Composite color-coating chromium-free passivating solution based on waterborne epoxy resin for galvanized sheet

A water-based epoxy resin, chromium-free passivation technology, applied in the direction of metal material coating process, to achieve the effect of improving corrosion resistance, excellent water resistance and alkali resistance, and simplifying the color coating process

Inactive Publication Date: 2011-11-23
ANHUI UNIVERSITY OF TECHNOLOGY
View PDF8 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of this patent is to overcome the problem of using chromium-containing surface treatment liquid for existing color-coated sheets, and provide a chromium-free passivation solution for color-coated galvanized sheets based on water-based epoxy resin composite

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Example 1: Prepare 1 liter of passivation solution with a pH value of 2~3 with an effective content of 100g of organic resin, 20g of organic acid, 3.3g of inorganic passivator, 3g of oxidant, and the rest of water and phosphoric acid. Among them, the organic resin is water-based epoxy resin and water-based curing agent resin, which are prepared according to the mass ratio of effective content of 2:1. The inorganic passivation agent is titanium oxysulfate and nickel nitrate, which is prepared according to the mass ratio of effective content of 1:6.

[0034] After the galvanized sheet pretreated by the above process, the area of ​​white rust in the 96h neutral salt spray test is less than 20%. After the electrochemical test, the self-corrosion potential is -0.9943V, and the self-corrosion current density is 108.3000 μA cm -2 , the polarization resistance is 0.3460kΩ·cm -2 . The scratch test found that there were peeling marks on the smooth edge of the cut, but the pee...

Embodiment 2

[0035] Example 2: Use organic resin with an effective content of 100g, 20g of organic acid, 3.3g of inorganic passivator, 3g of oxidant, and the rest of water and phosphoric acid to prepare 1 liter of passivation solution with a pH value of 2~3. Among them, the organic resin is water-based epoxy resin and water-based curing agent resin, which are formulated according to the mass ratio of the effective content of 1:2. The inorganic passivation agent is titanium oxysulfate and nickel nitrate, which is prepared according to the mass ratio of effective content of 1:3.

[0036] After the galvanized sheet pretreated by the above process, the area of ​​white rust in the 96h neutral salt spray test is less than 15%. After the electrochemical test, the self-corrosion potential is -0.9340V, and the self-corrosion current density is 74.9900 μA cm -2 , the polarization resistance is 0.5150kΩ·cm -2 . The scratch test found that there were peeling marks on the smooth edge of the cut, b...

Embodiment 3

[0037] Example 3:Prepare 1 liter of passivation solution with a pH value of 2~3 with an effective content of 150g of organic resin, 50g of organic acid, 5.8g of inorganic passivator, 12g of oxidant, and the rest of water and phosphoric acid. Among them, the organic resin is water-based epoxy resin and water-based curing agent resin, which are formulated according to the mass ratio of the effective content of 1:2. The inorganic passivation agent is titanium oxysulfate and nickel nitrate, which is prepared according to the mass ratio of effective content of 1:6.

[0038] After the galvanized sheet pretreated by the above process, the area of ​​white rust in the 96h neutral salt spray test is less than 15%. After the electrochemical test, the self-corrosion potential is -0.9330V, and the self-corrosion current density is 30.5600 μA cm -2 , the polarization resistance is 1.3610kΩ·cm -2 . The scratch test found that there were peeling marks on the smooth edge of the cut, but t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electric potential / voltageaaaaaaaaaa
current densityaaaaaaaaaa
electric potential / voltageaaaaaaaaaa
Login to View More

Abstract

The invention provides a composite color-coating chromium-free passivating solution based on waterborne epoxy resin for a galvanized sheet, belonging to the technical field of galvanized sheet surface treatment. The chromium-free passivating solution comprises the following components in contents per each liter: organic resin 100-300 g / L, organic acid 20-75 g / L, inorganic salt 2-6 g / L, oxidant 3-12 g / L, a certain amount of pH value regulator, and the balance of deionized water. Phosphoric acid is used as the pH value regulator for regulating the chromium-free passivating solution to be 2-3. The composite color-coating chromium-free passivating solution based on the waterborne epoxy resin for the galvanized sheet is characterized in that the waterborne epoxy resin, the organic acid, the inorganic salt and the oxidant are organically combined to act on the galvanized sheet so as to form a compact organic inorganic composite passive film. The chromium-free passivating solution provided by the invention is beneficial to simplifying the color-coating technology of the galvanized sheet and reducing the cost. The composite color-coating chromium-free passivating solution based on the waterborne epoxy resin for the galvanized sheet has no chromium in any valance state and is an environment-friendly chromium-free passivating solution.

Description

technical field [0001] The invention belongs to the technical field of surface treatment of galvanized sheets, and in particular relates to a chromium-free passivation solution for color coating of galvanized sheets based on water-based epoxy resin composite. technical background [0002] In order to improve the corrosion resistance and coating performance of color-coated galvanized sheets, hexavalent chromium is often used in industry to passivate the surface of galvanized sheets. However, according to the EU RoHS standard, surface passivation solutions containing hexavalent chromium are strictly regulated limits. At present, the research on the surface treatment solution of galvanized sheet is concentrated on the chromium-free passivation solution, which mainly includes inorganic passivation (using molybdate, silicate, rare earth salt and other inorganic salt passivation) and organic passivation (using plant acid, tannic acid, silane, resin and other organic matter passiv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/07
Inventor 张千峰叶鹏飞陈均胡丰徐丽萍
Owner ANHUI UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More