Mixed latex with antianaphylaxis

A latex, anti-allergic technology, applied in the field of mixed latex, can solve the problems of poor anti-aging performance, poor flexural resistance, poor elasticity, etc., to enhance chemical resistance and elasticity, improve anti-aging performance, and expand the scope of use Effect

Inactive Publication Date: 2012-08-22
蔡瑞琳 +2
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The production of traditional latex gloves has a history of nearly 40 years. Due to the ubiquity of water-soluble proteins in natural latex that cause allergic reactions in the human body, many people cannot use latex gloves because of allergies, which limits the use of latex gloves. People's life causes many inconveniences; In addition, existing latex gloves mostly adopt pure natural latex to make, adopt the latex gloves that pure natural latex is made to have poor aging resistance, poor flex resistance, and its elasticity is also relatively poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] There is the mixed latex liquid of antiallergic property, comprises the following components of each parts by weight:

[0033] Weight percent concentration is 65 parts by weight of natural latex of 60%

[0034] 3 parts by weight of nitrile latex

[0035] Deionized water 5 parts by weight

[0036] Carboxymethylcellulose 5 parts by weight

[0037] Sulfur 0.5 parts by weight

[0038] 0.5 parts by weight of ZDC accelerator

[0039] TMO auxiliary agent 0.5 parts by weight

[0040] Antiaging agent D 0.5 parts by weight

[0041] Zinc oxide 0.2 parts by weight

[0042] Potassium hydroxide 0.2 parts by weight

[0043] Casein 0.2 parts by weight

[0044] 0.2 parts by weight of lanolin

[0045] 0.1 parts by weight of red color paste.

[0046] The preparation method of the mixed latex liquid is as follows: in the state of stirring, natural latex and nitrile latex with a concentration of 60% by weight are added in the reactor, after stirring for 0.5 hours, slowly add deion...

Embodiment 2

[0048] There is the mixed latex liquid of antiallergic property, comprises the following components of each parts by weight:

[0049] Weight percent concentration is 115 parts by weight of natural latex of 60%

[0050] 15 parts by weight of nitrile latex

[0051] 30 parts by weight of deionized water

[0052] 40 parts by weight of carboxymethyl cellulose

[0053] Sulfur 5 parts by weight

[0054] 5 parts by weight of ZDC accelerator

[0055] 5 parts by weight of TMO additive

[0056] Antiaging agent D 5 parts by weight

[0057] Zinc oxide 3 parts by weight

[0058] Potassium hydroxide 3 parts by weight

[0059] Casein 3 parts by weight

[0060] Lanolin 3 parts by weight

[0061] 0.5 parts by weight of yellow color paste.

[0062]The preparation method of the mixed latex liquid is as follows: in the state of stirring, natural latex and nitrile latex with a concentration of 60% by weight are added in the reactor, after stirring for 2 hours, slowly add deionized water, ...

Embodiment 3

[0064] There is the mixed latex liquid of antiallergic property, comprises the following components of each parts by weight:

[0065] Weight percent concentration is 85 parts by weight of natural latex of 60%

[0066] Nitrile latex 9 parts by weight

[0067] 18 parts by weight of deionized water

[0068] 24 parts by weight of hydroxyethyl cellulose

[0069] Sulfur 2.8 parts by weight

[0070] 2.8 parts by weight of ZDC accelerator

[0071] 2.8 parts by weight of TMO additive

[0072] Antiaging agent D 2.8 parts by weight

[0073] Zinc oxide 1.6 parts by weight

[0074] 1.6 parts by weight of potassium hydroxide

[0075] Casein 1.6 parts by weight

[0076] 1.6 parts by weight of lanolin

[0077] 0.3 parts by weight of blue color paste.

[0078] The preparation method of the mixed latex liquid is as follows: in the state of stirring, natural latex and nitrile latex with a concentration of 60% by weight are added in the reactor, after stirring for 1.2 hours, slowly add ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses mixed latex with antianaphylaxis, which comprises the following components: natural latex of which the percentage concentration by weight is 60 percent, acrylonitrile butadiene rubber latex, deionized water, a thickening agent, sulphur, a zinc diethyl dithiocarbamate (ZDC) accelerating agent, a trimethadione (TMO) assistant, an anti-aging agent D, zinc oxide, potassium hydroxide, casein and wool grease. In the mixed latex disclosed by the invention, the natural latex is low in content, and the content of protein in latex gloves is reduced, therefore, the latex gloves made of the mixed latex have certain antianaphylaxis, so that the application range of the latex gloves is broadened, and the lives of people are facilitated. As an additive, such as the acrylonitrile butadiene rubber latex, is added to the natural latex of the mixed latex disclosed by the invention, and the latex gloves are made of the mixed latex, the ageing resistance and the flexing resistance of the latex gloves are greatly improved, and the chemical resistance and the elasticity are enhanced. Compared with simple natural latex, the mixed latex with the antianaphylaxis is higher in softness and stronger in grease resistance.

Description

technical field [0001] The present invention relates to mixed emulsions with antiallergic properties. Background technique [0002] The production of traditional latex gloves has a history of nearly 40 years. Due to the ubiquity of water-soluble proteins in natural latex that cause allergic reactions in the human body, many people cannot use latex gloves because of allergies, which limits the use of latex gloves. People's life causes many inconveniences; In addition, existing latex gloves mostly adopt pure natural latex to make, adopt the latex gloves that pure natural latex is made to have poor aging resistance, poor flex resistance, and its elasticity is also poor. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a mixed latex with anti-allergic performance. The latex gloves made of the mixed latex are not easy to cause skin allergies, and have good anti-aging performance and good flexibility resistance. [000...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L7/02C08L9/04C08K13/02C08K3/06C08K3/22
Inventor 蔡瑞琳蔡晓薇刘新春
Owner 蔡瑞琳
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com