Vegetable oil-based adhesive, composite plywood and method for manufacturing composite plywood

A vegetable oil-based, adhesive technology, applied in the direction of adhesives, oil/fat/wax adhesives, non-polymer organic compound adhesives, etc., can solve the problems that resin cannot be melted and processed, and recycling is difficult, so as to achieve a good social economy Effect, saving economic cost, good water resistance

Active Publication Date: 2012-10-17
CHENGDU SCI & TECH DEV CENT CHINA ACAD OF ENG PHYSICS
View PDF6 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, plastic materials that can be melt-processed can be made into other products, and their recycling is relatively easy; while thermosetting resins

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Vegetable oil-based adhesive, composite plywood and method for manufacturing composite plywood
  • Vegetable oil-based adhesive, composite plywood and method for manufacturing composite plywood
  • Vegetable oil-based adhesive, composite plywood and method for manufacturing composite plywood

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] For the vegetable oil-based adhesive of this embodiment, the raw materials of the adhesive include the following components by weight: 100 parts of vegetable oil-based resin, 250 parts of active resin, 150 parts of curing agent, 10 parts of catalyst, and 200 parts of additives.

[0028] The method of utilizing the vegetable oil-based adhesive of the present embodiment to manufacture a composite wood-based panel comprises the following steps:

[0029] a. crushing 3000 parts by weight of petrochemical resin into particles with a particle diameter of 1 mm, and uniformly mixing with 3000 parts by weight of fibers to obtain fillers;

[0030] b. uniformly mixing the vegetable oil-based resin, the active resin, the curing agent, the catalyst and the additive according to the set weight parts to prepare the adhesive glue;

[0031] c. Spray the adhesive glue that accounts for 30% of the total amount of filler in step a on the filler in step b, and mix evenly to obtain a wood-bas...

Embodiment 2

[0042] For the vegetable oil-based adhesive of this embodiment, the adhesive raw materials include the following components by weight: 120 parts of vegetable oil-based resin, 500 parts of active resin, 300 parts of curing agent, 50 parts of catalyst, and 400 parts of additives.

[0043] The method of utilizing the vegetable oil-based adhesive of the present embodiment to manufacture a composite wood-based panel comprises the following steps:

[0044] a. crushing 6000 parts by weight of petrochemical resin into particles with a particle diameter of 10 mm, and uniformly mixing with 6000 parts by weight of fibers to obtain fillers;

[0045] b. uniformly mixing the vegetable oil-based resin, the active resin, the curing agent, the catalyst and the additive according to the set weight parts to prepare the adhesive glue;

[0046] c. Spray the adhesive glue that accounts for 60% of the total amount of filler in step a on the filler in step b, and mix evenly to obtain a wood-based pan...

Embodiment 3

[0058] For the vegetable oil-based adhesive of this embodiment, the raw materials of the adhesive include the following components by weight: 80 parts of vegetable oil-based resin, 200 parts of curing agent, 10 parts of catalyst, and 200 parts of additives.

[0059] The method of utilizing the vegetable oil-based adhesive of the present embodiment to manufacture a composite wood-based panel comprises the following steps:

[0060] a. crushing 20 parts by weight of petrochemical resin into particles with a particle diameter of 0.01 mm, and uniformly mixing with 3000 parts by weight of fibers to obtain a filler;

[0061] b. uniformly mixing the vegetable oil-based resin, curing agent, catalyst and additives according to the set weight parts to prepare the adhesive glue;

[0062] c. Spray the adhesive liquid that accounts for 2% of the total amount of filler in step a on the filler in step b, and mix evenly to obtain a wood-based panel composite;

[0063] d. Lay the wood-based pa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a vegetable oil-based adhesive, a composite plywood and a method for manufacturing the composite plywood from the vegetable oil-based adhesive. The vegetable oil-based adhesive comprises a vegetable oil-based resin, a reactive resin, a curing agent, a catalyst and additives and does not contain the formaldehyde. The composite plywood manufactured from the vegetable oil-based adhesive has high strength and good water resistance, does not contain benzene, toluene, xylene and other harmful substances and can not cause pollution to the environment. The waste petrochemical resin can be recycled, the resources can be saved, the economic cost can be saved, the use amount of the environmentally-friendly renewable materials can be increased, and the harm of the traditional composite plywood comprising the formaldehyde glue to the environment can be avoided. The composite plywood can be used as the furniture board and the floor and can be used for architectural decoration and internal decoration of motor vehicles.

Description

technical field [0001] The invention relates to an adhesive, a manufacturing method of an artificial board and an artificial board, in particular to a vegetable oil-based adhesive, a method for manufacturing an artificial board by using the vegetable oil-based adhesive and a composite artificial board. Background technique [0002] Traditional wood-based panels are mainly made of wood or other non-wood plants bonded by adhesives, and then molded in a certain way, which has a wide range of uses in architectural decoration, furniture, flooring and other fields. At present, the adhesives used in the wood-based panel industry are mostly urea-formaldehyde resin, phenolic resin, and melamine-formaldehyde resin. These three types of glue use formaldehyde as a raw material, and a large amount of formaldehyde will be released during the processing and later utilization of wood-based panels, which seriously endanger people's health. At present, countries around the world have also pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J163/02C09J191/00C09J163/00C09J201/02C09J175/04C09J4/00C09J4/02C09J167/06B27N3/08
Inventor 唐昶宇任伍杨郭伟民刘焕明
Owner CHENGDU SCI & TECH DEV CENT CHINA ACAD OF ENG PHYSICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap