TiAl-based alloy with excellent high temperature oxidation resistance and creep resistance suitable for casting

A high-temperature anti-oxidation and creep performance technology, applied in the field of titanium-aluminum-based alloys, can solve the problems of poor high-temperature creep performance and high-temperature oxidation resistance of titanium-aluminum alloy materials, so as to improve oxidation resistance and high-temperature creep resistance. Effect of changing performance and increasing room temperature

Active Publication Date: 2013-01-02
LUOYANG SUNRUI TI PRECISION CASTING
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The high-temperature creep performance and high-temperature oxidation resistance of low-Nb (usually 1-3at%Nb) titanium-aluminum alloy materials are very poor, especially when the temperature is used for a long time at 850°C-950°C, the surface of the material is severely oxidized. Therefore, low Nb titanium-aluminum alloys are usually not suitable for the preparation of parts that are used for a long time in a high temperature environment of 850-950 °C

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • TiAl-based alloy with excellent high temperature oxidation resistance and creep resistance suitable for casting

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] The titanium aluminum material of the present invention all adopts sponge titanium, pure Al, AlNb50 alloy, AlMo60, AlSi10 alloy, pure C powder as raw material, carries out batching according to the composition and content requirement of embodiment 1--embodiment 9, in vacuum induction furnace Melt and cast turbine formwork. The smelting method of titanium-aluminum ingots for casting is as follows: first, vacuumize to 3.5Pa, and melt the raw materials of the new titanium-aluminum alloy material with argon pressure at 60,000 Pa. The ingot is repeatedly smelted 2 times. The casting process of the turbine formwork is as follows: the pre-vacuum degree is 3.5Pa, and the titanium-aluminum ingot is completely melted and then stirred for 2 minutes before casting the turbine formwork.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a TiAl-based alloy with excellent high temperature oxidation resistance and creep resistance suitable for casting and the alloy belongs to the gamma-TiAl alloy. The TiAl-based alloy comprises the following components by atomic percent: 44.0-48.0% of Al, 1.0-3.0% of Nb, 0.1-3.0% of Mo, 0-0.8% of Si or / and 0-0.6% of C, and the balance of Ti and impurity elements, wherein thesum of the atomic percents of Si and C is 0.1-0.9%. The TiAl-based alloy disclosed by the invention has good high temperature performances and casting fluidity and is suitable for the casting of thin-walled parts; methods such as chemical treatment, thermal spraying and ion implantation which are used to increase the oxidation resistance, are not required to treat the surface of the alloy at 850-950 DEG C; and the TiAl-based alloy is particularly suitable to cast the gasoline engine supercharger turbine rotor which can work below 900-950 DEG C.

Description

technical field [0001] The invention relates to a technology in the field of high-temperature alloys, in particular to a titanium-aluminum-based alloy that has excellent high-temperature oxidation resistance and creep resistance and is suitable for casting. Background technique [0002] With the continuous improvement of the performance of engines such as aviation, aerospace, automobiles, and ships, higher requirements are put forward for the performance of high-temperature materials, that is, higher strength, oxidation resistance, and lighter density. γ-TiAl-based alloy materials have the advantages of good high temperature strength, creep resistance and oxidation resistance, etc., and are developing into a new generation of aero-engine materials, which can be used to manufacture compressors, gas turbine blades, compressor stator windshields, stator machines Blocks and other large-scale casting and forging parts with complex shapes can partially replace bulky nickel-ba...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C14/00
Inventor 周洪强陈志强包淑娟王孟光吴胜男刘国良
Owner LUOYANG SUNRUI TI PRECISION CASTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com