology.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to high-gloss cathodic electrophoretic paint and a preparation method thereof. The paint comprises emulsion and a color paste; the mass percent of the emulsion is 36 to 40 percent; and the mass percent of the color paste is 5 to 6 percent. The formula of the emulsion takes the mass percent as the unit and comprises 20 to 60 percent of amine modified epoxy resin, 5 to 20 percent of isocyanate sealing element, 30 to 60 percent of deionized water, 0.3 to 0.6 percent of emulsifying agent and 0.3 to 0.6 percent of formic acid. The color paste comprises 10 to 40 percent of quaternary ammonium salt dispersion resin, 35 to 45 percent of deionized water, 5 to 8 percent of dibutyl tin oxide, 10 to 20 percent of kaolin, 5 to 15 percent of carbon black and 2 to 5 percent of emulsifying agent. The method comprises the following step of: after mixing the color paste, the emulsion and the deionized water according to the proportion of 1:7:11, carrying out electrophoresis coating for 3 to 4min at the construction voltage of 200V after curing for 48 to 50h at the temperature of 28 to 30 DEG C. The invention has scientific and reasonable mixture ratio, high gloss of a coated film, good decoration property, high safety and environmental protection.

Description

technical field [0001] The invention relates to a coating, in particular to a high-gloss cathodic electrophoretic paint capable of forming a high-gloss coating film on the surface of a metal substrate and a preparation method thereof. Background technique [0002] Cathodic electrophoretic coatings are widely used, and their proportions mainly use epoxy resin as the main film-forming material, which has good anti-corrosion ability. [0003] However, the above-mentioned prior art cathodic electrophoretic coatings have the following disadvantages: due to poor wettability to pigments, common cathodic electrophoretic coatings have low gloss and poor decorative properties, and are only used as primers. SUMMARY OF THE INVENTION [0004] The purpose of the present invention is to overcome the deficiencies in the prior art, and to provide a high-gloss cathodic electrophoretic paint with strong corrosion resistance, high gloss of the coating film and good decorative properties, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D7/12C09D5/44
Inventor 严刚王永裴俊胡峰
Owner 湖南伟邦汽车涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products