Parallel composite elastic fiber and manufacture method thereof

An elastic fiber, manufacturing method technology, applied in fiber processing, conjugated synthetic polymer rayon, filament/thread forming, etc., can solve the problems of high intrinsic viscosity, poor intrinsic viscosity, and low potential shrinkage of PET. , to achieve the effect of improving elastic recovery rate, cost reduction and good elasticity

Active Publication Date: 2010-10-06
TORAY IND INC
View PDF1 Cites 49 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The elastic fibers obtained by stretching and cutting through the combination of these two intrinsic viscosities of PBT and PET, but due to the small intrinsic viscosity difference a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Parallel composite elastic fiber and manufacture method thereof
  • Parallel composite elastic fiber and manufacture method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The two-component elastic fiber is prepared by the melting method, and polybutylene terephthalate with an intrinsic viscosity of 1.31dl / g and polyethylene terephthalate with an intrinsic viscosity of 0.51dl / g are selected for composite spinning. Their intrinsic viscosity difference is 0.80dl / g. Dry them separately so that the water content is less than 100ppm, and then put the dried polybutylene terephthalate and polyethylene terephthalate into No. 1 / No. 2 spinning boxes at a weight ratio of 50:50. Set the spinning temperature, the screw temperature of the No. 1 extruder is 265°C; the screw temperature of the No. 2 spinning machine is 285°C; the temperature of the spinning box is 270°C. Use side-by-side spinnerets to spin out, set the winding speed to 2500m / min, and control the raw silk variety to 300dtex / 48F.

[0022] False-twisting processing is carried out on the wound pre-oriented yarn. The temperature of the hot needle after feeding the roller on the false twister...

Embodiment 2

[0025] Adopt the polymer weight ratio identical with embodiment 1, spinning temperature, spinning speed, precursor kind, processing method, processing temperature, processing ratio, processing speed, but change the intrinsic viscosity difference of two kinds of polymers, select intrinsic viscosity Polybutylene terephthalate with an intrinsic viscosity of 1.50dl / g and polyethylene terephthalate with an intrinsic viscosity of 0.45dl / g were used for composite spinning, and their intrinsic viscosity difference was 1.05dl / g. See Table 1 for specific values.

Embodiment 3

[0027] Adopt the polymer weight ratio identical with embodiment 1, spinning temperature, spinning speed, raw silk kind, processing method, processing temperature, processing magnification, processing speed, but change the intrinsic viscosity difference of two kinds of polymers, select intrinsic viscosity Polybutylene terephthalate with an intrinsic viscosity of 1.00dl / g and polyethylene terephthalate with an intrinsic viscosity of 0.60dl / g are used for composite spinning, and their intrinsic viscosity difference is 0.40dl / g. See Table 1 for specific values.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Intrinsic viscosityaaaaaaaaaa
Intrinsic viscosityaaaaaaaaaa
Monofilament denieraaaaaaaaaa
Login to view more

Abstract

The invention discloses parallel composite elastic fiber and a manufacture method thereof. The parallel composite elastic fiber is obtained through false twisting process after parallel composite spinning of valox and polyethylene glycol terephthalate according to a weight ratio of 70/30 to 30/70, wherein the inherent viscosity of the valox is between 0.45 to 0.60 dl/g, and the difference of the inherent viscosity of the valox and the inherent viscosity of the polyethylene glycol terephthalate is between 0.40 and 1.05 dl/g. The elastic extensibility of the elastic fiber of the invention is between 130 and 220 percent, and the elastic recovery rate is higher than 85 percent.

Description

technical field [0001] The invention relates to a side-by-side composite elastic fiber, in particular to a two-component elastic fiber containing polybutylene terephthalate. Background technique [0002] Composite fiber is a new type of chemical fiber developed in the 1960s in the world, and the two-component composite fiber is also called two-component fiber or conjugate fiber. It is to transport two kinds of fiber-forming high polymer melts with different components, proportions, viscosities, etc. to the same spinning assembly, meet at the appropriate part of the assembly, and spray out from the same spinneret hole to form a fiber. [0003] Side-by-side composite fiber is the earliest developed composite fiber variety with large output and relatively important. When people first researched and developed composite fiber, they mainly wanted to simulate the crimp elasticity of natural wool with chemical fiber. As people continue to deepen the microstructure, it is found that...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01F8/14D01D5/32D02G1/02
Inventor 张雷曹海兵藤森稔
Owner TORAY IND INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap