An oil-resistant rubber, high-elasticity technology, applied in the field of rubber materials, can solve the problems of low elongation at break, low tear performance, low tear strength, etc., to improve thermal tear resistance and heat aging resistance, Excellent ozone resistance and the effect of improving elongation at break
Inactive Publication Date: 2011-06-15
JIANGSU YANGZHOU HELI RUBBER PROD
View PDF1 Cites 11 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] The structural feature of the air bag is a capsule with a small mouth and a large body. It is difficult to release this type of product. The rubber material of the general oil-resistant air bag is mainly nitrile rubber, but the elongation at break of ordinary nitrile rubber is not high. , The tearing strength is not high, and the tearing performance is not high, so that the "burst" phenomenon is prone to occur when the air bag product is released, resulting in waste products and increasing production costs
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0013] Take: 200 kilograms of (main ingredient) hydrogenated nitrile rubber,
[0014] (Stabilizer) 10 kg each of Martin Magnesium Hydroxide H5 and Martin Magnesium Hydroxide H10,
[0015] (Plasticizer) 7 kg of dioctyl phthalate, 8 kg of tri(n-octyl-n-decyl) trimellitate,
[0016] (Heat stabilizer) 12.5 kg of HT heat stabilizer,
[0017] (assisting crosslinking agent) 3 kilograms of triallyl isocyanurates,
[0018] (peroxide vulcanizing agent) 5 kilograms of dicumyl peroxide;
[0019] Mixing, masticating, and direct vulcanization to obtain a high-performance oil-resistant air bag.
Embodiment 2
[0021] Take: 200 kilograms of (main ingredient) hydrogenated nitrile rubber,
[0022] (Stabilizer) Martin Magnesium Hydroxide H5 Type 15kg,
[0023] (Plasticizer) 5 kg of dioctyl phthalate, 5 kg of tri(n-octyl-n-decyl) trimellitate,
[0024] (Heat stabilizer) 12.5 kg of HT heat stabilizer,
[0025] (assisting crosslinking agent) 5 kilograms of triallyl isocyanurates,
[0026] (peroxide vulcanizing agent) 6 kilograms of dicumyl peroxide,
[0027] (Vulcanizing agent) 2 kg of sulfur;
[0028] Mixing, masticating, and direct vulcanization to obtain a high-performance oil-resistant air bag.
Embodiment 3
[0030] Take: 200 kilograms of (main ingredient) hydrogenated nitrile rubber,
[0031] (Stabilizer) Martin Magnesium Hydroxide H5 Type 15kg,
[0032] (Plasticizer) 5 kg of dioctyl phthalate, 7 kg of tri(n-octyl-n-decyl) trimellitate,
[0033] (Heat stabilizer) 13 kg of HT heat stabilizer,
[0034] (assisting crosslinking agent) 6 kilograms of triallyl isocyanurates,
[0035] (peroxide vulcanizing agent) 8 kilograms of dicumyl peroxide,
[0036] (Vulcanizing agent) 2 kg of sulfur;
[0037] Mixing, masticating, and direct vulcanization to obtain a high-performance oil-resistant air bag.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to high strength and high elastic oil resistant rubber. The oil resistant rubber has high strength, good elasticity and wide temperature range while the strength and oil resistance can be ensured. The rubber comprises the following components in parts by weight: 100 parts of hydrogenated nitrile-butadiene rubber, 10-20 parts of heat stabilizer, 10-15 parts of plasticizer, 10-25 parts of reinforcing agent, 1-2 parts of vulcanizing agent, 1-5 parts of crosslinking aid and 2-5 parts of peroxide vulcanizing agent. The oil resistant rubber of the invention uses hydrogenated nitrile-butadiene rubber to replace common nitrile-butadiene rubber, uses nanometer reinforced material as auxiliary material and also adopts a special vulcanizing system. hydrogenated nitrile-butadiene rubber has good oil resistance; as the hydrogenated nitrile-butadiene rubber has a highly saturated structure, the hydrogenated nitrile-butadiene rubber has good heat resistance, good chemical resistance, excellent ozone resistance and higher compression set resistance; and the hydrogenated nitrile-butadiene rubber is also characterized by high tensile strength, high elongation at break, high tearing resistance, wear resistance and the like. The rubber of the invention can be used to produce the oil resistant air dome, solve the breakage phenomenon and save the production cost.
Description
technical field [0001] The invention relates to a rubber material with high strength, high elasticity, oil resistance and wide temperature adaptability range, in particular to a rubber formula for an oil-resistant air bag on an oil field mud pump. Background technique [0002] The structural feature of the air bag is a capsule with a small mouth and a large body. It is difficult to release this type of product. The rubber material of the general oil-resistant air bag is mainly nitrile rubber, but the elongation at break of ordinary nitrile rubber is not high. , The tearing strength is not high, and the tearing performance is not high, so that the "burst" phenomenon is prone to occur when the air bag product is released, resulting in waste products and increasing production costs. Contents of the invention [0003] Aiming at the above problems, the present invention provides a high-strength, high-elasticity oil-resistant rubber with high strength, good elasticity and wide t...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more