Hot-rolled pickled plate with excellent formability for automobile structure and production method thereof

A hot-rolled pickling, automobile structure technology, applied in metal rolling, metal rolling, rolling mill control device and other directions, to achieve the effect of simple method, good surface quality and good welding performance

Inactive Publication Date: 2012-10-17
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP +3
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Steel grades in the prior art cannot meet this requirement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] In terms of weight percentage, the chemical composition of billet is: C: 0.05%, Si: 0.05%, Mn: 0.15%, Cr: 0.20%, Ti: 0.010%, P: 0.011%, S: 0.010%, Als: 0.022% , and the rest are Fe and unavoidable impurities.

[0031] Its production process is: steel billet → hot rolling → laminar flow cooling → coiling → welding head and tail → pickling → smoothing → oiling → finished product. After the steel billet is heated at 1220°C, it is roughly rolled into a 35mm thick intermediate billet by two reversible rough rolling mills for 6 passes, and the rough rolling reduction rate is 82.5%. 1.8mm thick steel coil, the finishing rolling reduction rate is 94.9%, and the finishing rolling temperature is 850°C. After the steel coil is cooled by laminar flow, it enters the coiler to obtain the strip steel. The cooling rate is 19.5°C / s, and the temperature in the coiling step is 702°C. After the strip is welded head to tail, it is pickled, and the pickling flat elongation rate is 1.0%. F...

Embodiment 2

[0034] In terms of weight percentage, the chemical composition of billet is: C: 0.07%, Si: 0.04%, Mn: 0.25%, Cr: 0.25%, Ti: 0.015%, P: 0.010%, S: 0.008%, Als: 0.028% , and the rest are Fe and unavoidable impurities.

[0035] Its production process is: steel billet → hot rolling → laminar flow cooling → coiling → welding head and tail → pickling → smoothing → oiling → finished product. After the steel billet is heated at 1230°C, it is roughly rolled into a 38mm thick intermediate billet by two reversible rough rolling mills for 6 passes, and the rough rolling reduction rate is 81%. For a 2.5mm thick steel coil, the final rolling reduction rate is 93.4%, and the final rolling temperature is 870°C. After the steel coil is cooled by laminar flow, it enters the coiler to obtain the strip steel. The cooling rate is 18.4°C / s, and the temperature in the coiling step is 715°C. After the strip is welded head to tail, it is pickled, and the pickling flat elongation is 1.4%. Finally, i...

Embodiment 3

[0038] In terms of weight percentage, the chemical composition of billet is: C: 0.08%, Si: 0.03%, Mn: 0.32%, Cr: 0.32%, Ti: 0.02%, P: 0.015%, S: 0.007%, Als: 0.042% , and the rest are Fe and unavoidable impurities.

[0039] Its production process is: steel billet → hot rolling → laminar flow cooling → coiling → welding head and tail → pickling → smoothing → oiling → finished product. After the steel billet is heated at 1250°C, it is roughly rolled into a 37mm thick intermediate billet by two reversible rough rolling mills for 6 passes, and the rough rolling reduction rate is 81.5%. For a 4.0mm thick steel coil, the final rolling reduction rate is 89.2%, and the final rolling temperature is 880°C. After the steel coil is cooled by laminar flow, it enters the coiler to obtain the strip steel. The cooling rate is 17.7°C / s, and the temperature in the coiling step is 740°C. After the strip is welded head to tail, it is pickled, and the pickling flat elongation rate is 1.8%. Fina...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a hot-rolled pickled plate with excellent formability for an automobile structure. The plate comprises, in terms of weight percent, 0.05 to 0.10% of C, no more than 0.05% of Si, 0.15 to 0.50% of Mn, 0.20 to 0.40% of Cr, 0.01 to 0.02% of Ti, no more than 0.02% of P, no more than 0.010% of S and 0.02 to 0.07% of Als, with the balance being Fe and unavoidable impurities. According to a production method for the hot-rolled pickled plate provided in the invention, the hot-rolled pickled plate with excellent formability for an automobile structure is produced by controlling the parameters of chemical components in steel, a hot rolling process, a pickling process and the like. The hot-rolled pickled plate in the invention has excellent comprehensive properties like high strength, good welding performance and good surface quality; and the production method in the invention has the advantages of small process control difficulty, strong operationality, simpleness, low cost and the like.

Description

technical field [0001] The invention relates to a hot-rolled pickled sheet and a production method thereof, more specifically, to a hot-rolled pickled sheet for automotive structures with excellent formability and a production method thereof. Background technique [0002] The hot-rolled pickled plate is made of high-quality hot-rolled thin plate, which is made by removing the oxide layer, trimming and finishing by the pickling unit. The main processing procedures of the hot-rolled pickled plate include laser welding, turbulent pickling, On-line leveling, edge trimming, on-line oiling, etc., whose surface quality and use requirements are between hot-rolled and cold-rolled sheets, it is an ideal substitute for some hot-rolled and cold-rolled sheets. [0003] The advantages of hot-rolled pickled plate are: 1) Good surface quality, because the hot-rolled pickled plate removes the surface oxide scale, improves the surface quality of steel, and is convenient for welding, oiling an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/28B21B37/00C23G1/08C23G3/02
Inventor 李正荣李军向安平李卫平翁建军张列任守斌
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com