Method for preparing catalyst by using electrolysis waste water and electrolysis sludge

A technology for electroplating sludge and electroplating wastewater, applied in chemical instruments and methods, physical/chemical process catalysts, metal/metal oxide/metal hydroxide catalysts, etc., can solve environmental pollution, low pollution control level, factory site many other problems to achieve the effect of alleviating environmental pollution

Active Publication Date: 2012-08-08
SHANGHAI UNIV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, due to many problems in my country's electroplating industry, such as many factories, small scale, low level of equipment and low level of pollution control, most of the electroplating sludge is still simply landfilled or even piled up randomly, causing serious pollution to the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing catalyst by using electrolysis waste water and electrolysis sludge
  • Method for preparing catalyst by using electrolysis waste water and electrolysis sludge
  • Method for preparing catalyst by using electrolysis waste water and electrolysis sludge

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0023] The process and steps of this embodiment are as follows:

[0024] (1) Industrial waste electroplating wastewater and sludge are used and pretreated.

[0025] The main heavy metal content (mg / L) in electroplating wastewater is shown in Table 1 below:

[0026] Table 1 Main heavy metal content in electroplating wastewater (mg / L)

[0027] element Ni Zn Cr Cu Fe co Ca Al mg / L 2300.4 3200.6 946.8 3.4 9.7 3.4 18.7 8.9

[0028] The main heavy metal content (wt%) in the electroplating sludge is shown in Table 2 below:

[0029] Table 2 Contents of main heavy metals in electroplating sludge (wt%)

[0030] element Ni Zn Cr Cu Fe co Ca Al g / 100g dry sludge 4.8 6.5 3.5 0.6 50.4 0.2 23.4 1.7

[0031] (2) Mix the above-mentioned electroplating wastewater and electroplating sludge according to a certain ratio: each gram of dry electroplating sludge

[0032] Add 5 mL of electrop...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a process method for preparing a catalyst by using electrolysis waste water and electrolysis sludge, and belongs to the technical field of waste recycling and environmental engineering. The process method comprises the following process steps: mixing, stirring, settling, separating solid from liquid, drying, calcining and the like. Through the coordinated treatment of electrolysis waste water and sludge, which are industrial wastes, and industrial CO2, the use of the process method has a great significance for the treatment of electrolysis waste water and the emissionreduction and capture of green house gases, fully utilizes wastes and fulfils the aim of recycling; and a catalyst can be obtained, the environment pollution can be relieved, and the aim of treating waste with waste is fulfilled.

Description

technical field [0001] The invention relates to a process method for preparing a catalyst by utilizing electroplating wastewater and sludge, in particular to a process method for synergistically treating electroplating sludge and carbon dioxide gas to prepare a catalyst, and belongs to the technical field of waste resource utilization and environmental engineering. Background technique [0002] Since the electroplating industry uses a large amount of strong acid, strong alkali, heavy metal solutions, and even toxic and harmful chemicals such as chromium, cyanide, and chromic anhydride, waste water, waste gas, and waste residue that pollute the environment and endanger human health are discharged during the process. a heavily polluting industry. Electroplating sludge is the discharge produced in the process of electroplating wastewater treatment, which contains a large amount of toxic heavy metals such as copper, cadmium, nickel, zinc, chromium, etc., and its composition is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/86
Inventor 钱光人刘冲郑建昌余颖谷雨吴岳英
Owner SHANGHAI UNIV