A polyester fiber, composite technology, applied in the field of fiber silk, can solve the problems of inability to achieve nano-scale tea fiber particles, inability to absorb and antibacterial properties, easy to dye, etc., to increase additional effects, improve fiber-related functionality, and sustainable. long-lasting effect

Active Publication Date: 2014-04-09
FUJIAN JINJIANG HUAYU WEAVING
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] The purpose of the present invention is to overcome the inadequacy of nano-scale tea fiber particles, activated carbon particles and polyester synthetic fibers in the prior art, and innovate to overcome the strength, moisture absorption, breathability, easy-to-dye, adsorption and antibacterial properties of the synthesized fibers Technical problems of fibers whose properties cannot coexist

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A continuous high-strength core-skin composite tea-charcoal polyester fiber. The raw materials of the continuous high-strength core-skin composite tea-charcoal polyester fiber are nano-scale natural tea fibrils, nano-scale activated carbon particles, and hygroscopic and easy-to-dye ECDP polyester.

Embodiment 2

[0031] A continuous high-strength core-skin composite tea charcoal polyester fiber, the raw materials of the continuous high-strength core-skin composite tea charcoal polyester fiber are nano-scale natural tea fibrils, nano-scale activated carbon particles and hygroscopic and easy-to-dye ECDP polyester; the nano-scale The diameter of the cross-section of the natural tea fibrils ranges from 11 to 14nm, and the particle diameter of the nanoscale activated carbon particles ranges from 12 to 15nm; the nanoscale natural tea fibrils and the nanoscale activated carbon particles respectively occupy 3-4.5% and 6-7.5% of the total weight of the core layer of the fiber; nano-scale natural tea fibrils and nano-scale activated carbon particles respectively account for 6-7.5% and 3-4.5%; the continuous high-strength core-skin composite tea-charcoal polyester fiber is prepared through the following processing steps in sequence;

[0032] 1) Preparation of the core layer: put nano-scale natura...

Embodiment 3

[0036] A continuous high-strength core-skin composite tea charcoal polyester fiber, the raw materials of the continuous high-strength core-skin composite tea charcoal polyester fiber are nano-scale natural tea fibrils, nano-scale activated carbon particles and hygroscopic and easy-to-dye ECDP polyester; the nano-scale The diameter of the cross-section of the natural tea fibrils ranges from 11 to 14nm, and the particle diameter of the nanoscale activated carbon particles ranges from 12 to 15nm; the nanoscale natural tea fibrils and the nanoscale activated carbon particles respectively occupy 3-4.5% and 6-7.5% of the total weight of the core layer of the fiber; nano-scale natural tea fibrils and nano-scale activated carbon particles respectively account for 6-7.5% and 3-4.5%; the continuous high-strength core-skin composite tea-charcoal polyester fiber is prepared through the following processing steps in sequence;

[0037] 1) Preparation of the core layer: put nano-scale natura...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a composite tea carbon polyster fiber of a continuous high-strength core sheath, which solves the technical problem that the properties of strength, hygroscopicity, air permeability, chromatophilia, adsorbability, antibacterial property and the like of synthetic fiber cannot commonly exist in the prior art by utilizing the nanoscale natural tea fibrils, nanoscale activated carbon particles and hygroscopic chromophilous ECDP (easy cationic dyeable polyester) through a compound structure of the core sheath and a series of unique designs of processes such as filtering, fusing, extruding and the like. The properties of strength, hygroscopicity, air permeability, chromatophilia, adsorbability, antibacterial property, comfortableness and the like of the fiber are several times over those of the same fiber. The composite tea carbon polyster fiber has no harm to comfort property of decorative fiber, the environment and the human body; subsequent dyeing of the fiber is also omitted, and the beneficial advantages of strength, hygroscopicity, air permeability and after-treatment of stronger adsorption are intensified.

Description

technical field [0001] The invention relates to the technical field of fiber filaments, in particular to a tea-charcoal polyester fiber, in particular to a continuous high-strength core-skin composite tea-charcoal polyester fiber. Background technique [0002] Tea charcoal has the reputation of "black diamond" and is rich in trace elements that are beneficial to the body. Tea charcoal is a kind of porous material with micropores, mesopores and small pores, which is made of recycled tea leaves and tea dregs as raw materials. It has a large specific surface area and super adsorption performance. Odor, odor absorption and other special effects. Tea charcoal has the special functions of dehumidification and adjusting the ambient temperature, which can make the absorbed water weakly alkaline, and has the effects of bleaching and beautifying the skin. In addition, due to its special molecular structure and super adsorption function, tea charcoal has weak conductivity, which pla...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F8/14D01F1/10D01D5/34D01D1/04
Inventor 柯文新王朝生曾志明
Owner FUJIAN JINJIANG HUAYU WEAVING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap