Ethylene perchloride floor coating

A technology of floor coating and perchloroethylene, applied in the direction of coating, can solve the problems of easy mildew, poor corrosion resistance, easy brittleness and dry cracking, etc., and achieve the effect of good water resistance

Inactive Publication Date: 2012-09-19
HAIAN GUOLI CHEM
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the perchlorethylene floor coatings on the market have poor water resistance, poor corrosion resistance, poor wear resistance and easy to mold, and they are easy to become brittle and cracked in cold conditions, so they are very convenient to use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] A kind of perchlorethylene floor coating, comprising the following raw materials in mass parts: 90 parts of perchlorethylene resin, 3 parts of dibutyl phthalate, 3 parts of ethyl acetate, 0.3 part of titanium dioxide, 1 part of antimony oxide, two 680 parts of toluene solvent, 8 parts of talc powder, and 1 part of carbon black.

Embodiment 2

[0010] A kind of perchlorethylene ground coating, comprises the raw material of following mass parts: 100 parts of perchlorethylene resin, 5 parts of dibutyl phthalate, 5 parts of ethyl acetate, 0.5 part of titanium dioxide, 2 parts of antimony oxide, two parts 700 parts of toluene solvent, 10 parts of talc powder, and 2 parts of carbon black.

Embodiment 3

[0012] A kind of perchlorethylene ground paint, comprises the raw material of following mass parts: perchlorethylene resin 95 parts, dibutyl phthalate 4 parts, ethyl acetate 4 parts, titanium dioxide 0.4 part, antimony oxide 1.5 part, two 690 parts of toluene solvent, 9 parts of talcum powder, and 1.5 parts of carbon black.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an ethylene perchloride floor coating which comprises the raw materials based on parts by weight: 90-100 parts of ethylene perchloride resin, 3-5 parts of dibutyl phthalate, 3-5 parts of acetic ether, 0.3-0.5 part of titanium dioxide, 1-2 parts of antimony oxide, 680-700 parts of dimethylbenzene solvent, 8-10 parts of talcum powder and 1-2 parts of carbon black. The ethylene perchloride floor coating has better water resistance, corrosion resistance, atmospheric resistance stability, wear resistance, antibacterial property and cold resistance, and is not easily crisped and cracked, thus being used for spraying or painting the floor in the environment of below 60 DEG C.

Description

technical field [0001] The invention relates to a paint, in particular to a perchlorethylene floor paint with excellent performances such as corrosion resistance and cold resistance. Background technique [0002] At present, the perchlorethylene floor coatings on the market have poor water resistance, poor corrosion resistance, poor wear resistance, and easy to mold, and are prone to brittleness and cracking in cold conditions, and are extremely convenient to use. Contents of the invention [0003] Purpose of the invention: In order to solve the deficiencies in the prior art, the present invention provides a perchlorethylene floor coating with excellent performances such as corrosion resistance and cold resistance. [0004] Technical solution: A perchlorethylene floor coating according to the present invention includes the following raw materials in parts by mass: 90-100 parts of perchlorethylene resin, 3-5 parts of dibutyl phthalate, 3-5 parts of ethyl acetate 5 part...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D127/24C09D7/12
Inventor 王国才
Owner HAIAN GUOLI CHEM