Formula of imitative wood filling slurry for building formwork supporting keel and processing method

A technology for building formwork and keels, which is applied in sustainable waste treatment, solid waste management, climate sustainability, etc. It can solve problems such as filling slurry formulation problems, and achieve the effects of low cost, high strength, and convenient processing

Active Publication Date: 2011-11-02
YUNNAN INST OF BUILDING RES
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] One of the purposes of the present invention is to provide a building formwork support keel imitation wood filling slurry formula to solve the problem of filling slurry formula in practical applications
[0006] The second object of the present invention is to disclose a processing method of building formwork support keel imitation wood filling slurry to solve the processing problem of imitation wood filling slurry in practical application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A. Detect and adjust the particle size of recycled rubber powder to meet the following requirements:

[0033] 40 mesh 10%

[0034] 60 mesh 10%

[0035] 80 mesh 25%

[0036] 100 mesh 25%

[0037] More than 120 mesh 30%

[0038] All the above are percentages by mass.

[0039] B. Soak the sawdust with antiseptic oil for later use.

[0040] C, first put the above-mentioned recycled rubber powder, sawdust and hydraulic cementitious material for standby use in a high-speed mixer according to the mass percentage of recycled rubber powder 15%, sawdust 24%, and hydraulic cementitious material 27%. After 3 minutes, add 33% water and 1% additive by mass, and then mix for 2 minutes to make building formwork support keel imitation wood filling slurry. Among them, high-strength Portland cement is selected as the hydraulic cementitious material; polyvinyl formal is selected as the additive.

Embodiment 2

[0042] A. Detect and adjust the particle size of recycled rubber powder to meet the following requirements:

[0043] 59 mesh 20%

[0044] 79 mesh 20%

[0045] 99 mesh 20%

[0046] 119 mesh 20%

[0047] More than 120 mesh 20%

[0048] All the above are percentages by mass.

[0049] B. The crushed platycodon grandiflorum of the agricultural crop is soaked with coal tar and then set aside.

[0050] C, first put the above-mentioned treated standby recycled rubber powder, sawdust and hydraulic cementitious material in a high-speed mixer according to the mass percentage of recycled rubber powder 20%, sawdust 28%, and hydraulic cementitious material 21%. After 3 minutes, add 30% water and 1% additive by mass, and mix for another 2 minutes to make building formwork support keel imitation wood filling slurry. Among them, high-strength Portland cement is selected as the hydraulic cementitious material; polyvinyl formal is selected as the additive.

Embodiment 3

[0052] A. Detect and adjust the particle size of recycled rubber powder to meet the following requirements:

[0053] 50 mesh 15%

[0054] 65 mesh 15%

[0055] 85 mesh 20%

[0056] 110 mesh 20%

[0057] More than 120 mesh 30%

[0058] All the above are percentages by mass.

[0059] B. Soak the sawdust with anthracene oil for later use.

[0060] C, first put the above-mentioned regenerated rubber powder, sawdust and hydraulic cementitious material for standby use in a high-speed mixer according to the mass percentage of 18% of recycled rubber powder, 25% of sawdust, and 24% of hydraulic cementitious material After 3 minutes, add 32% water and 1% additive by mass, and mix for another 3 minutes to make building formwork support keel imitation wood filling slurry. Among them, high-strength Portland cement is selected as the hydraulic cementitious material; polyvinyl formal is selected as the additive.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a formula of imitative wood filling slurry of a building formwork supporting keel and a processing method. The formula comprises reclaimed rubber powder, plant fibers, hydraulic cementing materials, an additive agent and water. The processing method comprises the following steps of: (1) detecting and adjusting the particle size of the reclaimed rubber powder to accord with a combination requirement for later use; (2) carrying out immersion treatment on sawdust or pulverized matters of crop platycodon grandiflorum by using antiseptic oil or coal tar or anthracene oil for later use; (3) firstly, placing the reclaimed rubber powder, the plant fibers and the hydraulic cementing materials processed for later use in a high-speed mixing device according to the proportion of the components, adding water and the additive agent after mixing for 2-3 minutes, mixing for 2-3 minutes again to prepare the imitative wood filling slurry for the building formwork supporting keel. The imitative wood filling slurry has the remarkable advantages of low cost, high strength and convenience for processing.

Description

technical field [0001] The invention belongs to the technical field of metal-reinforced concrete structure formwork support structure, especially the formula and processing method of building formwork support keel imitation wood filling slurry. Background technique [0002] In construction engineering, the key to the forming quality of reinforced concrete structures lies in the formwork installation quality, and the key to the formwork installation quality lies in the formwork support system. To ensure the strength, stiffness and stability of the formwork support system, the support poles, keels and connectors in the support system play a decisive role. The support keel transmits the load from the formwork to the support pole, and its strength, stiffness and stability directly affect the quality of formwork installation and the performance of its functions. [0003] At present, the keels of the formwork support system in engineering practice include shaped steel keels, wood...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B28/06C04B18/22C04B18/24
CPCC04B28/04C04B20/026C04B20/1025Y02W30/91C04B18/22C04B24/26C04B18/24C04B18/26C04B20/0076C04B24/2623C04B40/005
Inventor 彭彪李继荣孙群刘光宗李宏雷杨永菊
Owner YUNNAN INST OF BUILDING RES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com