Regenerated wire drawing modified material of waste polypropylene woven bags and preparation method thereof

A technology for waste polypropylene and modified materials is applied in the field of waste polypropylene woven bag regeneration wire drawing modified material and its preparation, to achieve the effects of reducing product production cost, stable performance and reducing performance probability

Inactive Publication Date: 2010-12-15
丁飞鹏 +1
View PDF2 Cites 45 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a kind of regenerated drawing modified material of waste polypropylene woven bag and its preparation method, through recycling and processing of waste polypropylene woven bag, adding appropriate amount of other raw materials and auxiliary materials to generate new drawing modified woven bag Non-toxic materials, which solve the problems existing in the existing recycling technology of waste polypropylene woven bags

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0037] Step 1, take the waste polypropylene woven bag material accounting for 50% of the total weight, wash, chop, dry and set aside;

[0038] Step 2, 20% of the toughening modifier 1000 mesh mica powder, 5% of the toughening modifier ethylene-vinyl acetate copolymer (EVA), 0.6% of the activator titanate coupling agent, 0.4% lubricant dispersant polypropylene wax is put into a high-speed mixer heated to 180°C for stirring and kneading activation treatment and then used;

[0039] Step 3, put the ready-to-use material processed in step 1 and step 2 into a mixer and stir evenly with 4% of the total weight of the phosphite lipid antioxidant and 20% of the new polyolefin material;

[0040] Step 4. Stir and mix the materials evenly and put them into a screw drawing machine for heating. When the temperature is heated to 220°C, wire drawing is carried out to produce finished woven bag materials.

example 2

[0042] Step 1, take the waste polypropylene woven bag material accounting for 57% of the total weight, wash, chop, dry and set aside;

[0043] Step 2, take 5% of the total weight of propylene-based elastomer (VISTAMAXX) and 1% of maleic anhydride grafted polypropylene two toughening modifiers, 0.5% of activator titanate coupling agent, 0.5% The lubricant dispersant polypropylene wax is put into a high-speed mixer heated to 180°C for stirring and kneading activation treatment before use;

[0044] Step 3, the ready-to-use material processed in step 1 and step 2 and the toughening modifier 1500 mesh mica powder accounting for 15% of the total weight, 1% phosphite lipid antioxidant and 20% polyolefin new material Throw in a blender and mix well;

[0045] Step 4: Stir and mix the material evenly and put it into a screw drawing machine for heating, and draw it when the temperature is heated to 200°C, that is, the finished woven bag material is produced.

[0046] The performance of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a regenerated wire drawing modified material of waste polypropylene woven bags, comprising the following components in percentage by weight: 1-35 percent of polyolefin fresh material, 25-95 percent of waste polypropylene material, 1-55 percent of enhanced modifier, 1-30 percent of toughening modifier, 0.01-5 percent of activator, 0.1-3 percent of antioxidant, 0.01-6 percent of lubricant and 0.01-6 percent of dispersing agent. The invention also provides a preparation method of the regenerated wire drawing modified material of the waste polypropylene woven bags. In the preparation method, based on the arecovery treatment on the waste polypropylene woven bags, the new wire drawing modified material of woven bags are produced by adding proper amount of other raw materials and auxiliary materials and can be directly used for producing polyolefine flat fibers with stable performance. The performance of a new polypropylene woven tape produced from the prepared material and a small quantity of fresh material is equivalent to a woven bag wholly produced by carrying out granulation and wire drawing on the fresh material. The new polypropylene woven tape can completely satisfy the use performance requirements, dramatically lower the product production cost and provide a proper way for waste recycling utilization and environmental pollution reduction.

Description

technical field [0001] The invention belongs to the technical field of chemical engineering and environmental protection, and relates to a polyolefin woven material enhancement modification technology, in particular to a regenerated drawing modification material for waste polypropylene woven bags and a preparation method thereof. Background technique [0002] my country's annual waste of nearly 3 million tons of woven bags is called white pollution, just like the agricultural film that is difficult to degrade naturally. At present, waste woven bag recycled wire drawing factories basically only use simple cleaning, then chop up, and melt, extrude and granulate through a spiral heating extruder with water in the recycling process of waste woven bags, without any process. modification treatment. Firstly, this method consumes part of the original additives in the waste polypropylene woven bag, and the heating method with water will further age and carbonize the plastic. In addi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/12C08L23/00C08L23/08C08L51/06C08K13/04C08K3/34
Inventor 丁飞鹏何芳炆
Owner 丁飞鹏
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com