Method for quickly detecting crosslinked polyethylene cable insulating material structure

A technology for cross-linked polyethylene and cable insulation, which is applied in the direction of applying stable tension/pressure to test material strength, analyze materials, and measurement devices. It can solve problems such as indirect characterization methods, poor repeatability, and long experiment cycles.

Inactive Publication Date: 2011-09-14
SICHUAN UNIV
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, volatile organic solvents are often used in the equilibrium swelling measurement, so the repeatability of the measurement results is poor
[0007] To sum up, although the existing characterization techniques can reflect the crystal structure and

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for quickly detecting crosslinked polyethylene cable insulating material structure
  • Method for quickly detecting crosslinked polyethylene cable insulating material structure
  • Method for quickly detecting crosslinked polyethylene cable insulating material structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] Put 96.7g of polyethylene PE1030, 0.3g of glycol bis-3-(3-tert-butyl-4-hydroxy-5-methylphenyl) propionate and 3.0g of dicumyl peroxide in the internal mixer , at a temperature of 110° C., 30 rpm, blended for 6 minutes, and discharged to obtain a premixed material. 10 g of the premixed material was cross-linked in a vulcanizer at a temperature of 175° C. for 10 minutes to obtain cross-linked polyethylene.

[0058] The above-mentioned cross-linked polyethylene is subjected to thermal classification analysis, and the results of the thermal classification experiment are further calculated with Thomson-Gibbs equation (1) and statistical formulas (2)-(4), and the wafer thickness distribution curve and number average of the sample are obtained. Wafer thickness L n , Weight average wafer thickness L w , Wafer distribution coefficient I, the results are shown in Tables 1 to 4 and Figure 1.

[0059] L = 2 σ ...

Embodiment 2

[0074] Put 97.8g of polyethylene PE1030, 0.2g of 2,6-di-tert-butyl-4-ethylphenol and 2.0g of 2,5-dimethyl-2,5-di-tert-butylperoxyhexane into the internal mixer , at 118° C., 50 rpm, blended for 9 minutes, and discharged to obtain a premixed material. 10 g of the premixed material was cross-linked in a vulcanizer at 170° C. for 15 minutes to obtain cross-linked polyethylene.

[0075] The above-mentioned cross-linked polyethylene was subjected to thermal classification analysis, and the Thomson-Gibbs equation (1) and statistical formulas (2)-(4) were used to further calculate the results of the thermal classification experiment to obtain the wafer thickness distribution curve and the number average of the samples. Wafer thickness L n , Weight average wafer thickness L w , Wafer distribution coefficient I, the results are shown in Tables 1 to 4 and Figure 1.

[0076] L = 2 σ Δ ...

Embodiment 3

[0091] Put 100.0 g of polyethylene PED4 in an internal mixer, blend at 115° C., 40 rpm, and discharge for 7 minutes to obtain a premixed material. 10 g of the premixed material was cross-linked in a vulcanizer at 175° C. for 10 minutes to obtain cross-linked polyethylene.

[0092] The above-mentioned cross-linked polyethylene was subjected to thermal classification analysis, and the Thomson-Gibbs equation (1) and statistical formulas (2)-(4) were used to further calculate the results of the thermal classification experiment to obtain the wafer thickness distribution curve and the number average of the samples. Wafer thickness L n , Weight average wafer thickness L w , Wafer distribution coefficient I.

[0093] L = 2 σ Δ H 0 * T m 0 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Surface free energyaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for quickly detecting a crosslinked polyethylene cable insulating material structure. The method has the characteristics that: crystallinity, wafer thickness and distribution of a crosslinked polyethylene cable material are detected by a thermal fractionation method; elasticity modulus and entanglement density of the crosslinked polyethylene cable material at a high temperature are detected by a dynamic mechanical method; and a simple and effective method for detecting the crosslinked polyethylene cable insulating material structure is provided by synthesizing the thermal fractionation method and the dynamic mechanical method. By the method, theoretical basis is provided to improve a polymerization process of a polyethylene basic material and adjust a formula of the polyethylene cable insulating material. The method is simple and convenient in test process, sensitive and accurate in result and high in repeatability.

Description

technical field [0001] The invention relates to a method for rapidly detecting the structure of cross-linked polyethylene cable insulating material, which belongs to the field of polymer structure characterization. Background technique [0002] Compared with oil-filled cables, ultra-clean XLPE insulated cables have the advantages of simple structure, fewer production processes, fast production speed, short manufacturing cycle, light weight of cables, convenient installation and use, and are conducive to large-scale production. It is difficult to solve the problem of high drop laying of cables, especially without the danger of major fires caused by oil leakage. The working temperature of the XLPE insulated cable can reach 90°C, and the cross-section of the conductor with the same ampacity can be reduced by one to two grades, which can save the conductor by 20% to 30%, and the cost is also low. Therefore, with the continuous development of the material industry and related in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G01N25/12G01N3/08G01N9/00G01N5/04G01B21/08C08L23/06C08K5/14C08J3/24
Inventor 向明盖景刚杨峰亢健曹亚蔡燎原蓝方
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap