Preparation method and application for pineapple fiber yarns

A technology of pineapple fiber and yarn is applied in the field of preparation of pineapple fiber yarn, which can solve the problems of no antibacterial properties, poor moisture absorption and air permeability, etc., and achieve long-term antibacterial and moisture absorption and air permeability, good moisture absorption and air permeability, good antibacterial and moisture absorption. The effect of breathability

Inactive Publication Date: 2012-10-17
SHANGHAI SHUIXING HOME TEXTILE
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a kind of spinning method that has natural antibacterial, the good pineapple fiber yarn of hygroscopic air permeability for the characteristic of the pineapple fiber mentioned in the above-mentioned background technology, solves the problem that traditional yarn does not have antibacterial performance, The problem of poor moisture absorption and breathability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] It is processed by blending process with pineapple fiber, viscose fiber and cotton fiber as raw materials. According to the blending ratio of 40% pineapple fiber, 40% viscose fiber and 20% cotton fiber by weight, it is processed according to the following steps: raw material → raw material Preparation → combing → drawing → roving → spun yarn.

[0016] The yarn obtained through the above steps is processed into a fabric according to the following steps: winding→warping→sizing→reeding→weaving→dyeing→finishing.

Embodiment 2

[0018] It is processed by blending process with pineapple fiber, viscose fiber and cotton fiber as raw materials. According to the blending ratio of 40% pineapple fiber, 45% viscose fiber and 15% cotton fiber by weight, it is processed according to the following steps: raw material → raw material Preparation → combing → drawing → roving → spun yarn.

[0019] The yarn obtained through the above steps is processed into a fabric according to the following steps: winding→warping→sizing→reeding→weaving→dyeing→finishing.

Embodiment 3

[0021] It is processed by blending process with pineapple fiber, viscose fiber and cotton fiber as raw materials. According to the blending ratio of 40% pineapple fiber, 50% viscose fiber and 10% cotton fiber by weight, the processing is carried out according to the following steps: raw material → raw material preparation → Combing hemp → drawing frame → roving → spun yarn.

[0022] The yarn obtained through the above steps is processed into a fabric according to the following steps: winding→warping→sizing→reeding→weaving→dyeing→finishing.

[0023] Using the fabrics in the above embodiments for the production of home textile products, four-piece sets and six-piece sets in home textile products can be prepared.

[0024] The home textile kit developed with this fabric is moisture-absorbing, breathable, soft and comfortable, and also has a natural antibacterial effect, and the antibacterial effect reaches 80%-98% after testing.

[0025] The corresponding antibacterial property o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method for pineapple fiber yarns. The pineapple fiber yarns are made by a blending process with pineapple fibers, viscose fibers and cotton fibers as main materials. The method is characterized in that the blended ratio of the pineapple fibers, viscose fibers and cotton fibers is 30%-40% of pineapple fibers, 30%-50% of viscose fibers and 10%-20% of cotton fibers. The method of the invention is to blend the pineapple fibers and viscose fibers as the main materials into yarns, using the pineapple fibers' characteristics of natural resistance to bacteria, good moisture absorption and air permeability. Family products for family use, which is made of the yarns [Home textile sets made from the fabric woven by the yarns], have properties of long-time resistance to bacteria and good moisture absorption.

Description

technical field [0001] The invention relates to a preparation method of textile fiber yarn, in particular to a preparation method of pineapple fiber yarn. Background technique [0002] At present, strengthening the development and utilization of various natural fiber resources has become a major issue of common concern in the global textile and paper industry. The chemical composition of pineapple fiber is similar to that of flax and jute, but the content of cellulose is low, and the content of hemicellulose and lignin is relatively high. , so the pineapple fiber is thick and hard, the elongation is small, the elasticity is poor, and the moisture absorption and dehumidification are fast. The fat and wax content in the fiber is higher, so the gloss is better. Pineapple fiber has the advantages of hemp fiber, high strength, small elongation, fast moisture absorption and moisture release, thick and hard fiber, high initial modulus, poor elasticity, and excellent antibacterial ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information