Gypsum mold oil composition

An oil composition, gypsum mold technology, applied in the directions of lubricating composition, petroleum industry, additives, etc., can solve problems such as damage, shorten service life, harmful models, etc., achieve reasonable raw material compatibility, prolong service life, and simple preparation method. Effect

Active Publication Date: 2013-02-13
CHINA PETROLEUM & CHEM CORP
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Long-term use of over-humidity model is harmful to the model itself, it will cause premature aging of the model and shorten the service life, because when the water content of the model is high, the salt that penetrates into the model will chemically react with dihydrate gypsum reaction
This will cause serious corrosion and damage to the internal structure of the model
[0015] In addition, after the plaster mold has been used many times, there will be many cavities on the inner surface, and there will be serious seams at the seams such as the edges of the mold.
As a result, the smoothness of the appearance of the finished ceramic wine bottle is affected. Therefore, when the smoothness of the outer surface of the bottle is unacceptable, the plaster mold meets the scrapping requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Get lanolin magnesium soap (purchased from Nanjing Runyou Chemical Additive Co., Ltd.) 0.2kg, microcrystalline wax (purchased from Dalian Petrochemical Company) 6.0kg, rosin 3.0kg, solvent oil (No. 260 solvent gasoline) (purchased from Daqing Petrochemical Company) ) 20kg, phthalocyanine blue BGS (purchased from Anqing Hexing Chemical Co., Ltd.) 0.6kg, and then added to 70.2kg of base oil (45# transformer oil) in turn, mixed and stirred for 2 hours at 50 ° C to make a plaster mold oil composition.

[0038] After testing, the product has a flash point of 71°C.

Embodiment 2

[0040] Get lanolin magnesium soap (purchased from Taicang Xinyao Lanolin Co., Ltd.) 0.3kg, microcrystalline wax (purchased from Daqing Petrochemical Company) 5.0kg, rosin 4.0kg, solvent oil (No. 260 solvent gasoline) (purchased from Dalian Petrochemical Company) ) 25kg, phthalocyanine blue BGS (purchased from Anhui Sanxin Chemical Co., Ltd.) 0.5kg, and then added to 65.2kg of base oil (45# transformer oil) in turn, mixed and stirred at 55°C for 1.5 hours to make plaster mold oil combination.

[0041] After testing, the product has a flash point of 70°C.

Embodiment 3

[0043] Take 0.5kg of lanolin magnesium soap, 3.0kg of microcrystalline wax, 5.0kg of rosin, 30kg of solvent oil (No. 260 solvent gasoline), and 0.5kg of phthalocyanine blue BGS, and then add them to 61kg of base oil (45# transformer oil) in sequence , mixed and stirred at 65° C. for 1 hour to prepare a plaster mold oil composition.

[0044] After testing, the product has a flash point of 68°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Flash pointaaaaaaaaaa
Flash pointaaaaaaaaaa
Flash pointaaaaaaaaaa
Login to View More

Abstract

The invention provides a gypsum mold oil composition. The gypsum mold oil composition comprises 0.2-0.5wt% of lanolin magnesium soap, 3.0-6.0wt% of microcrystalline wax, 3.0-5.0wt% of rosin, 20-30wt% of solvent oil, 0.5-0.6wt% of phthalocyanine blue BGS, and the balance base oil. The gypsum mold oil composition is developed according to the technological characteristics of gypsum molds used in the ceramic production, can satisfy use requirements of molds for ceramic production by like enterprises, and enables the service lives of the gypsum molds to be prolonged by above 20%. The gypsum mold oil composition has the advantages of reasonable compatibility of product raw materials, simple preparation method, wide application range, and easily available raw materials.

Description

technical field [0001] The invention relates to a mold lubricating composition, in particular to a composition used for lubricating plaster molds, and belongs to the field of chemical industry. Background technique [0002] At present, the traditional production process of ceramic wine bottle production enterprises mainly has the following steps: [0003] 1) Beating: The ceramic raw materials configured according to a certain ratio are mixed and crushed, sieved, stirred with water, and precipitated. [0004] 2) Inverting: Introduce the milky raw materials into the mold, and after the rapid water absorption of the gypsum mold, the condensed and formed ones are left as preforms, and the excess is poured out. [0005] 3) Demolding and molding: After several minutes of moisture absorption, it can be demoulded and formed. [0006] 4) Engraving: Carry out bottle mouth repair, and the traces left by the bonding part with the mold should be repaired after drying the preform. [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C10M141/06
Inventor 汤涛陈惠卿李万英王向阳韦安柱贾睿
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com