High-density glass fiber board and production method thereof

A glass fiber board and glass fiber cloth technology, which is applied in the field of high-density glass fiber board and its preparation, can solve the problems of polluting the indoor environment, low flexural strength, and high brittleness of high-density glass wool board, so as to simplify the construction procedure and reduce the engineering cost. The effect of cost and high tensile strength

Active Publication Date: 2013-02-27
无锡市明江保温材料有限公司
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because the high-density glass wool board is made of glass fiber resin wool by heating and pressing, and the bonding resin is phenolic resin, with a content of 8-10%, the high-density glass wool board is brittle and has low flexural strength. , especially containing 8~10% organic resin, which reduces the non-combustible performance of the material, and will release the harmful substance formaldehyde for a long time, pollute the indoor environment, and is not conducive to safety and environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] (1) Preparation of non-alkali glass fiber blanket: firstly cut 80 parts of non-alkali glass fiber into fixed-length fibers with a length of 50 mm, then open, card, lay and acupuncture to prepare non-alkali glass fiber blanket ;

[0023] The alkali-free glass fiber blanket has a thickness of 8 mm and a bulk density of 80 kg / m3;

[0024] (2) Preparation and modification of binder: take 5 parts of inorganic binder, 0.1 part of thickener, and 0.1 part of water repellent, disperse and emulsify with a high-speed disperser; the speed is 800r / min, and the time is 5min;

[0025] (3) Centrifugal drying: soak 5 parts of non-alkali glass fiber cloth and the non-alkali glass fiber blanket prepared in step (2) in the binder prepared in step (2) for 5 minutes, take it out, and put it in a centrifuge Spin dry in medium; centrifuge speed 800r / min, dehydration time 2 minutes;

[0026] (4) Rolling: Take out the alkali-free glass fiber blanket dehydrated and dried by the centrifuge in st...

Embodiment 2

[0034] (1) Preparation of non-alkali glass fiber blanket: First, 90 parts of non-alkali glass fiber is chopped into fixed-length fibers with a length of 100mm, and then the non-alkali glass fiber blanket is obtained by opening, carding, laying and acupuncture ;

[0035] The alkali-free glass fiber blanket has a thickness of 10 mm and a bulk density of 100 kg / m3;

[0036] (2) Preparation and modification of binder: Take 15 parts of inorganic binder, 0.5 part of thickener, and 0.5 part of water repellent, disperse and emulsify with a high-speed disperser; the speed is 1000r / min, and the time is 10min;

[0037] (3) Centrifugal drying: soak 10 parts of non-alkali glass fiber cloth and the non-alkali glass fiber blanket prepared in step (2) in the binder prepared in step (2) for 10 minutes, take it out, and put it into a centrifuge Drying in medium; centrifuge speed 1000r / min, dehydration time 5 minutes;

[0038] (4) Rolling: Take out the alkali-free glass fiber blanket dehydrate...

Embodiment 3

[0046] (1) Preparation of non-alkali glass fiber blanket: firstly cut 85 parts of non-alkali glass fiber into fixed-length fibers with a length of 80mm, then open, card, lay and acupuncture to prepare non-alkali glass fiber blanket ;

[0047] The alkali-free glass fiber blanket has a thickness of 9 mm and a bulk density of 90 kg / m3;

[0048] (2) Preparation and modification of binder: take 10 parts of inorganic binder, 0.3 parts of thickener, and 0.3 parts of water repellent, disperse and emulsify with a high-speed disperser; the speed is 900r / min, and the time is 8min;

[0049] (3) Centrifugal drying: soak 8 parts of non-alkali glass fiber cloth and the non-alkali glass fiber blanket prepared in step (2) in the binder prepared in step (2) for 8 minutes, take it out, and put it into a centrifuge Spin dry in medium; centrifuge speed 900r / min, dehydration time 3 minutes;

[0050] (4) Rolling: Take out the alkali-free glass fiber blanket dehydrated and dried by the centrifuge i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-density glass fiber board and a production method thereof which are used for reinforcing and protecting surface layers of soft heat-insulating materials of shipboard cabins and belong to the technical field of inorganic materials. The preparation method comprises the following steps of: preparing alkali-free glass fibers into an alkali-free glass fiber blanket; and taking a bonding agent, a thickening agent and a water repellent agent to prepare a bonding agent; centrifugally drying, rolling, compounding and setting alkali-free glass fiber cloth and the alkali-free glass fiber blanket to obtain the high-density glass fiber board. The high-density glass fiber board is formed by needling continuous fibers, so that the fiber blanket has a three-dimensional network structure and has strong tensile strength; and in addition, the bonding agent is used for compressing and setting, so that the strength of the product can be greatly improved. After the surface is impregnated with the alkali-free glass fiber cloth and is integrally formed with a fiber board, the product has functions of reinforcing boards and fireproof boards; and a heat insulating layer is integrated with a protecting layer, so that the construction procedure is simplified and the construction cost of projects is reduced.

Description

technical field [0001] The invention relates to a high-density glass fiber board and a preparation method thereof, which are used for strengthening and protecting the surface layer of soft heat-insulating materials in ship cabins, and belong to the technical field of inorganic materials. Background technique [0002] At present, the cabin thermal insulation layer of various ships, due to the particularity of the structure, generally uses soft thermal insulation materials as the thermal insulation layer, such as rock mineral wool, glass wool, ceramic wool, etc. Two methods are generally adopted in the design of the outer sheath. One is to install the outer protective fireproof board after installing the heat insulation layer. The advantage is that the surface is smooth and the decoration effect is good. The disadvantage is that the structure is complex, no sound absorption, and the cost is high. The other is to apply two layers of flame-retardant white cloth on the surface a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/26C04B28/24C04B28/34C04B14/42
Inventor 周致中尤仁兴
Owner 无锡市明江保温材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com