Manufacture method of ceramic wine bottle with liquid gold

A manufacturing method and technology for ceramic wine bottles, which are applied in the field of manufacturing gold-painted ceramic wine bottles, can solve the problems of easy foaming of metal patterns, waste of raw materials, graying of metal patterns, etc., achieve rich color levels, improve manufacturing methods, and reduce burning. The effect of loss

Inactive Publication Date: 2010-12-22
SHANGHAI GAOCHENG CREATIVE TECH GRP
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If the firing is excessive, it is easy to cause blistering, discoloration, and cracking of the metal pattern; if the firing is insufficient, the raised height of the metal pattern is not enough, the three-dimensional effect is poor, the gloss of the metal pattern is poor, and the metal pattern is gray
Secondly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacture method of ceramic wine bottle with liquid gold
  • Manufacture method of ceramic wine bottle with liquid gold

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0035] The present invention will be further described below in conjunction with the accompanying drawings and embodiments.

[0036] figure 1 It is a process flow chart of the manufacturing method of the gold-painted ceramic wine bottle of the present invention.

[0037] See figure 1 , the manufacture method of the gold-painted ceramic wine bottle provided by the invention comprises the following steps successively:

[0038] Step S1: Provide ceramic carcass, use 800-1200 mesh sandpaper for grinding, and enter step S2;

[0039] Step S2: Carry out the first firing of the above-mentioned carcass at 800-1000° C. to remove moisture and organic impurities in the carcass, increase the surface strength of the carcass, and proceed to step S3;

[0040] Step S3: glaze the surface of the carcass, and perform a second firing at 1180-1320° C., and proceed to step S4;

[0041]Step S4: Provide ceramic decals with concave-convex patterns, paste them on the surface of the carcass, and perfo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a manufacture method of a ceramic wine bottle with liquid gold, which sequentially comprises the following steps of: offering and polishing a ceramic blank body; firstly burning the blank body at the temperature of 800-1000 DEG C to remove the water gas and the organic matter impurity in the blank body; glazing the surface of the blank body; secondarily burning at the temperature of 1180-1320 DEG C; offering a ceramic stained paper with concave-convex patterns, adhering the ceramic stained paper on the surface of the blank body, thirdly burning at the temperature of 760-1150 DEG C, and removing an adhesive film in a baking way to lead the ceramic stained paper to be completely adhered to the surface of the blank body to form into the concave-convex pattern; and spraying the liquid gold on the surface of the blank body, fourthly burning at the temperature of 600-700 DEG C to manufacture the pattern with the liquid gold. By repeatedly burning and controlling the burning temperature, the manufacture method of the ceramic wine bottle with the liquid gold can form into colorful, hierarchical and abundant liquid gold patterns at the outer surface of the whole ceramic wine bottle, and avoiding foaming, discoloring and cracking.

Description

technical field [0001] The invention relates to a method for manufacturing a ceramic wine bottle, in particular to a method for manufacturing a gold-painted ceramic wine bottle. Background technique [0002] Alumina ceramics are a kind of α-Al 2 o 3 The alumina content of the main crystal phase ceramic material is generally between 75% and 99%. The alumina ceramics have different manufacturing methods according to different types, different performance requirements, and different shapes, sizes and thicknesses of the products. But generally through the following process: [0003] 1. Pre-firing of alumina [0004] Since the raw material of industrial alumina is usually γ-Al 2 o 3 Therefore, before making alumina ceramics with alumina powder, the alumina powder must be pre-fired, or calcined. [0005] (1) Purpose of burn-in [0006] Pre-burning can make γ-Al 2 o 3 All become α-Al 2 o 3 Reduce firing shrinkage. Because of γ-Al 2 o 3 to α-Al 2 o 3 Transformation...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B41/89
Inventor 蔡世山
Owner SHANGHAI GAOCHENG CREATIVE TECH GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap