ASA (acrylonitrile-styrene-acrylate) resin with favorable appearance performance and preparation method thereof

A technology of ASA resin and appearance, applied in the field of ASA resin and its preparation, can solve the problems of uneven iridescence and gloss, easy occurrence of white spots, low tinting strength, etc., and achieve simple process flow, excellent appearance performance and high production efficiency. Effect

Active Publication Date: 2011-08-24
SHANGHAI KUMHO SUNNY PLASTICS
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to solve the above-mentioned deficiencies in the prior art, provide a kind of ASA resin with excellent appearance performance and its preparation method, on the basis of keeping the original

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • ASA (acrylonitrile-styrene-acrylate) resin with favorable appearance performance and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0041] Example 1

[0042] The scratch-resistant resin with excellent appearance properties is prepared according to the following components:

[0043] (1) Preparation of ASA cross-linked modified graft copolymer:

[0044] ASA rubber powder 50 copies

[0045] SAN resin 40 parts

[0046] 10 parts of third polymer

[0047] Initiator 0.8 parts

[0048] Antioxidant 0.3 parts

[0049] Lubricant 0.5 parts

[0050] Among them, ASA rubber powder is Korea Kumho;

[0051] The SAN resin is Zhenjiang Chimei SAN D168;

[0052] The third polymer is polycarbonate;

[0053] Initiator: BPO;

[0054] The lubricant is PETS;

[0055] Antioxidant is B900;

[0056] (1) After mixing ASA rubber powder, SAN resin, third polymer, initiator, antioxidant, and lubricant in a high-speed mixer, they are fed into a twin-screw extruder through a metering device to control the double-screw extruder. The temperature of the screw extruder is 180~220℃, the screw length-to-diameter ratio is 40, and the screw speed is 300rpm. Under th...

Example Embodiment

[0065] Example 2

[0066] The scratch-resistant resin with excellent appearance properties is prepared according to the following components:

[0067] (1) Preparation of ASA cross-linked modified graft copolymer:

[0068] ASA rubber powder 50 copies

[0069] SAN resin 30 parts

[0070] The third polymer 20 parts

[0071] Initiator 0.3 parts

[0072] Antioxidant 0.3 parts

[0073] Lubricant 0.5 parts

[0074] Among them, ASA rubber powder is Korea Kumho;

[0075] The SAN resin is Zhenjiang Chimei SAN D168;

[0076] The third polymer is ethylene-methacrylate copolymer;

[0077] Initiator: BPO;

[0078] The lubricant is PETS;

[0079] Antioxidant is B900;

[0080] (1) After mixing ASA rubber powder, SAN resin, third polymer, initiator, antioxidant, and lubricant in a high-speed mixer, they are fed into a twin-screw extruder through a metering device to control the double-screw extruder. The temperature of the screw extruder is 180~220℃, the screw length-to-diameter ratio is 40, and the screw speed ...

Example Embodiment

[0089] Example 3

[0090] The scratch-resistant resin with excellent appearance properties is prepared according to the following components:

[0091] (1) Preparation of ASA cross-linked modified graft copolymer:

[0092] ASA rubber powder 60 parts

[0093] SAN resin 30 parts

[0094] 10 parts of third polymer

[0095] Initiator 1.0 parts

[0096] Antioxidant 0.3 parts

[0097] Lubricant 0.5 parts

[0098] Among them, ASA rubber powder is Korea Kumho;

[0099] The SAN resin is Zhenjiang Chimei SAN D168;

[0100] The third polymer is polysiloxane;

[0101] Initiator: DCP;

[0102] Lubricant is EBS;

[0103] Antioxidant is B900;

[0104] (1) After mixing ASA rubber powder, SAN resin, third polymer, initiator, antioxidant, and lubricant in a high-speed mixer, they are fed into the twin-screw extruder through the metering device to control the double-screw extruder. The temperature of the screw extruder is 180~220℃, the screw length-to-diameter ratio is 40, and the screw speed is 300rpm. Under the c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an ASA (acrylonitrile-styrene-acrylate) resin with favorable appearance performance and a preparation method thereof. The ASA resin comprises the following components in parts by weight: 10-50 parts of SAN (styrene-acrylonitrile), 50-90 parts of ASA crosslinking-modified graft copolymer, 0.2-0.6 part of light stabilizer, 0.2-1 part of antioxidant and 0.2-2 parts of lubricant. The preparation method comprises the following steps: stirring and mixing the raw materials, and sending the mixture into a double screw extruder; and under the actions of delivering, shearing andmixing of the screws, melting and compounding the material, extruding, drawing, cooling, and granulating to obtain the ASA resin with favorable appearance performance. The invention solves the problems of uneven luster, high tendency to irisation and white spotting, and low coloring power in the existing injection-molding ASA resin, thus has excellent appearance performance, and greatly widens the application range of the ASA resin in the fields of building materials, automobiles, electronic and electrical engineering, outdoor supplies, sports equipment and the like.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to an ASA resin with excellent appearance properties and a preparation method thereof. Background technique [0002] Acrylonitrile-acrylate-styrene (ASA) resin is an impact-modified resin formed by the copolymerization of styrene, acrylonitrile and acrylate terpolymer. It is mainly developed for the disadvantage of poor weather resistance of ABS resin. engineering plastics. It was first industrialized by German BASF company in 1962, followed by Japan's Asahi Kasei. At present, ASA is a main product of GE company in the United States. Its Geloy brand co-extruded raw materials were pushed to PVC color co-extruded in 2002. Profile market. The structure of ASA is similar to that of ABS, and it retains the excellent mechanical and physical properties of ABS as an engineering plastic. Since ASA resin introduces acrylate rubber without double bonds instead of butadiene rubber,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L51/00C08L25/12B29B9/06B29C47/92B29C48/92
CPCB29C48/04B29C48/40B29C48/92B29C2948/92704B29C2948/92895
Inventor 周霆邱卫美宋治乾辛敏琦
Owner SHANGHAI KUMHO SUNNY PLASTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap