Impregnation formula, impregnation production method and impregnation technology for high temperature resistant conveyer belt

A production process and production method technology, applied in the field of canvas dipping formula, can solve problems such as poor high temperature resistance, and achieve the effects of long service life and good high temperature aging performance

Active Publication Date: 2011-10-19
浙江尤夫科技工业有限公司
View PDF4 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The technical problem to be solved by the present invention is to provide a dipping formula, production method and dipping process for high temperature resistant conveyor belts, so as to overcome the shortcomings of poor high temperature resistance in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0052] Embodiment of the present invention: The formula of the present invention includes a first bath formula and a second bath formula, and the formula is as follows in parts by weight:

[0053] The first bath formula of high heat resistance two bath dipping can be formulated and produced according to the following parts by weight:

[0054] The RF resin formula is as follows:

[0055] Soft water 418.4;

[0056] Sodium hydroxide 5% 10.3;

[0057] Resorcinol solid 18.8;

[0058] Formaldehyde 37% 26.9.

[0059] The RF resin is formulated as follows:

[0060] 1. Put a certain amount of soft water into the reaction tank. The water temperature is controlled at 20℃ + / - 1℃;

[0061] 2. Dissolve a certain amount of soft water with a certain amount of sodium hydroxide, prepare an aqueous solution with a concentration of about 5%, put it into the reaction tank, and stir and mix for 5 minutes. Stirring speed: 60 rpm;

[0062] 3. Dissolve a certain amount of resorcinol solids in soft water to prepare...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses an impregnation formula, an impregnation production method and an impregnation technology for a high temperature resistant conveyer belt. The impregnation technology comprise the following steps that: a impregnation machine contains 5 drying heat treatment baking oven and is equipped with far-infrared predrying; after put on the machine, canvas is unwound with a unwinding tension force of 100kg, and passes through a cloth storage rack with a cloth storage tension force of 160kg; the canvas is impregnated through a impregnation station with a impregnation compression roller pressure of 1000kg; after the impregnation residual slurries are sucked through a vacuum suction with a degree of vacuum of 20MPa; after suction, the canvas enters into far-infrared preheat baking ovens with baking oven temperature preset to 65 DEG C. An impregnation speed is 5m / min; the unwinding tension force is 100kg / m; a dipping adhesive amount of a first bath is 0.7%; a first bath drying temperature is 150-160 DEG C, and a first bath heat treatment temperature is 210 DEG C; a second dipping adhesive amount is 4-6%; a second bath predrying temperature is 90 DEG C; a second bath predrying temperature is 150 DEG C; and a second bath heat treatment temperature is 210 DEG C.

Description

Technical field [0001] The invention relates to a dipping formula, a dipping production method and a dipping process of a canvas for a high temperature resistant rubber conveyor belt. It belongs to the technical field of industrial fabrics. Background technique [0002] Polyester industrial textiles use polyester industrial yarn as the main raw material. Polyester industrial yarn has become the main raw material for industrial textiles due to its high strength, high modulus, and high temperature resistance. Mechanical rubber products—rubber conveyor belts, transmission belts , The skeleton material necessary for rubber hose has been basically polyesterified. Polyester material has a melting point of 264°C and has good heat resistance. Therefore, polyester dipped canvas has generally replaced the earlier cotton canvas, and various high temperature resistant conveyor belt applications have shown its strong advantages. [0003] The transportation of coal slag in power plants, sinter...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/564D06M15/41C08G8/22D06N3/18D06M101/32
Inventor 茅惠新
Owner 浙江尤夫科技工业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap