PC/ABS alloy possessing metal luster and its preparation method

A metal luster and alloy technology, which is applied in the field of PC/ABS alloy and its preparation, can solve the problems of potential safety hazards, explosions, and fires, and achieve the effects of not being prone to fires and explosions, reducing production costs, and eliminating potential safety hazards

Inactive Publication Date: 2012-02-08
SHENZHEN KEJU NEW MATERIAL
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are serious safety hazards in this technology. During the mixing, kneading, extrusion, and granulation of silver powder and gold powder with plastics, there is a risk of fire and explosion.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PC/ABS alloy possessing metal luster and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Polycarbonate (PC): 30% by weight percentage; ABS: 60%; Toughening agent: 5%; Antioxidant: 0.2%; Coupling agent: 1%; Processing aid: 0.8%; 3% is mixed in a high-speed mixer for 12 minutes, melted and extruded by a twin-screw extruder, and granulated. The temperature in the zone is 215°C, the temperature in the fifth zone is 235°C, the temperature in the sixth zone is 235°C, the temperature in the seventh zone is 235°C, and the temperature in the eighth zone is 240°C; the residence time in the barrel is 90S, and the melt pressure is 15MPa.

Embodiment 2

[0043] Polycarbonate (PC): 40% by weight percentage; ABS: 46%; Toughening agent: 8%; Antioxidant: 0.5%; Coupling agent: 2%; Processing aid: 1%; 2.5% is mixed in a high-speed mixer for 12 minutes, melted and extruded by a twin-screw extruder, and granulated. The temperature in the zone is 215°C, the temperature in the fifth zone is 235°C, the temperature in the sixth zone is 235°C, the temperature in the seventh zone is 235°C, and the temperature in the eighth zone is 240°C; the residence time in the barrel is 90S, and the melt pressure is 15MPa.

Embodiment 3

[0045] Polycarbonate (PC): 50% by weight percentage; ABS: 35%; Toughening agent: 12%; Antioxidant: 0.8%; Coupling agent: 0.2%; Processing aid: 0.5%; 1.5% is mixed in a high-speed mixer for 12 minutes, melted and extruded by a twin-screw extruder, and granulated. The temperature in the zone is 215°C, the temperature in the fifth zone is 235°C, the temperature in the sixth zone is 235°C, the temperature in the seventh zone is 235°C, and the temperature in the eighth zone is 240°C; the residence time in the barrel is 90S, and the melt pressure is 15MPa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a PC / ABS alloy possessing metal luster and its preparation method. The PC / ABS alloy possessing metal luster comprises the following ingredients by weight percentage: 30-80% of polycarbonate, 10-60% of acrylonitrile-styrene-butadiene copolymer; 5-20% of flexibilizer; 0.2-2% of coupling agent; 0.2-1% of anti-oxidant; 0.5-2% of processing auxiliary agent and 0.5-3% of pearl powder. According to the invention, the pearl powder replaces of metal powder, the fire hazard and blast are not easy to happen during the preparation process, so that the potential safety hazard can be eliminated. The pearl powder has small influence on the material performance; the material keeps good mechanical property. The material has metal luster which is a substitution of metal material in certain extent, thereby the production cost of the product can be effectively reduced.

Description

[technical field] [0001] The invention relates to the field of polymer materials, in particular to a PC / ABS alloy with metallic luster and a preparation method thereof. [Background technique] [0002] The lightweight of the car is to reduce the curb weight of the car as much as possible under the premise of ensuring the strength and safety performance of the car, so as to improve the power of the car, reduce fuel consumption, and reduce exhaust pollution. Most of a car's weight comes from its metal components. In order to reduce the weight of automobiles, replacing metal with plastics has become a trend in the development of the automobile industry. [0003] At present, the interior parts of foreign automobiles have basically been plasticized, and the application range of plastics in automobiles is expanding from interior parts to exterior parts, body parts and structural parts. The key development direction in the future is to develop reinforced plastic composite material...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L55/02C08K13/06C08K5/134C08K5/20C08K9/10C08K9/02C08K3/34B29C47/92B29C48/92
Inventor 徐东徐永陈土华
Owner SHENZHEN KEJU NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com