Reinforced PA6/ABS(Polyamide 6/Acrylonitrile-Butadiene- Styrene) alloy material and preparation method thereof
An alloy material, PA630 technology, applied in the field of polymer composite modified engineering plastics, can solve the problems of limited ABS application, insufficient cold resistance and high temperature resistance of ABS, and achieve dimensional stability, good fluidity and good wear resistance. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1、2、3
[0027] SMA or ABS-g-MAH is used as compatibilizer, 1076 / 168 (1:1) is used as antioxidant, and ultra-high molecular weight polyethylene wax is used as lubricant.
[0028] Matching ratio 1, 2, 3
[0029] raw material name
Proportion 1 (wt%)
Proportion 2 (wt%)
Proportion 3 (wt%)
[0030] PA6
32
40
37.5
ABS
34
29
37.5
MBS type impact modifier
5
5
8
20
20
10
SMA
--
5
6
ABS-g-MAH
8
--
--
1076 / 168(1∶1)
0.5
0.5
0.4
Ultra High Molecular Weight Polyethylene Wax
0.5
0.5
0.4
[0031] Except for the glass fiber, put the other components into the high mixer according to the proportion and mix them for 8 minutes, then extrude and granulate together with the glass fiber with a twin-screw extruder, the processing temperature is 200-240°C, the sc...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com