Forsterite fireproof castable

A refractory castable and forsterite technology, applied in the field of refractory materials, can solve the problems of single development and application, fine powder entering the river, and low added value of products, so as to reduce resource waste, good resistance to slag erosion, and good thermal shock resistance The effect of the high temperature performance of the

Inactive Publication Date: 2012-08-01
宜兴新威利成耐火材料有限公司 +1
View PDF2 Cites 34 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

my country is rich in forsterite resources, but its development and application is relatively simple. The amount of forsterite in the steel and foundry industries accounts for more than 90%, but the particle size requirements are strict, and only coarse and medium particle sizes are required, making small particle size and fine powder resources All backlogs; in production, due to the fragility of forsterit

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Forsterite fireproof castable

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0024] Example 1

[0025] Take 11.88 kg of forsterite with a particle size of 5-3mm, 19.8 kg of forsterite with a particle size of 3-1 mm, 15.84 kg of forsterite with a particle size of 1-0 mm, and 18.48 kg of forsterite with a particle size of 0.088 mm. 12 kg of magnesium oxide, 10 kg of fine forsterite powder, 5 kg of silica micropowder binder, 6.8 kg of zircon sand powder, and 0.2 kg of sodium hexametaphosphate, mixed uniformly into 100 kg of refractory castable bulk material. The refractory castable bulk material is added with appropriate amount of water and stirred evenly, and then poured into a 40×40×160mm triple mold. After natural curing for 24 hours, it will be demolded, and then dried at 110°C for 24 hours, and finally at 1400°C-1500 Incubate at ℃ for 2 to 3 hours to prepare samples. After the sample is cooled, its performance is tested, and the results are shown in the attached table.

Example Embodiment

[0026] Example 2

[0027] Put 12.73 kg of forsterite with a particle size of 5-3 mm, 19.43 kg of forsterite with a particle size of 3-1 mm, 15.41 kg of forsterite with a particle size of 1-0 mm, and 19.43 kg of forsterite with a particle size of 0.088 mm. 11 kg of magnesium oxide, 9.8 kg of fine forsterite powder, 6 kg of silica micropowder binder, 6 kg of silicon carbide, and 0.2 kg of sodium hexametaphosphate are mixed uniformly into 100 kg of refractory castable bulk materials. The refractory castable bulk material is added with appropriate amount of water and stirred evenly, and then poured into a 40×40×160mm triple mold. After natural curing for 24 hours, it will be demolded, and then dried at 110°C for 24 hours, and finally at 1400°C-1500 Incubate at ℃ for 2 to 3 hours to prepare samples. After the sample is cooled, its performance is tested, and the results are shown in the attached table.

Example Embodiment

[0028] Example 3

[0029] Put 13.6 kg of forsterite with a particle size of 5-3mm, 19.04 kg of forsterite with a particle size of 3-1 mm, 14.96 kg of forsterite with a particle size of 1-0 mm, and 20.4 kg of forsterite with a particle size of ≦0.088 mm. 11 kg of magnesium oxide, 8 kg of fine forsterite powder, 6 kg of silica micropowder binder, 6.8 kg of zircon sand powder, and 0.2 kg of sodium tripolyphosphate, mixed uniformly into 100 kg of refractory castable bulk material. The refractory castable bulk material is added with appropriate amount of water and stirred evenly, and then cast in a 40×40×160mm triple mold. After natural curing for 24 hours, the mold will be demolded, then dried at 110°C for 24 hours, and finally at 1400°C-1500 Incubate at ℃ for 2 to 3 hours to prepare samples. After the sample is cooled, its performance is tested, and the results are shown in the attached table.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a forsterite fireproof castable which is characterized by comprising the following components in percentage by weight: 65 to 70 percent of forsterite granular aggregate, 10 to 12 percent of undercalcined magnesia, 8 to 10 percent of forsterite fine powder, 4 to 6 percent of silica micro powder combination agent, 5 to 7 percent of additive and 0.1 to 0.3 percent of water reducing agent. The small-granularity forsterite and forsterite fine powder are used as raw materials of the fireproof castable; the forsterite resources are used fully, so that resource waste is reduced, and environment pollution is reduced; furthermore, the cost of the fireproof castable is reduced, the preparation working procedure is simple, and the fireproof castable is convenient to construct; moreover, the fireproof castable has the advantages of relatively high usability, high slag erosion resistance and thermal shock resistance high-temperature performance, and can be widely applied to smelting industries.

Description

technical field [0001] The invention relates to a refractory material, in particular to a forsterite refractory castable, which fully utilizes forsterite resources and reduces waste of resources. Background technique [0002] As a kind of unshaped refractory material, refractory castables do not need to be formed, dried and fired before use, which is beneficial to energy saving and emission reduction, and the production process is simple, easy to construct, and the integrity and airtightness of the furnace lining are good, which can be mechanized construction. Easy to repair and other advantages. At present, high-alumina bauxite resources, which are widely used as refractory materials, are becoming increasingly scarce, and it is imminent to research, develop and utilize alkaline refractory materials to replace aluminum-silicon refractory materials. Forsterite is an alkaline refractory material. Due to its good properties, it is widely used in foundry sand, metallurgical aux...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/66
Inventor 钱元英袁雪峰周彦文
Owner 宜兴新威利成耐火材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap