Organic polymer gelator and preparation method and application thereof

A technology of gelling factor and polymer, applied in the field of its preparation, organic polymer gelling factor, can solve problems such as few reports

Active Publication Date: 2012-12-12
NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI
View PDF8 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Organic polymer gels are one of the hotspots of current research, but there are few reports on organic polymer gels with aromatic polymers as gelling factors

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic polymer gelator and preparation method and application thereof
  • Organic polymer gelator and preparation method and application thereof
  • Organic polymer gelator and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] In this embodiment, the organic polymer gel factor is a polymer whose main chain is polyether ether ketone, and the side chain contains benzenesulfonimide groups. The synthesis method of the organic polymer gel factor includes the following steps.

[0029] Step 1: Dissolve 7.96g of sulfonated polyetheretherketone (DS=66%) in 50ml of thionyl chloride, slowly add 0.5ml of pyridine dropwise, and react at reflux temperature for 24h. After the reaction, mix the solution Pour into 1L of deionized water to precipitate a white solid, filter and wash with deionized water until neutral to obtain sulfonyl chloride polyether ether ketone;

[0030] Step 2: Dissolve 4.16g of sulfonyl chloride polyetheretherketone obtained in step 1 and 3.42g of p-toluenesulfonamide in 50ml of 1,2-dichloroethane, slowly add 3ml of triethylamine dropwise to it, at 60°C The mixture was reacted for 48 hours, then filtered, and washed successively with chloroform, hydrochloric acid solution and deionized ...

Embodiment 2

[0034] In this embodiment, the organic polymer gel factor is a polymer whose main chain is polyether ether ketone, and the side chain contains benzenesulfonimide groups. The synthesis method of the organic polymer gel factor includes the following steps.

[0035] Step 1: Dissolve 8.01g of sulfonated polyetheretherketone (DS=53%) in 50ml of thionyl chloride, slowly add 0.5ml of pyridine dropwise, and react at reflux temperature for 24h. After the reaction, mix The solution was poured into 1L of deionized water, a white solid was precipitated, filtered, washed with deionized water until neutral, and sulfonyl chloride polyether ether ketone was obtained;

[0036] Step 2: Dissolve 3.70 g of the sulfonyl chloride polyether ether ketone obtained in step 1 and 3.42 g of p-toluenesulfonamide in 50 ml of chloroform, slowly add 0.60 g of sodium hydroxide therein, and react at 60°C for 48 hours. Then, it was filtered and washed successively with chloroform, hydrochloric acid solution and...

Embodiment 3

[0039] In this embodiment, the organic polymer gel factor is a polymer whose main chain is polyether ether ketone, and the side chain contains benzenesulfonimide groups. The synthesis method of the organic polymer gel factor includes the following steps.

[0040] Step 1: Dissolve 8.24g of sulfonated polyetheretherketone (DS=74%) in 50ml of thionyl chloride, slowly add 0.5ml of pyridine dropwise, and react at reflux temperature for 24h. After the reaction, mix the solution Pour into 1L of deionized water to precipitate a white solid, filter and wash with deionized water until neutral to obtain sulfonyl chloride polyether ether ketone;

[0041] Step 2: Dissolve 3.90 g of the sulfonyl chloride polyether ether ketone obtained in step 1 and 3.42 g of p-toluenesulfonamide in 50 ml of dimethyl sulfoxide, add 0.73 g of potassium fluoride to it, and react at 60°C for 48 hours. Then, it was filtered and washed successively with chloroform, hydrochloric acid solution and deionized water ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an organic polymer gelator and a preparation method and application thereof. The organic polymer gelator is excellent in gelation ability, takes an aromatic polymer as a main chain and is structurally modified to enable a side chain to contain benzenesulfonyl imidogen, so that the organic polymer gelator and polarity organic solvent molecules can efficiently form a hydrogen-bond cross-linked structure, and further, gel is formed. The organic polymer gelator has potential application value and development potentials in the fields of water treatment agents, oil spill at sea, biological tissue engineering, drug transportation, food, cosmetics, biological sensing and sensitive device preparation and the like.

Description

technical field [0001] The invention belongs to the field of polymer materials, and specifically relates to an organic polymer gel factor, its preparation method and application. The polymer gel factor has high-efficiency gel performance in polar organic solvents, so it is used in water treatment, nano It has good application prospects in the fields of material templates and drug carriers. Background technique [0002] Due to the special properties of both solid and liquid, organogels are widely used in biological tissue engineering, drug delivery, inorganic material templates, water treatment agents, cosmetics, food, marine oil spills, biosensing and sensitive device preparation, propellant performance optimization, etc. It has great application potential and has attracted more and more attention. [0003] According to the different molecular weights of gelling factors, organogelling factors can be divided into low molecular weight organic gelling factors and organic polym...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G8/28C08G8/02C08G75/20C08G75/23
Inventor 薛立新章勤陶慷赵秀兰魏增斌
Owner NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com