Compact steel wire braided rubber hose and preparation method thereof

A steel wire braided rubber hose, compact technology, applied in the direction of hoses, pipes, mechanical equipment, etc., can solve the problems of unreasonable rubber formula and skeleton layer design, and achieve the effects of light weight, increased service life and stable pulse performance

Active Publication Date: 2014-07-02
LUOHE LETONE RUBBER
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main reason for this problem is that the formula of the rubber compound and the design of the skeleton layer are unreasonable.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Compact steel wire braided rubber hose and preparation method thereof
  • Compact steel wire braided rubber hose and preparation method thereof
  • Compact steel wire braided rubber hose and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A preparation method of a dense steel wire braided rubber hose. The preparation methods of the materials of the inner rubber hose, the middle rubber layer and the outer rubber layer are the same, including the following steps:

[0021] a. Weigh each raw material in parts by weight, pass the raw rubber thinly on the open mill, with a roll distance of 0.5~0.8mm, and a time of 3~4min; relax the roll distance by 2~3mm, put in small materials in order, wait for small materials Eat up all, add the reinforcing agent and softener in batches. When adding the compounding agent, do not use the knife to knead. Add the vulcanization system. After all is eaten, adjust the roller pitch to 0.5~0.8mm, thin 3 times; then adjust the roller pitch to 2~3mm, make 5 triangle packages and 3 rolls, and cool the next film;

[0022] b. The test piece is vulcanized on a plate vulcanizing machine, and the vulcanization condition is 151℃×60min;

[0023] Among them: the materials for preparing the inner ru...

Embodiment 2

[0038] A preparation method of a dense steel wire braided rubber hose. The preparation methods of the materials of the inner rubber hose, the middle rubber layer and the outer rubber layer are the same, including the following steps:

[0039] Steps a and c are the same as in Example 1, but step b is different,

[0040] Step b: The test piece is vulcanized on a flat vulcanizing machine, and the vulcanization condition is 151℃×60min;

[0041] Among them: the materials for preparing the inner rubber tube, the middle rubber layer and the outer rubber layer are as follows:

[0042] The inner rubber of the inner rubber layer is prepared from the following raw materials by weight: raw rubber: nitrile rubber N1042 100kg, reinforcing agent: carbon black N660 90kg and white carbon black 10kg; softener: dioctyl phthalate 10kg; sample: zinc oxide 3kg, stearic acid 1kg, antioxidant 2,2,4-trimethyl-1,2-dihydroquinoline 2kg, sulfur 1kg, adhesive RC5kg and accelerator N-cyclohexyl -2-Benzothiazole s...

Embodiment 3

[0047] A preparation method of a dense steel wire braided rubber hose. The preparation methods of the materials of the inner rubber hose, the middle rubber layer and the outer rubber layer are the same, including the following steps:

[0048] Steps a and c are the same as in Example 1, but step b is different,

[0049] Step b: The test piece is vulcanized on a flat vulcanizing machine, and the vulcanization condition is 151℃×60min;

[0050] Among them: the materials for preparing the inner rubber tube, the middle rubber layer and the outer rubber layer are as follows:

[0051] The inner rubber of the inner rubber layer is prepared from the following raw materials by weight: raw rubber: nitrile rubber N1052 100kg, reinforcing agent: carbon black N550 115kg and white carbon black 13kg; softener: dioctyl phthalate 14kg ; Sample: zinc oxide 6kg, stearic acid 3kg, antioxidant N-isopropyl-N-phenyl-p-phenylenediamine 4kg; curing system: sulfur 3kg, binder RC7kg and accelerator N-cyclohexyl-2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
compressive strengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a dense steel wire braided rubber hose and a preparation method thereof. The dense steel wire braided rubber hose includes an inner rubber layer, two steel wire layers braided outside the inner rubber layer, a middle rubber layer between the two steel wire layers and the outside of the steel wire layer outer rubber layer. The inner rubber of the inner rubber layer, the middle rubber of the middle rubber layer and the outer rubber of the outer rubber layer are all prepared from the following raw materials in parts by weight: raw rubber, reinforcing agent; softener, sample, adhesive and accelerator . The invention also discloses a preparation method of the dense steel wire braided rubber hose. The invention has the following advantages: the compact braided rubber hose of the invention has reasonable structure, small deformation under pulse pressure, light rubber hose, small bending radius, all properties of the finished product meet the requirements of SAEJ517R17 remarks, stable pulse performance, and the number of pulses exceeds 300,000 Second, greatly increasing the service life of the hose.

Description

technical field [0001] The invention relates to a steel wire braided rubber hose, and also relates to a preparation method of the rubber hose. Background technique [0002] At present, many heavy industry supporting enterprises have a great demand for SAE R17 series hoses, and the requirements are getting higher and higher, while SAER17 The 25×2-layer steel wire braided rubber hose has been tested. Well-known domestic rubber hose manufacturers only reach about 100,000 times, and rarely reach the 200,000 times required by the standard, which is far from meeting the needs of customers. The main reason for this problem is that the formula of the rubber compound and the design of the skeleton layer are unreasonable. Contents of the invention [0003] The purpose of the present invention is to overcome the above disadvantages and provide a dense steel wire braided rubber hose and its preparation method. The dense steel wire braided rubber hose is an SAE R17 rubber hose with c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B32B1/08F16L11/08C08L9/02C08K13/02C08K3/04C08K3/36C08K5/12C08K3/22C08K5/09C08L101/00
Inventor 赵付会
Owner LUOHE LETONE RUBBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap