Utilization method for polymeric aluminium reaction residues

A polyaluminum chloride and reaction technology are applied in the field of treatment and utilization of polyaluminum chloride reaction residues to achieve the effects of reducing the content of water-insoluble matter, reducing usage, and facilitating transportation and utilization

Active Publication Date: 2010-12-08
CHANGZHOU WUJIN YOUBANG WATER PURIFICATION MATERIALS
View PDF5 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is: to overcome the defects of the reaction residue treatment method produced in the production of polyaluminum chloride at present, and to provide a technology for resourceful and clean utilization of reaction residue

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Utilization method for polymeric aluminium reaction residues

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] The total acidity of the inorganic mixed acid in this example is 6% (in HCl mass fraction), which is formed by mixing 6% hydrochloric acid, 8% sulfuric acid and 5.4% phosphoric acid, and the mass ratio of the three is 80:1:1.

[0014] Add 3600kg of 5% mixed mineral acid in a 5000L reactor, add 600kg of polyaluminum chloride reaction residue successively under continuous stirring, heat and stir at about 50°C for 0.5 hours, then pour the reaction solution into a sedimentation tank for precipitation for 1 hour to obtain The supernatant liquid is the alumina-containing acid liquid, and the specific properties and characteristics of the sludge and the reaction liquid are shown in Table 1.

Embodiment 2

[0016] The total acidity of the inorganic mixed acid of this example is 8% (in terms of HCl mass fraction), which is formed by mixing 8% hydrochloric acid and 10.7% sulfuric acid, and the mass ratio of the two is 30:1.

[0017] Add 3600kg of 8% mixed mineral acid in a 5000L reactor, add 720kg of polyaluminum chloride reaction residue successively under constant stirring, heat and stir at about 70°C for 1 hour, then pour the reaction solution into the sedimentation tank for 0.5 hour precipitation, and obtain The supernatant liquid is the alumina-containing acid liquid, and the specific properties and characteristics of the sludge and the reaction liquid are shown in Table 1.

Embodiment 3

[0019] The total acidity of the inorganic mixed acid of this example is 12% (in HCl mass fraction), which is formed by mixing 12% hydrochloric acid, 16.1% sulfuric acid and 10.7% phosphoric acid, and the mass ratio of the two is 80:1:3.

[0020] Add 3600kg of 12% mixed mineral acid in a 5000L reactor, add 900kg of polyaluminum chloride reaction residue successively under constant stirring, heat and stir at about 90°C for 1.5 hours, then pour the reaction solution into a sedimentation tank for precipitation for 2 hours to obtain The supernatant liquid is the alumina-containing acid liquid, and the specific properties and characteristics of the sludge and the reaction liquid are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a technology for treating chemical wastes, in particular to a treatment and utilization method for polymeric aluminium reaction residues. The method comprises the following specific steps: (1) putting 4%-20% (by weight parts of HCl) of inorganic mixed acid and reaction residues in the weight ratio of 1:6-1:2 into reaction equipment, evenly mixing, and reacting while stirring at the temperature of 50-110 DEG C for 0.5-2h; and (2) throwing reaction liquid into a sedimentation tank for sedimentation for 0.5-2h or directly utilizing a filter-press to carry out solid-liquid separation, wherein the obtained clear liquid is aluminiferous acid liquor capable of being reused in the polymeric aluminium production process. The invention comprehensively utilizes the solid reaction residues, turns waste materials into things of value, reduces the yield of the solid residues in the polymeric aluminium production process, saves the handling expenses for the residues, reduces the usage amount of calcium aluminate powder and bauxite in the polymeric aluminium production process, saves production cost and improves product quality.

Description

technical field [0001] The invention relates to a treatment technology of chemical waste, in particular to a treatment and utilization method of polyaluminum chloride reaction residue. Background technique [0002] At present, my country's polyaluminum chloride manufacturers mostly use the one-step method of acid-dissolving calcium aluminate or the two-step method of acid-dissolving calcium aluminate and bauxite to produce polyaluminium chloride. Due to the composition characteristics of calcium aluminate powder and bauxite Different from the process conditions, the final reaction liquid will contain a certain amount of water-insoluble residues, which need to be settled naturally, or added with a settling agent to accelerate the settling, or removed by filter press equipment. The conventional treatment plan for the final residue is: as a solid After paying a certain treatment fee, the waste will be handed over to the relevant environmental protection unit for disposal. For a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01F7/56B09B3/00
Inventor 赵志萍王桂玉王振宇
Owner CHANGZHOU WUJIN YOUBANG WATER PURIFICATION MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap