Monocomponent addition type silicone rubber packaging glue with strong cohesiveness and preparation method thereof

A cohesive and additive technology, applied in the direction of polymer adhesive additives, non-polymer adhesive additives, chemical instruments and methods, etc., can solve the problems of poor bonding performance of substrates and improve production efficiency , time-saving, strong bonding effect

Active Publication Date: 2012-06-13
SHANGHAI RES INST OF CHEM IND
View PDF5 Cites 46 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Throughout the existing patents and literature, the addition-type silicone rubber encapsulant described therein is either a one-component system but has poor bonding performance with the substrate after vulcanization; or it is a two-component system that needs to be mixed before use. two-component

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] In parts by weight, add 30 parts of 1,3,5,7-tetramethylcyclotetrasiloxane and 115 parts of allyl glycidyl ether into the three-necked flask; blow nitrogen, add 0.1 parts of platinum catalyst, and react at 60°C for 3 hours ; Reaction mixture 150 ° C under reduced pressure (10kPa) distillation to remove low boilers, to obtain organopolysiloxane tackifier.

[0020] In parts by weight, 80 parts of vinyl silicone oil with a vinyl content of 0.1wt% and a viscosity of 1000mPa·s, 10 parts of MQ silicone resin with a viscosity of 1000mPa·s, 20 parts of hydrogen-containing silicone oil with a hydrogen content of 0.3wt%, organic Mix 2 parts of polysiloxane tackifier, 2 parts of white carbon black, and 5 parts of titanium dioxide in a mixer for 30 minutes at high speed (3500 rpm); then add 0.1 part of inhibitor and mix at high speed for 10 minutes (3500 rpm); finally add 0.2 parts of platinum catalyst were mixed at a medium speed for 30 minutes (1500 rpm), and discharged to obtain ...

Embodiment 2

[0026] The preparation method of the organopolysiloxane tackifier is the same as in Example 1.

[0027] In parts by weight, 100 parts of vinyl silicone oil with a vinyl content of 5.0wt% and a viscosity of 7500mPa·s, 5 parts of MTQ silicone resin with a viscosity of 30000mPa·s, 10 parts of hydrogen-containing silicone oil with a hydrogen content of 3.0wt%, organic 1 part of polysiloxane tackifier, 3 parts of white carbon black, and 1 part of titanium dioxide were mixed in a mixer for 10 minutes at high speed (4000 rpm); then 0.3 parts of inhibitor were added and mixed at high speed for 5 minutes (4000 rpm); finally added 0.5 parts of the platinum catalyst were mixed at a medium speed for 10 minutes (2000 rpm), and discharged to obtain a one-component strong adhesive addition type silicone rubber encapsulant.

[0028] The one-component strong cohesive addition type silicone rubber encapsulant obtained above was made into a sample according to GB / T 7124-2008 (Determination of Te...

Embodiment 3

[0033] The preparation method of the organopolysiloxane tackifier is the same as in Example 1.

[0034]In parts by weight, 120 parts of vinyl silicone oil with a vinyl content of 10.0wt% and a viscosity of 10000mPa·s, 20 parts of MT silicone resin with a viscosity of 10000mPa·s, 30 parts of hydrogen-containing silicone oil with a hydrogen content of 2.0wt%, organic Mix 3 parts of polysiloxane tackifier, 1 part of white carbon black, and 3 parts of titanium dioxide in a mixer for 60 minutes at high speed (2500 rpm); add 0.5 parts of inhibitor and mix at high speed for 20 minutes (2500 rpm); finally add 0.1 part of the platinum catalyst was mixed at a medium speed for 20 minutes (1000 rpm), and the material was discharged to obtain a one-component strong adhesive addition type silicone rubber encapsulant.

[0035] The one-component strong-adhesive addition-type silicone rubber encapsulant obtained above was made into a sample according to GB / T 7124-2008 (Determination of Tensile...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a monocomponent addition type silicone rubber packaging glue with strong cohesiveness and a preparation method thereof. The packaging glue comprises, by weight, 80-120 parts of vinyl silicone oil, 5-20 parts of vinyl silicone resin, 10-30 parts of hydrogen-containing silicone oil, 1-3 parts of white carbon black, 1-5 parts of titanium dioxide, 0.1-0.5 part of inhibitor and 0.1-0.5 part of platinum catalyst. The preparation method comprises steps of: first mixing vinyl silicone oil, vinyl silicone resin, hydrogen-containing silicone oil, organic polysiloxane adhesion agent, white carbon black and titanium dioxide by high speed stirring; then adding inhibitor and mixing by high speed stirring; finally adding platinum catalyst and mixing by middle speed stirring; and discharging. After sulfuration, the monocomponent addition type silicone rubber packaging glue prepared by the method of the invention has a bonding strength with a base material (copper) higher than 1.86 MPa.

Description

technical field [0001] The invention relates to an addition type silicone rubber encapsulation glue and a preparation method thereof, in particular to a one-component strong adhesive addition type silicone rubber encapsulation glue and a preparation method thereof. Background technique [0002] Addition-type liquid silicone rubber does not produce by-products during the vulcanization process, has a very small shrinkage rate, can be vulcanized deeply, has good high-temperature sealing performance, is convenient for processing and molding, and is easy to realize automatic production; after vulcanization, it is resistant to high and low temperature, ultraviolet rays, and radiation. Insulating and physiologically inert. Therefore, addition-type liquid silicone rubber is often used as a packaging material for electronic components to prevent moisture, dust and harmful gases from affecting electronic components, and to slow down the vibration of components, thereby protecting elec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J183/07C09J183/05C09J11/08C09J11/04C09K3/10
Inventor 凌钦才谢国庆郭文欣
Owner SHANGHAI RES INST OF CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap