Oxo-biodegradable BOPP (biaxially-oriented polypropylene) film and preparation method thereof

A technology of polypropylene film and biaxial stretching, which is applied in the direction of chemical instruments and methods, synthetic resin layered products, layered products, etc., can solve the problems of product function and appearance, product refractory decomposition, etc. Effect

Active Publication Date: 2011-04-20
ZHEJIANG KINLEAD PACKAGING MATERIAL
View PDF1 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Biodegradation is achieved by adding modified starch, but it has a certain impact on product function and appearance, and some products are difficult to decompose eventually

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The oxidative biodegradable biaxially stretched polypropylene optical film of the present invention is prepared by selecting components of homopolypropylene 96.5% by weight, antisticking agent 2.5% AB6018PP, and oxygen-containing biodegradant 1.0% for the upper surface layer. And the melt index range of homopolypropylene is 2.6-3.2g / 10min. The core layer is made of components with weight percentages of 93% homopolypropylene, 3.0% antistatic agent, 3.0% slip agent, and 1.0% oxygen-containing biodegradation agent, and the melt index range of homopolypropylene is 2.6-3.2g / 10min. The antistatic agent is an alkylamine antistatic agent; the slip agent is an erucamide slip agent. The lower surface layer is made of components with 96.5% by weight of homopolypropylene, 2.5% of anti-sticking agent AB6018PP, and 1.0% of oxygen-containing biodegradation agent, and the melt index range of homopolypropylene is 2.6-3.2g / 10min. The thickness of the upper surface layer is controlled...

Embodiment 2

[0040]The oxidative biodegradable biaxially stretched polypropylene optical film of the present invention is prepared by selecting the upper surface layer of 97.5% by weight of homopolypropylene, 1.5% of anti-sticking agent AB6018PP, and 1.0% of oxygen-containing biodegradation agent. And the melt index range of homopolypropylene is 2.6-3.2g / 10min. The core layer is made of components with 97% by weight of homopolypropylene, 1.0% of antistatic agent, 1.0% of slip agent and 1.0% of oxygen-containing biodegradation agent, and the melt index range of homopolypropylene is 2.6-3.2g / 10min. The antistatic agent is an alkylamine antistatic agent; the slip agent is an erucamide slip agent. The lower surface layer is made of components with 97.5% by weight of homopolypropylene, 1.5% of anti-sticking agent AB6018PP, and 1.0% of oxygen-containing biodegradation agent, and the melt index range of homopolypropylene is 2.6-3.2g / 10min. The thickness of the upper surface layer is controlle...

Embodiment 3

[0050] The oxidative biodegradable biaxially stretched polypropylene double-sided heat-sealing film of the present invention is prepared by selecting the components by weight percentage of 97.5% of copolymerized polypropylene, 1.5% of anti-sticking agent AB6018CPP, and 1.0% of oxygen-containing biodegradation agent for the upper surface layer. become. The core layer is made of components with weight percentages of 95% homopolypropylene, 2.0% antistatic agent, 2.0% slip agent, and 1.0% oxygen-containing biodegradation agent, and the melt index range of homopolypropylene is 2.6-3.2g / 10min. The antistatic agent is an alkylamine antistatic agent; the slip agent is an erucamide slip agent. The lower surface layer is made of components with weight percentages of 97.5% of copolymerized polypropylene, 1.5% of anti-sticking agent AB6018CPP, and 1.0% of oxygen-containing biodegradation agent. The thickness of the upper surface layer is controlled to be 1.0μ, the thickness of the core ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Melt fingeraaaaaaaaaa
Melt fingeraaaaaaaaaa
Login to View More

Abstract

The invention discloses an oxo-biodegradable BOPP (biaxially-oriented polypropylene) film and a preparation method thereof, belonging to the technical field of the processing of BOPP films. The oxo-biodegradable BOPP film comprises an upper surface layer, a sandwich layer and a lower surface layer, and is prepared by the following steps of: adding 0.5-1.0 percent of an oxygen-containing biodegradable agent and other constituents into the upper surface layer, the sandwich layer and the lower surface layer, melting and extruding by utilizing a double-screw extruder at low temperature of 220-230DEG C, and then biaxially stretching on a Germany Bruckner machine. The structure of the traditional equipment is not changed in the invention, at the same time, the oxo-biodegradable BOPP film can solve the problem of white pollution, can not change the function and appearance of the traditional BOPP and produce harmful substances to the environment during decomposition process, and has the advantages of controlled degradation period, non-toxicity and the like.

Description

technical field [0001] The invention relates to an oxidative biodegradable biaxially stretched polypropylene film and a manufacturing method thereof, belonging to the technical field of biaxially stretched polypropylene film processing. Background technique [0002] There are generally four types of existing plastic waste disposal methods: traditional landfill, incineration, recycling, and composting. Studies have confirmed that it takes more than 400 years for plastics to slowly decompose, so traditional burial and composting cannot fundamentally solve environmental pollution. Incineration of waste plastics will produce a large amount of carbon dioxide and toxic gases, which will aggravate environmental pollution and the greenhouse effect. More importantly, the above processing methods are limited to the situation where waste plastics are collected. As an excellent packaging material, biaxially oriented polypropylene film (BOPP film) is widely used in the packaging of sta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B27/08B32B27/18B32B27/32
Inventor 陈利锋尹望林虞万金陈华任通余序安张爱民
Owner ZHEJIANG KINLEAD PACKAGING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com