B-family crystal vitamin microcapsules and method for preparing microcapsules by utilizing solvent evaporation method

A vitamin and microcapsule technology, applied in the application, additional food elements, molding or processing of animal feed, etc., can solve the problems affecting the addition effect of B group crystalline vitamins, the properties and structure are easily destroyed, and the crystalline vitamins are easily destroyed, etc. problem, to achieve good slow release effect, low cost, and improve the effect of adding effect

Active Publication Date: 2011-08-17
广东省农业科学院畜牧研究所 +1
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, in the process of fish and shrimp farming, the main reasons why fish and shrimp cannot make full use of B group crystal vitamins are: ① fish and shrimp feed slowly, and B group crystal vitamins are easily soluble in water, and are easy to seep out from feed particles, affecting Addition effect of B group crystal vitamins
②The properties and structure of some B crystal vitamins are easily destroyed after contact with the external environment (such as VB 1 , VB 2 , VB 6 , folic acid)
During the storage of B group crystalline vitamins and aquatic feed, the properties and structure of B group crystalline vitamins are destroyed after contact with the external environment, which affects the addition effect of B group crystalline vitamins
③ Some B crystal vitamins are not resistant to high temperature (such as VB 3 , VB 7 , folic acid)
In the process of preparing aquatic feed, the temperature can reach 130°C, and crystal vitamins are easily destroyed at this temperature, which affects the effect of adding B group crystal vitamins

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • B-family crystal vitamin microcapsules and method for preparing microcapsules by utilizing solvent evaporation method
  • B-family crystal vitamin microcapsules and method for preparing microcapsules by utilizing solvent evaporation method
  • B-family crystal vitamin microcapsules and method for preparing microcapsules by utilizing solvent evaporation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The raw material formula of the B family crystalline vitamin microcapsules of the present embodiment is made up of following components by mass parts:

[0016] 1 part by mass of ethyl cellulose, 801.4 parts by mass of Span, crystalline vitamin B 1 5 parts by mass, 31.2 parts by mass of cyclohexane and 53.064 parts by mass of dichloromethane;

[0017] Measure cyclohexane with a beaker, then weigh Span 80 and dissolve it in cyclohexane to obtain solution B, place it in a water bath at 35°C, and stir with a stirrer. Take ethyl cellulose, dissolve it in dichloromethane, after the dissolution is complete, obtain solution A, add solution A to solution B, and then continue to add the ultrafine crystalline vitamin B 1 (Vitamin granules 85% pass 200 mesh), add in the above solution, adjust the rotating speed at 400r / min, stir evenly, until the solution becomes thick, stop stirring, pour the thick solution into a petri dish, dry, pulverize available products. After crushing, t...

Embodiment 2

[0019] The raw material formula of the B family crystalline vitamin microcapsules of the present embodiment is made up of following components by mass parts:

[0020] 1 part by mass of ethyl cellulose, 802.5 parts by mass of Siban, crystalline vitamin B 6 4 parts by mass, 31.2 parts by mass of cyclohexane and 53.064 parts by mass of dichloromethane;

[0021] Measure cyclohexane with a beaker, then weigh Span 80 and dissolve it in cyclohexane to obtain solution B, place it in a water bath at 35°C, and stir with a stirrer. Take ethyl cellulose, dissolve it in dichloromethane, after dissolving, obtain solution A, add solution A to solution B, and then continue to add crystal vitamin B 6 (Vitamin granules are 100-150 mesh), add to the above solution, adjust the rotation speed at 400r / min, stir evenly until the solution becomes thick, stop stirring, pour the thick liquid into a petri dish, dry it, and crush it. available products. After crushing, the product is screened through ...

Embodiment 3

[0023] The raw material formula of the B family crystalline vitamin microcapsules of the present embodiment is made up of following components by mass parts:

[0024] 1 part by mass of ethyl cellulose, 801 parts by mass of Span, crystalline vitamin B 1 3 parts by mass, 26 parts by mass of cyclohexane and 55.6 parts by mass of dichloromethane;

[0025] Measure cyclohexane with a beaker, then weigh Span 80 and dissolve it in cyclohexane to obtain solution B, place it in a water bath at 30°C, and stir with a stirrer. Take ethyl cellulose, dissolve it in dichloromethane, after the dissolution is complete, obtain solution A, add solution A to solution B, and then continue to add the ultrafine crystalline vitamin B 1 (Vitamin granules 85% pass 200 mesh), add in the above solution, adjust the rotating speed at 200r / min, stir evenly, until the solution becomes thick, stop stirring, pour the thick solution into a petri dish, dry and pulverize. available products. After crushing, the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses B-family crystal vitamin microcapsules and a method for preparing the microcapsules by utilizing the solvent evaporation method. In the preparation method, raw materials comprise the following components in parts by weight: 1-1.3 parts of ethyl cellulose, 1-4 parts of Span80, 3-9.4 parts of B-family crystal vitamin, 26-47.4 parts of cyclohexane and 32-55.6 parts of dichloromethane; and the preparation method comprises the following steps: dissolving the ethyl cellulose in the dichloromethane according to the formula to get solution A; further dissolving the Span80 in the cyclohexane to get solution B, sequentially adding the solution A and the B-family crystal vitamin into the solution B under the situation of keeping the temperature of the solution B at 30 DEG C-40 DEG C, uniformly stirring till becoming thick, air-drying the thick solution, then smashing and finally getting the B-family crystal vitamin microcapsules. The vitamin microcapsules have slow-release effect and good stability, and can greatly improve the adding effect of the B-family crystal vitamin and reduce the feed cost, the method is simple, low in cost and applicable to large-scale production, and products are used for feed for fishes and shrimps and can greatly improve the cultivation benefits.

Description

Technical field: [0001] The invention belongs to the field of animal feed, and in particular relates to a B group crystal vitamin microcapsule and a method for preparing the microcapsule by solvent evaporation. Background technique: [0002] At present, in the process of fish and shrimp farming, the main reasons why fish and shrimp cannot make full use of B group crystal vitamins are: ① fish and shrimp feed slowly, and B group crystal vitamins are easily soluble in water, and are easy to seep out from feed particles, affecting Addition effect of B group crystalline vitamins. ②The properties and structure of some B crystal vitamins are easily destroyed after contact with the external environment (such as VB 1 , VB 2 , VB 6 , folic acid). During the storage of B group crystalline vitamins and aquatic feed, the properties and structure of B group crystalline vitamins are destroyed after contact with the external environment, which affects the addition effect of B group crys...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A23K1/16A23K1/18A23K20/105A23K20/174A23K40/00A23K50/80
CPCY02A40/818
Inventor 曹俊明黄燕华蒋卫亮王国霞陈冰
Owner 广东省农业科学院畜牧研究所
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com