Natural down flocculus made of composite thermal insulation materials and manufacturing process of the natural down flocculus

A down and natural technology, applied in the field of natural down flakes of composite thermal insulation materials, can solve the problems of unstable price, limited clothing styles, limited quantity, etc., and achieve the effect of large market demand potential, breaking through the price bottleneck, and high cost performance.

Inactive Publication Date: 2012-07-18
河北兴瑞羽绒制品有限公司
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Although down and cashmere on the market can achieve a certain degree of warmth, the quantity is limited, the market price is high and the price is extremely unstable, and the processing technology is still very complicated. After the product is produced, it is too fluffy, which affects the appearance of the product (such as down jacket)
Although cotton and hemp are natural products, their warmth retention coefficient is low. When the weather is very cold, they cannot play a good heat preservation effect.
Although down has the advantages of lightness, softness, and fluffiness, it has always been used as a filler for clothing and bedding to keep warm, and it does not have spinnability, so the style of garments is limited.
Moreover, generally down feathers will have some peculiar smell of feathers, which is inconvenient to wash after being made into finished clothes, and sometimes also reveals an uncomfortable peculiar smell.
[0004] Although artificial synthetic fibers are low in price, they also have a low thermal insulation coefficient and poor thermal insulation effect, and most of them are chemical products, which will cause pollution during the production process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] 1: Open the hot-melt fiber and polyester staple fiber separately through a textile opener, and mix the two according to the weight ratio of 16:10;

[0027] 3: Then mix 90% down with the mixed fiber, the mixing ratio depends on the required content of the finished down product, after mixing, it is mixed evenly by a mixer and impurities such as fine feather rods are removed again, and it is called down mixed fiber;

[0028] 4: Flatten the above-mentioned down mixed fiber at the entrance of the light flower machine and control its entering quantity to 60 kg / hour, and then sew it into a block with duck down thread;

[0029] 5: Then remove impurities from the sewn down blended fiber by carding machine (mainly to remove the small feather rods remaining in the down) and control its thickness between 0.3 mm and 0.5 mm;

[0030] 6: Laying the feather silk mixed fiber layer by layer through the net-laying machine, the number of overlapping laying depends on the thickness requirem...

Embodiment 2

[0033] 1: Open the hot-melt fiber and polyester staple fiber separately through the textile opener, and mix the two according to the weight ratio of 17:12;

[0034] 3: Then mix 90% down with the mixed fiber, the mixing ratio depends on the required content of the finished down. After mixing, mix it evenly with a mixer and remove impurities such as fine feather rods again. It is called down mixed fiber;

[0035] 4: Spread the above-mentioned down mixed fiber at the entrance of the light flower machine and control its entering quantity to 70 kg / hour, and then sew it into a block with duck down thread;

[0036] 5: Then remove impurities from the sewn down blended fiber by carding machine (mainly to remove the small feather rods remaining in the down) and control its thickness between 0.3 mm and 0.5 mm;

[0037] 6: Laying the down mixed fiber layer by layer through the web-laying machine, and the number of overlapping layers depends on the thickness requirements of the finished pr...

Embodiment 3

[0040] 1: Open the hot-melt fiber and polyester staple fiber separately through the textile opener, and mix the two according to the weight ratio of 15:7;

[0041] 3: Then mix the 90% down with the mixed fiber, the mixing ratio depends on the required content of the finished down, after mixing, mix it evenly with a mixer and remove impurities such as fine feather rods again, and call it down mixed fiber;

[0042] 4: Flatten the above-mentioned down mixed fiber at the entrance of the light flower machine and control its entering quantity to 80 kg / hour, and then sew it into a block with duck down thread;

[0043] 5: Then remove impurities from the sewn down blended fiber by carding machine (mainly to remove the small feather rods remaining in the down) and control its thickness between 0.3 mm and 0.5 mm;

[0044] 6: Laying the down mixed fiber layer by layer through the web-laying machine, and the number of overlapping layers depends on the thickness requirements of the finished...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Melting pointaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a natural down flocculus made of composite thermal insulation materials, which is made through taking down mainly comprising duck down and goose down as a main material, as well as a manufacturing process of the natural down flocculus. The natural down flocculus made of the composite thermal insulation materials is made of blend fiber and down mainly comprising duck down and goose down, wherein the blend fiber is formed by blending meldable fibers and polyester staple fibers according to weight ratio of (13-18):(6-15); and the blended ratio of the down and the blend fiber is determined according to the requirement of a down product. In manufacturing, animal down serves as a main material while the meldable fibers and the polyester staple fibers serve as auxiliary materials; and the composite thermal insulation material with the down content of above 65% is produced according to different ratios of all materials. The down flocculus has a good thermal insulation property like a down product or a cashmere product, is green and environment-friendly, and also has spinnability and tailorability. The process is relatively low in cost, concise and mature in process and easy to operate, and has a great market potential.

Description

technical field [0001] The invention relates to a natural down wadding flake of a composite heat-preserving material made of down mainly including duck down and goose down as main materials and a manufacturing process thereof. Background technique [0002] At present, thermal insulation materials can be divided into two types, natural fibers and artificial chemical fibers (commonly known as chemical fibers). Natural thermal insulation materials are mainly animal hair such as down, cashmere, camel hair, silk, etc., and plant fibers such as cotton and hemp. Artificial compounds are mainly based on oil and other extracts, such as silk cotton. [0003] Although down and cashmere on the market can achieve a certain warmth retention factor, the quantity is limited, the market price is high and extremely unstable, and the processing technology is still very complicated. After the product is produced, it is too fluffy, which affects the appearance of the product (such as down jacke...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D04H1/02D04H1/42D04H1/4266D04H1/435D04H1/4382D04H1/542D04H1/556
Inventor 张会锁司仁杰李亚军
Owner 河北兴瑞羽绒制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com