High-dehydration hardenable plugging sealing agent
A plugging agent and high water loss technology, applied in hardenable, plugging plugging agent, and high water loss fields, it can solve the problems of difficult construction and plugging failure, and achieve simplified drilling procedures, fast plugging speed, High plugging success rate
Active Publication Date: 2012-05-09
BC P INC CHINA NAT PETROLEUM CORP +1
View PDF2 Cites 58 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
During the plugging process of the curable cement slurry system, the cement slurry is not easy to stay in the lost channel, and the plugging failure is often caused by leakage int
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Example Embodiment
[0010] Example 1: 35Kg of solidified material, 25Kg of composite lost circulation agent, 15Kg of high water loss material, 10Kg of elastic expansion material, and 15Kg of fiber material.
Example Embodiment
[0011] Example 2: 40 Kg of cured material, 30 Kg of composite leak-stopping agent, 10 Kg of high water loss material, 5 Kg of elastic expansion material, and 15 Kg of fiber material.
Example Embodiment
[0012] Example 3: 45 Kg of cured material, 35 Kg of composite leak-stopping agent, 5 Kg of high water loss material, 5 Kg of elastic expansion material, and 10 Kg of fiber material.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Login to view more Abstract
The invention relates to a high-dehydration hardenable plugging sealing agent which comprises the following components by mass percent: 35-50% of solidifying material, 25-35% of composite sealing agent, 5-15% of high-dehydration material, 5-10% of elastic expending material and 10-15% of fiber material, wherein the composite sealing agent is formed by mixing granular husk, mica and cotton seed hull in a mass ratio of 5:2:1; the solidifying material is formed by mixing gypsum, cement, blast furnace slag and sodium phosphate in a mass ratio of 1:1:0.5:0.1; the high-dehydration material is kieselguhr or coal ash; the elastic expending material is formed by mixing coated water-sucking rubber and coated water-sucking resin in a mass ratio of 1:1; and the fiber material is polyacrylonitrile fiber of 9-11mm. The sealing agent integrates with high dehydration, delay expanding, plugging solidification and physical overlap joint; and the formed sealing layer is not easy to destroy in the subsequent drilling process, thereby effectively improving the sealing efficiency.
Description
technical field [0001] The invention relates to an additive used in the field of oil field drilling, in particular to a high water loss, hardenable, plugging and plugging agent. Background technique [0002] Lost circulation is a phenomenon in which drilling fluid, cement slurry or other working fluids are lost into the formation during drilling. The occurrence of lost circulation not only consumes drilling time and loss of drilling fluid, but also may cause a series of complex situations such as pipe sticking, blowout, and well collapse. In severe cases, the wellbore will be scrapped and cause major economic losses. [0003] Currently commonly used plugging materials are mainly divided into physical plugging materials and chemical plugging materials: physical plugging materials mainly include bridging plugging materials and high water loss plugging materials. The bridging plugging material is mainly based on the principle of particle gradation, using walnut shells, mica fl...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more IPC IPC(8): C09K8/46
Inventor 竹学友刘永贵何恕郝立志赵晓竹闫晶姜强
Owner BC P INC CHINA NAT PETROLEUM CORP
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap