Relieved tooth and preparation method thereof

A technology of shovel teeth and mass percentage, applied in the field of shovel teeth for loaders and their preparation, can solve the problems of complex smelting process, unsatisfactory wear resistance of materials, and high cost of raw materials and heat treatment

Inactive Publication Date: 2012-04-04
NINGBO JIADA PRECISION CASTING
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Existing wear-resistant steel for shovel teeth, such as ZGMn 13 The material, whose hardness after solid solution treatment is HB170-210, has good strong impact resistance, but its wear resistance mai...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Relieved tooth and preparation method thereof
  • Relieved tooth and preparation method thereof
  • Relieved tooth and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] The composition and mass percentage of the shovel teeth in this embodiment are: C: 0.29%, Mn: 0.90%, Si: 0.8%, Cr: 1.40%, B: 0.001%, Al: 0.02%, and the balance is Fe. At the same time, due to the adverse effects of S and P elements on the mechanical properties of the shovel teeth, it is necessary to ensure that the mass percentage of the S element is less than or equal to 0.025%, and the mass percentage of the P element is less than or equal to 0.025%.

[0013] As the basic element of alloy steel, C element forms carbides with Fe and Mn, which improves the hardness and wear resistance of steel, and plays an important role in solid solution strengthening.

[0014] Although Mn element is an element that promotes the formation of austenite in alloy steel, the content of Mn element is usually higher, above 10%. However, under the premise of ensuring the austenite structure, with the decrease of the content of Mn element, although the stability of austenite decreases, the pr...

Embodiment 2

[0027] The composition and mass percentage of the shovel teeth in this embodiment are: C: 0.31%, Mn: 1.2%, Si: 1.0%, Cr: 1.50%, B: 0.003%, Al: 0.03%, and the balance is Fe. At the same time, due to the adverse effects of S and P elements on the mechanical properties of the shovel teeth, it is necessary to ensure that the mass percentage of the S element is less than or equal to 0.025%, and the mass percentage of the P element is less than or equal to 0.025%.

[0028] In this embodiment, the shovel teeth go through a casting process and a heat treatment process. The heat treatment process adopts the same process conditions as in Example 1, that is, quenching after heating up to 900 ° C and tempering at 220 ° C to 250 ° C after holding for 2-4 hours Temper at low temperature, and keep warm for 2-4 hours after tempering. Test its mechanical properties as shown in Table 2:

[0029] Table 2

[0030]

[0031] After adopting the ratio of this embodiment, the mechanical propertie...

Embodiment 3

[0033] The composition and mass percentage of the shovel teeth in this embodiment are: C: 0.33%, Mn: 1.40%, Si: 1.20%, Cr: 1.70%, B: 0.005%, Al: 0.06%, and the balance is Fe. At the same time, due to the adverse effects of S and P elements on the mechanical properties of the shovel teeth, it is necessary to ensure that the mass percentage of the S element is less than or equal to 0.025%, and the mass percentage of the P element is less than or equal to 0.025%.

[0034] In this embodiment, the shovel teeth go through a casting process and a heat treatment process. The heat treatment process adopts the same process conditions as in Example 1, that is, quenching after heating up to 900 ° C and tempering at 220 ° C to 250 ° C after holding for 2-4 hours Temper at low temperature, and keep warm for 2-4 hours after tempering. Test its mechanical properties as shown in Table 3:

[0035] table 3

[0036]

[0037] After adopting the ratio of this embodiment, the mechanical propert...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a relieved tooth and a preparation method thereof, and the relieved tooth and the preparation method disclosed by the invention can be used for solving the problems of poor abrasion resistance and impact property of an existing relieved tooth. The relieved tooth disclosed by the invention comprises the following compositions in percentage by weight: 0.29%-0.33% of C, 0.90%-1.40% of Mn, 0.8%-1.20% of Si, 1.40%-1.70% of Cr, 0.001%-0.005% of B, 0.02%-0.06% of Al and the balance of Fe. The invention provides the preparation method for preparing the relieved tooth, and the preparation method comprises a casting process and a thermal treatment process. The relieved tooth disclosed by the invention is good in mechanical property, high in hardness, high in tensile strengthand high in tenacity and can meet the special working environment requirements of a loader.

Description

technical field [0001] The invention relates to a shovel tooth and a preparation method thereof, in particular to a shovel tooth for a loader and a preparation method thereof. Background technique [0002] Loader shovel teeth are important parts on the loader, similar to human teeth, and are also vulnerable parts. The shovel teeth of the loader directly work with the ore, and are subjected to strong abrasive wear, and the force is complex and periodically changed. At the same time, the shovel teeth of the loader are also accompanied by high stress when working with the ore, and their service conditions are very harsh. Therefore, the shovel teeth High wear resistance requirements, but also requires good comprehensive mechanical properties. [0003] Existing wear-resistant steel for shovel teeth, such as ZGMn 13 The material has a hardness of HB170-210 after solid solution treatment, and has good strong impact resistance, but its wear resistance mainly comes from the hardeni...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/32C21D1/18E02F9/28
Inventor 钱嘉镕新
Owner NINGBO JIADA PRECISION CASTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap