A technology of radioactive waste and radioactive waste resin, applied in the direction of radioactive purification, solid waste management, sustainable waste treatment, etc., can solve the problems of low strength of solidified body, cracking of solidified body, low containment capacity, etc.

Inactive Publication Date: 2011-01-05
TSINGHUA UNIV
View PDF5 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The cured body has defects such as low strength of the cured body and low resin inclusion capacity
[0004] Evaporation is the main method for the treatment of radioactive wastewater in nuclear power plants. After evaporation, the non-volatile radionuclides and salts in the wastewater are concentrated into the concentrated solution. This part of the concentrated solution has high radioactivi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Mix each component according to the following dosage, 90kg sulfoaluminate cement + 1kg sodium silicate (Na 2 SiO 3 9H 2 (2)+45L concentrated solution, the initial setting time of the solidified body is 5 hours, the volume of the solidified body obtained is 90L, and the inclusion capacity of the concentrated solution in the solidified body is 50%.

Embodiment 2

[0017] Mix each component according to the following dosage, 90kg sulphoaluminate cement + 5kg sodium silicate (Na 2 SiO 3 9H 2 (2)+45L concentrated solution, the initial setting time of the solidified body is 3 hours, the volume of the solidified body obtained is 90L, and the inclusion capacity of the concentrated solution in the solidified body is 50%.

Embodiment 3

[0019] Mix each component according to the following dosage, 90kg sulfoaluminate cement + 10kg sodium silicate (Na 2 SiO 3 9H 2 (2)+45L concentrated solution, the initial setting time of the solidified body is 1 hour, the volume of the solidified body obtained is 90L, and the inclusion capacity of the concentrated solution in the solidified body is 50%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a curing agent for curing radioactive wastes containing borate, belonging to the technical field of a waste treatment. The curing agent is the mixture of cement and sodium silicate, wherein the weight ratio of the cement to the sodium silicate is 100 to (1-15). The invention also discloses a method for curing the radioactive wastes containing the borate by utilizing the curing agent. The mixture of the cement and the sodium silicate in the invention can be used for curing the radioactive wastes generated in a nuclear power station, avoiding the phenomenon of non-condensing cement slurry because of the delayed coagulation of the borate adsorbed in the wastes on the cement and cracking of cement curing bodies after being soaked in water, enhancing the capacity, shortening the initial coagulation time of the cement slurry, and ensuring that no crack is generated on the surfaces of the curing bodies and various performance indexes can meet the requirements of the national standard GB14569.1-93.

Description

technical field [0001] The invention belongs to the technical field of waste treatment, and in particular relates to a curing agent for curing borate-containing radioactive waste and a method thereof. Background technique [0002] Radioactive waste is mainly produced in the nuclear industry, including radioactive waste resin and radioactive concentrate. [0003] Radioactive waste resin is one of the main low and medium radioactive wastes produced during the operation of nuclear power plants and nuclear facilities. During the operation of pressurized water reactor nuclear power plants, boric acid needs to be added to the primary circuit to control the reaction rate. Therefore, it is used to treat primary circuit water A large amount of boric acid will be adsorbed on the resin. Boric acid is a kind of retarder for cement. The existence of a large amount of boric acid will cause the setting time of cement to be too long, and the too long setting time will lead to the delaminati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/26C04B28/36G21F9/16G21F9/28
CPCC04B2111/00862C04B28/26C04B2111/00767C04B40/0039Y02W30/91
Inventor 李俊峰王建龙孙奇娜
Owner TSINGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap