Method for producing acrylic acid priming paint base-material and acrylic acid priming paint

A technology of acrylic acid and methyl methacrylate, which is applied in the field of paint making, can solve the problems of topcoat containing and not meeting the performance requirements of water boiling, and achieve the effect of no difference in weather resistance performance, similar formula cost, and low metallic feeling

Inactive Publication Date: 2012-03-07
深圳市美丽华科技股份有限公司
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a kind of base material of acrylic primer and the preparation method of acrylic primer, aiming at solv

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] The present invention also provides the preparation technology of acrylic primer:

[0033] S100, make the base material of the primer with the above base material formula, and stir for 5 minutes at a speed of 400-600 revolutions per minute;

[0034] S200. Add halogen-free color paste with a content not higher than 25% (weight ratio) while stirring according to the color required by the paint user;

[0035] S300, after feeding and color matching, continue to stir for 30 minutes to complete the primer produced with the base material formula of the present invention.

[0036] In the preparation process of the present invention, the following steps may also be included after step S200:

[0037] S210, adding aluminum paste and (or) pearl powder with a halogen-free content not higher than 8% (by weight).

[0038] The main application process of the acrylic primer product produced with the acrylic primer base material formula of the present invention:

[0039] Surface treat...

Embodiment 1

[0055] Polystyrene modified methyl methacrylate 62.5%;

[0056] 80-200 seconds nitrocellulose solution 27.5%;

[0057]Cyclohexanone 2.5%;

[0058] Toluene 5.0%;

[0059] Ethyl acetate 2.0%;

[0060] Polyacrylic acid leveling agent (BYK-358) 0.5%.

[0061] Use the above-mentioned base material formula to make the base material of the primer, and stir at a speed of 400-600 rpm for 5 minutes; while stirring, add a halogen-free color paste with a weight ratio not higher than 25%, and the color matching is completed Then continue to stir for 30 minutes and have just completed the primer produced with the base material formula of the present invention. The acrylic primer produced by the base material formula of this embodiment is used in conjunction with spraying diluent and ultraviolet radiation curing topcoat, sprayed on polycarbonate plastic, and dried and cured.

Embodiment 2

[0063] Polystyrene modified methyl methacrylate 60.0%;

[0064] 80-200 seconds Nitrocellulose solution 30.0%;

[0065] Cyclohexanone 5.0%;

[0066] Toluene 1.0%;

[0067] Ethyl acetate 3.9%;

[0068] Polyacrylic acid leveling agent (BYK-358) 0.1%.

[0069] Use the above-mentioned base material formula to make the base material of the primer, and stir at a speed of 400-600 rpm for 5 minutes; while stirring, add a halogen-free color paste with a weight ratio not higher than 25%, and the color matching is completed Then continue to stir for 30 minutes and have just completed the primer produced with the base material formula of the present invention. The acrylic primer produced by the base material formula of this embodiment is used in conjunction with spraying diluent and ultraviolet radiation curing topcoat, sprayed on polycarbonate plastic, and dried and cured.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for producing an acrylic acid priming paint base-material and an acrylic acid priming paint. The polystyrene modified methyl methacrylate and 80-200 seconds nitro cellulose liquid are taken as the main components in an acrylic acid priming paint base-material formula, and a solvent and a leveling agent are also concluded. The acrylic acid priming paint base-material formula accords with the halogen-free requirement of the cell phone industry on paint (bromine content in the formula is less than 900ppm, chlorine content in the formula is less than 900ppm, the total content of bromine and chlorine is less than 1500ppm). The acrylic acid priming paint produced by the base-material formula is matched with a spraying diluent and an ultraviolet radiation solidification topcoat to spray on the polycarbonate plastics, the dried and solidified coating has excellent water-boiling resistance, the coating has no foaming, no cracking and no discoloration after being boiled for 30 minutes in boiling water at the temperature of 100 DEG C.

Description

technical field [0001] The invention relates to the field of paint making, in particular to an acrylic primer base material and a preparation method of the acrylic primer. Background technique [0002] At present, the plastic casing and buttons of mobile phones are painted with halogen-containing primers and UV radiation-curable topcoats, and some are coated with halogen-free primers and UV radiation-curable topcoats. With the environmental management of some foreign mobile phone manufacturers The limitation of substances has clearly stipulated the halogen content in the mobile phone coating formula, requiring the bromine content in the mobile phone coating formula to be less than 900ppm, the chlorine content to be less than 900 ppm, and the total content of bromine and chlorine to be less than 1500 ppm. Some mobile phone manufacturers are no longer in compliance; so far, no halogen-free primer and UV-curable topcoat have been found that can pass the test of boiling at 100°C...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D125/14C09D133/12C09D101/18C09D7/12C08J7/04
Inventor 鲁春风
Owner 深圳市美丽华科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap