Natural environment-friendly plant gloss oil

A natural environmental protection, natural plant technology, applied in the direction of coating, can solve environmental hazards and other problems, achieve the effect of high environmental protection index, high transparency of varnish, plump and smooth paint film

Active Publication Date: 2014-04-02
千浪化研新材料(上海)有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The existing environmentally friendly paints do not completely contain any chemical synthetic substances, but try to minimize the chemical substances, which is still harmful to the environment. Therefore, providing a natural plant environmental protection varnish has become our main Task

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Natural environment-friendly plant gloss oil
  • Natural environment-friendly plant gloss oil
  • Natural environment-friendly plant gloss oil

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The component weight ratio of natural environment-friendly vegetable varnish is shown in Table 1. In the case of the weight component ratio in Table 1, the adhesion and hardness of natural environment-friendly vegetable varnish were tested.

[0022] Table 1

[0023]

[0024] Under the weight ratio of the natural environment-friendly vegetable varnish components in Table 1, the results of testing adhesion and hardness are shown in Table 2.

[0025] Table 2

[0026]

[0027] As shown in table 1 and table 2, the weight ratio of natural plant secretion oil is 40.5%, the weight ratio of ethoxylated pentamylol oligomer is 17.5%, and the weight ratio of dioxymethyl separating agent is 4.0%, When the weight ratio of the polyester moisture desiccant was 5.8%, the experimental results showed that the surface of the paint film was slightly depainted, and the hardness was H.

Embodiment 2

[0029] The component weight ratio of natural environment-friendly vegetable varnish is shown in Table 3. In the case of the weight component ratio of Table 3, the adhesion and hardness of natural environment-friendly vegetable varnish are tested.

[0030] table 3

[0031]

[0032] Under the weight ratio of the natural environment-friendly vegetable varnish in Table 3, the results of testing the adhesion and hardness of the natural environment-friendly vegetable varnish are shown in Table 4;

[0033] Table 4

[0034]

[0035]

[0036] As shown in table 3 and table 4, the weight ratio of natural plant secretion oil is 47.3%, the weight ratio of ethoxylated pentamylol oligomer is 9.6%, and the weight ratio of dioxymethyl separating agent is 4.6%, When the weight ratio of the polyester water desiccant was 6.3%, the experimental results showed that there was no paint stripping on the surface of the paint film, and the hardness of the paint film was 2H.

Embodiment 3

[0038] The component weight ratio of natural environment-friendly vegetable varnish is shown in Table 5. In the case of the weight component ratio in Table 5, the adhesion and hardness of natural environment-friendly vegetable varnish are tested.

[0039] table 5

[0040]

[0041]

[0042] Under the weight ratio of the natural environment-friendly vegetable varnish in Table 5, the results of testing the adhesion and hardness of the natural environment-friendly vegetable varnish are shown in Table 6;

[0043] Table 6

[0044]

[0045]

[0046] As shown in table 5 and table 6, the weight ratio of natural plant secretion oil is 51.3%, the weight ratio of ethoxylated pentamylol oligomer is 5.6%, and the weight ratio of dioxymethyl separating agent is 5.2%, When the weight ratio of the polyester moisture desiccant is 6.8%, the experimental results show that the surface of the paint film has a slight paint peeling and a hardness of H.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of gloss paint, and in particular relates to natural environment-friendly plant gloss oil. The natural environment-friendly plant gloss oil is characterized by comprising the following components by weight percent: 42-50% of natural plant secreted oil, 10-12% of bisphenol A acrylate methacrylate, 5.5-16% of ethoxylated pentahydroxy methyl oligomer, 6-8% of pentaerythritol hexapropionate, 5-6.5% of ethoxylated hydroxymethyl dimethylmethane, 7-9% of pentahydroxymethyl propane dimethyl ester, 3.5-5.5 % of dioxymethyl separating agent, 5.5-7% of polyester moisture drying agent and 0.5%-1.5% of flatting agent. The natural environment-friendly plant gloss paint provided by the invention has high environment-friendly index number, is plump and soft and has good hand feeling; the gloss oil has high transparency, and natural color of wood can be restored; the gloss oil is hard and wear-resistant, and has good scratch resistance; the gloss oil is clean-smelling, healthy, environment-friendly, good in scratch resistance and wear resistance and strong in adhesive force; and the gloss oil has good hardness, is free of after-tack and resists sea water.

Description

technical field [0001] The invention relates to the technical field of varnish, in particular to a natural environment-friendly vegetable varnish. Background technique [0002] Varnish is a kind of synthetic resin, which usually refers to the surface transparent varnish, which is made of base material and additives, without adding any pigments. After the film is formed, it is shiny and shiny. It is commonly called varnish. There are UV varnish and PU varnish. points. [0003] With the progress of human society and the development of science and technology, people have obtained a large amount of material resources and energy for production and consumption, which has improved human life, but at the same time, synthetic chemistry has brought changes to human beings. This change, in turn, has caused extreme changes in living space due to urban concentration, and increased exposure to synthetic chemicals in daily life with the densification of living space. The reduction of nat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D4/02C09D4/06
Inventor 谢梦静
Owner 千浪化研新材料(上海)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More