Oil-resisting heat-resisting seal piece size and preparation method thereof

A seal and heat-resistant technology, applied in the field of rubber composite material processing, can solve the problems of high price, low production efficiency and long vulcanization time of hydrogenated nitrile rubber and chlorohydrin rubber, and achieve other good comprehensive performance and high production efficiency , The effect of low material cost

Active Publication Date: 2013-11-06
CGP WUHU SEALING
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The usual 41 nitrile rubber formula is inferior to hydrogenated nitrile rubber and chlorohydrin rubber in terms of oil resistance, heat resistance and air tightness, but hydrogenated nitrile rubber and chlorohydrin rubber are expensive, and the vulcanization time is long during processing, and the production efficiency is low and the cost is high. , how to increase the vulcanization speed and improve production efficiency without reducing other comprehensive properties of rubber materials provides a new research direction for rubber production and researchers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Oil-resisting heat-resisting seal piece size and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] 1. Raw material preparation:

[0017] NBR3606 80, NBR2707 80, sulfur 0.8, magnesium oxide 3.5, zinc oxide 8, zinc stearate 1.5, antioxidant RD 3, antioxidant MB 1.5, microcrystalline wax 1.6, rubber processing aid WB212 1.8, carbon black N550100, Carbon black N330 50, dioctyl ester 60, accelerator DM2.4, accelerator TMTD 1.6, accelerator TETD1.6.

[0018] 2. A method for preparing an oil-resistant and heat-resistant seal material, comprising the following steps:

[0019] (1) Masticating: Start the internal mixer, put NBR3606 and NBR2707 into the internal mixer for masticating, after 15-25 minutes of masticating, when the temperature reaches 110-120°C, start discharging, and stop to cool after discharging 23-25 ​​hours;

[0020] (2) Mixing: Add the above-mentioned cooled plasticized rubber into the internal mixer, then add magnesium oxide, zinc oxide, zinc stearate, antioxidants, microcrystalline wax, rubber processing aid WB212, and mix After 3-4 minutes, add carbon ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an oil-resisting heat-resisting seal piece size and a preparation method thereof. The oil-resisting heat-resisting seal piece size comprises the following raw material components in parts by weight: 75-85 of NBR (nitrile-butadiene rubber) 3606, 75-85 of NBR 2707, 0.7-0.9 of sulphur, 3-4 of magnesium oxide, 7-9 of zinc oxide, 1-2 of zinc stearate, 2-4 of antiager RD, 1-2 of antiager MB, 1.5-1.7 of microcrystal wax, 1.7-1.9 of rubber processing agent WB, 95-105 of carbon black N550, 48-52 of carbon black N330, 55-65 of dioctyl ester, 2.3-2.5 of accelerating agent DM, 1.5-1.7 of accelerating agent TMTD (tetramethyl thiuram disulfide) and 1.5-1.7 of accelerating agent TETD (tetraethylthiuram disulfide). The rubber size formula disclosed by the invention is rapid in vulcanizing speed; the obtained size is good in other comprehensive performances; and an oil-resisting seal piece produced by using the size is good in oil resistance and heat resistance and good in gas tightness, and simultaneously, production cost is reduced, and production efficiency is improved.

Description

technical field [0001] The invention relates to the field of processing rubber composite materials, in particular to an oil-resistant and heat-resistant rubber material for sealing parts and a preparation method thereof. Background technique [0002] Oil-resistant seals have special requirements for the formulation of rubber materials, and the products are required to have high oil resistance, high weather resistance, and high air tightness. The usual 41 nitrile rubber formula is inferior to hydrogenated nitrile rubber and chlorohydrin rubber in terms of oil resistance, heat resistance and air tightness, but hydrogenated nitrile rubber and chlorohydrin rubber are expensive, and the vulcanization time is long during processing, and the production efficiency is low and the cost is high. , How to increase the vulcanization speed and improve production efficiency without reducing other comprehensive properties of rubber materials provides a new research direction for rubber prod...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L9/02C08K13/02C08K3/06C08K3/22C08K5/098C08K3/04C08K5/10B29B7/28B29B7/72
Inventor 邵仁杰
Owner CGP WUHU SEALING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com