Coated part and manufacturing method thereof

A production method and technology for coating parts, which are applied in the field of coating parts and their production, can solve the problems of decreased anti-corrosion performance, poor wear resistance, and affect the appearance, so as to improve wear resistance and service life, and the method is simple and easy to implement. Efficiency-enhancing effect

Inactive Publication Date: 2012-05-30
HONG FU JIN PRECISION IND (SHENZHEN) CO LTD +1
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the preparation process of this coating is also complicated, and some fillers doped in the anti-fingerprint paint and anti-fingerprint oil also contain free formaldehyde, which is not conducive to environmental protection and human health.
Moreover, this kind of organic coating has poor wear resistance and is easy to wear after a period of use, so that the substrate is exposed, the corrosion resistance performance is greatly reduced and the appearance is affected
In addition, the use of anti-fingerprint oil will make the surface of the coating look greasy, greatly reducing the visual aesthetics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coated part and manufacturing method thereof
  • Coated part and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] see figure 1 , a coating member 10 according to a preferred embodiment of the present invention includes a substrate 11 and an anti-fingerprint layer 13 formed on the surface of the substrate 11 .

[0017] The base body 11 can be made of metallic or non-metallic materials. The metal material may include stainless steel, aluminum, aluminum alloy, copper, copper alloy and the like. The non-metallic material is mainly plastic. The base body 11 has a rough surface, which is directly combined with the anti-fingerprint layer 13 . The roughness of the rough surface is 0.1 to 0.2 μm.

[0018] Anti-fingerprint layer 13 is a nanoscale tin dioxide (SnO 2 ) layer, which can be made by vacuum sputtering, such as magnetron sputtering. The thickness of the anti-fingerprint layer 13 is below 2 microns (μm), preferably 0.1-0.5 μm. The anti-fingerprint layer 13 is directly formed on the rough surface of the substrate 11 and has strong bonding force with the substrate 11 . The anti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
surface roughnessaaaaaaaaaa
Login to view more

Abstract

The invention provides a coated part and a manufacturing method of the coated part. The coated part comprises a basal body and an anti-fingerprint coating formed on the surface of the basal body, wherein the anti-fingerprint coating is a nano-sized tin dioxide coating and nano-sized protrusions are formed on the surface of the coating. The manufacturing method of the coated part comprises the following steps of: providing a basal body and forming an anti-fingerprint coating on the surface of the basal body by vacuum sputtering method, wherein the anti-fingerprint coating is a nano-sized tin dioxide coating and nano-sized protrusions are formed on the surface of the coating.

Description

technical field [0001] The invention relates to a film-coated part and a manufacturing method thereof, in particular to a film-coated part with an anti-fingerprint function and a manufacturing method of the film-coated part. Background technique [0002] In the traditional technology, the early anti-fingerprint treatment is generally used to form a chromate layer and a special resin layer on the galvanized layer of stainless steel. This method first needs to electroplate a layer of zinc on the stainless steel plate, then apply chromate treatment, and finally apply a layer of resin by rolling. The process is complicated and requires chromate treatment, which seriously pollutes the environment. higher cost. [0003] Therefore, in order to avoid pollution and reduce costs, people began to study new anti-fingerprint materials. At present, it is widely used in industry to spray a layer of organic chemical substances on the substrate, such as anti-fingerprint paint and anti-fing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C14/08C23C14/34
CPCC23C14/028C23C14/086C23C14/022Y10T29/49
Inventor 张新倍陈文荣蒋焕梧陈正士彭立全
Owner HONG FU JIN PRECISION IND (SHENZHEN) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap